Coated paper produced from K8 cable paper and used for high-speed battery production line and preparation method thereof

A technology for pulp layer paper and cable paper, which is applied in the field of dry battery manufacturing, can solve the problems of pulp layer paper rupture, difficulty in feeding zinc cans, powder drop, etc., and achieves improved smoothness and elasticity, good mechanical applicability, and good static elimination effect. Effect

Active Publication Date: 2013-06-12
辽源市金玉征程隔膜有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Pulp layer paper produced by ordinary technology generally has the characteristics of high hardness and is prone to static electricity. In addition, during the production of batteries on high-speed battery production lines, the pulp layer paper is often broken, difficult to feed into the zinc cylinder, and powder falls, which seriously affects The normal performance of the high-speed battery production line has resulted in an increase in defective and waste batteries
However, the pulp paper produced by composite base paper increases the production cost due to its high price, which makes it difficult for ordinary zinc-manganese dry batteries to bear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coated paper produced from K8 cable paper and used for high-speed battery production line and preparation method thereof
  • Coated paper produced from K8 cable paper and used for high-speed battery production line and preparation method thereof
  • Coated paper produced from K8 cable paper and used for high-speed battery production line and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] In this embodiment, K8 cable paper is used to produce pulp paper for high-speed battery production line (≥800 pieces / min). The base paper of the pulp paper is K8 cable paper, and a coating layer is coated on one side of the base paper. When preparing the cloth layer, weigh each component according to the following formula:

[0042] Modified starch 48%; polyacrylamide 3.5%;

[0043] Instant glue 33%; Alkylphenol polyoxyethylene ether 1.5%;

[0044] Dioctadecyldimethylamine chloride 3%; Polyethyleneimine 3%;

[0045] Hydroxyethyl cellulose 5%; Composite corrosion inhibitor 3%.

[0046] The instant glue in the above formula is composed of instant glue silk 100-27H and instant glue silk 100-37H produced by Hunan Xiangwei Co., Ltd. with a mass ratio of 14:16; the modified starch is produced by Foshan Huahao Huafeng Starch Co., Ltd. Composition of cross-linked starch JLS and etherified starch H315 with a mass ratio of 25:20; the composite corrosion inhibitor is composed of...

Embodiment 2

[0049] In this embodiment, K8 cable paper is used to produce pulp paper for high-speed battery production line (≥800 pieces / min). The base paper of the pulp paper is K8 cable paper, and a coating layer is coated on one side of the base paper. When preparing the layer, weigh each component according to the following formula:

[0050] Modified starch 45%; Polyacrylamide 4%;

[0051] Instant glue 35%; Alkylphenol polyoxyethylene ether 2%;

[0052] Dioctadecyldimethylammonium chloride 2.5%; Polyethyleneimine 3.5%;

[0053] Hydroxyethyl cellulose 4.5%; Composite corrosion inhibitor 3.5%.

[0054] The instant glue in the above formula is composed of instant glue silk 100-27H and instant glue silk 100-37H produced by Hunan Xiangwei Co., Ltd. with a mass ratio of 18:16; the modified starch is produced by Foshan Huahao Huafeng Starch Co., Ltd. The mass ratio of cross-linked starch JLS and etherified starch H315 is 30:20; the composite corrosion inhibitor is composed of bismuth trich...

Embodiment 3

[0057] In this embodiment, K8 cable paper is used to produce pulp paper for high-speed battery production line (≥800 pieces / min). When preparing the layer, weigh each component according to the following formula, and the sum of the weight percentages of each component of the following formula is 100%:

[0058] Modified starch 50%; Polyacrylamide 3%;

[0059] Instant glue 30%; Alkylphenol polyoxyethylene ether 2%;

[0060] Dioctadecyldimethylammonium chloride 3%; Polyethylene immonium 3.5%;

[0061] Hydroxyethyl cellulose 5%; Composite corrosion inhibitor 3.5%.

[0062] The instant glue in the above formula is composed of instant glue silk 100-27H and instant glue silk 100-37H produced by Hunan Xiangwei Co., Ltd. with a mass ratio of 16:16; the modified starch is produced by Foshan Huahao Huafeng Starch Co., Ltd. The mass ratio of cross-linked starch JLS and etherified starch H315 is 25:25; the composite corrosion inhibitor is composed of bismuth trichloride and EDTA, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a coated paper produced from K8 cable paper and used for high-speed battery production line and a preparation method thereof. The coated paper has base paper which is K8 cable paper, and a coating layer is coated on one surface of the base paper. The coating layer comprises the following components in percentage by weight: 45-50% of modified starch, 3-4% of polyacrylamide, 30-35% of instant gelatin silk, 1.5-2% of alkylphenol ethoxylates, 2.5-3% of dioctadecyl dimethyl ammonium chloride, 2.5-3.5% of polyethyleneimine, 4-5% ofhydroxyethyl cellulose and 2.5-3.5% of compound corrosion inhibitor. The coated paper disclosed by the invention has the advantage of low production cost, not only achieves good isolation performance and good water retainability which are required by dry cell production, but also can well reach the production process requirements of the high-speed battery production line with production capacity being not less than 800 per minute.

Description

technical field [0001] The invention relates to a pulp paper and a preparation method thereof, belonging to the technical field of dry battery manufacturing, in particular to a mercury-free zinc-manganese dry battery pulp paper for high-speed battery production lines (≥800 pieces / min) produced with K8 cable paper and its preparation method. Background technique [0002] With the rise of labor costs, the proportion of labor costs in production costs has increased sharply, and the battery production industry is facing a situation of transformation from traditional labor-intensive industries to mechanized and highly automated labor-efficient industries. With the continuous advancement of production technology, the automation of battery production equipment is getting higher and higher, and the production speed is getting faster and faster. Pulp layer paper produced by ordinary technology generally has the characteristics of high hardness and is prone to static electricity. In ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine