Diatom ooze wall paint formula and preparation process thereof

A preparation process and a technology for wall paint, applied in the field of wall paint, can solve the problems of only focusing on the surface performance of the paint, poor humidity regulation, insufficient safety and environmental protection, etc., and achieve the effect of strong elasticity, good anti-fouling, and improved antibacterial effect.

Inactive Publication Date: 2013-06-05
GUANGDONG VALSPAR CHEM IND
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, many wall paints cannot solve or completely solve these problems, especially the environmental protection and safety problems of the living environment. The main reason is that the currently used wall paints only focus on the surface properties of the paint, such as: water and alkali resistance , elasticity, scrub resistance and other properties, but its volatile organic compound (hereinafter referred to as VOC) content, antibacterial, air purification, adsorption of harmful substances such as smoke and dust, and humidity adjustment are not good or not effective enough, not safe and environmentally friendly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Equipped with 100kg of diatom mud wall paint of the present invention, which is prepared from the following components by weight:

[0032] 27.5kg of clean water, 0.8kg of dispersant, 0.1kg of surfactant, 0.8kg of defoamer, 3kg of ethylene glycol, 25kg of titanium dioxide, the titanium dioxide is rutile type, 20kg of diatomaceous earth, the Diatomite is the remains of seabed plants, pure acrylic emulsion 19.3kg, polyurethane thickener 1kg, preservative 0.2kg, antifungal agent 0.3kg, film-forming aid 2kg; the preservative is isothiazolinone The antifungal agent is a mixture of carbamic acid-1-chloro-benzimidazole-2-methyl acid and N-(3,4 dichlorophenyl)-N.N-dimethylurea; the film-forming The auxiliary agent is 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate; the dispersant is modified polycarboxylate sodium salt; the surfactant is alkoxylated alcohol ; The defoamer is a mixture of silicone and mineral oil.

[0033] Equipped with 100kg of diatom mud wall paint of the pre...

Embodiment 2

[0035] Equipped with 100kg of diatom mud wall paint of the present invention, which is prepared from the following components by weight:

[0036] 23.8kg of clean water, 0.8kg of dispersant, 0.1kg of surfactant, 0.6kg of defoamer, 2.8kg of ethylene glycol, 23kg of titanium dioxide, the titanium dioxide is rutile type, 10kg of diatomaceous earth, the Diatomite is the remains of seabed plants, 35.4kg of pure acrylic emulsion, 0.8kg of polyurethane thickener, 0.2kg of preservative, 0.3kg of antifungal agent, and 2.2kg of film-forming aid; the preservative is isothiazolinone The antifungal agent is a mixture of carbamic acid-1-chloro-benzimidazole-2-methyl acid and N-(3,4 dichlorophenyl)-N.N-dimethylurea; the film-forming The auxiliary agent is 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate; the dispersant is modified polycarboxylate sodium salt; the surfactant is alkoxylated alcohol ; The defoamer is a mixture of silicone and mineral oil.

[0037] Equipped with 100kg of diatom ...

Embodiment 3

[0039] Equipped with 100kg of diatom mud wall paint of the present invention, which is prepared from the following components by weight:

[0040] 28.6kg of clean water, 0.8kg of dispersant, 0.1kg of surfactant, 0.8kg of defoamer, 3kg of ethylene glycol, 21kg of titanium dioxide, the titanium dioxide is rutile type, 13kg of diatomaceous earth, the Diatomite is the remains of seabed plants, pure acrylic emulsion 28.3kg, polyurethane thickener 1.2kg, preservative 0.2kg, antifungal agent 0.5kg, film-forming aid 2.5kg; the preservative is isothiazolinone The antifungal agent is a mixture of carbamic acid-1-chloro-benzimidazole-2-methyl acid and N-(3,4 dichlorophenyl)-N.N-dimethylurea; the film-forming The auxiliary agent is 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate; the dispersant is modified polycarboxylate sodium salt; the surfactant is alkoxylated alcohol ; The defoamer is a mixture of silicone and mineral oil.

[0041]Equipped with 100kg diatom mud wall paint of the pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a diatom ooze wall paint formula and a preparation process thereof. The wall paint comprises the following components in percentage by weight: 20-30% of water, 0.5-1% of dispersant, 0.1-0.2% of surfactant, 0.4-0.8% of defoamer, 0.8-3.5% of ethylene glycol, 10-25% of titanium dioxide, 5-25% of diatomite, 15-45% of pure acrylic emulsion, 0.8-1.5% of polyurethane thickener, 0.1-0.2% of preservative, 0.2-0.7% of mildew preventive and 1-2.5% of coalescing agent. The preparation process of the wall paint comprises the following step of: sequentially adding the dispersant, the surfactant, the defoamer, ethylene glycol, titanium dioxide, diatomite, pure acrylic emulsion, the polyurethane thickener, the preservative, the mildew preventive and the coalescing agent into water. The wall paint prepared by the formula and process has the advantages of resisting bacteria continuously, purifying air, absorbing harmful substances such as soot, adjusting humidity, preventing mildew and algae, maintaining water tolerance of the paint film, resisting alkali and the like.

Description

【Technical field】 [0001] The invention relates to a wall paint used for foundation construction, in particular to a formula of diatom mud wall paint and a preparation process thereof. 【Background technique】 [0002] In home decoration, problems such as excessive formaldehyde limit, wall cracks, blooming, mildew, water leakage, and anti-fouling have long plagued people's home life, and these problems can be solved by painting wall paint. At present, many wall paints cannot solve or completely solve these problems, especially the environmental protection and safety problems of the living environment. The main reason is that the currently used wall paints only focus on the surface properties of the paint, such as: water and alkali resistance , elasticity, scrub resistance and other properties, but its content of volatile organic compounds (hereinafter referred to as VOC), antibacterial, air purification, adsorption of harmful substances such as smoke and dust, and humidity adju...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/12
Inventor 高小兵蔡森
Owner GUANGDONG VALSPAR CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products