Production method of magnesium alloy hub

A magnesium alloy and hub technology, which is applied in the field of magnesium alloy hub preparation, can solve problems such as low material utilization, long production cycle, and complex process flow, and achieve the effects of improving comprehensive mechanical properties, reducing production processes, and reducing manufacturing costs

Active Publication Date: 2013-07-17
NO 52 INST OF CHINA NORTH IND GRP CORP
View PDF10 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are two kinds of manufacturing processes of magnesium alloy wheels, casting and forging. For example, the Chinese invention patent "A Manufacturing Method for Magnesium Alloy Wheels" (authorized announcement number CN100515804C) with the patent number ZL03109034. Magnesium alloy wheels, similar to ZL200610086359.0, ZL201010253694.1, etc., adopt casting method, although the production process is simple, the cost is low, and the material utilization rate is high, but the mechanical properties of the body sampling mater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of magnesium alloy hub
  • Production method of magnesium alloy hub
  • Production method of magnesium alloy hub

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1, combining figure 1 , figure 2 with image 3 As shown, the method for manufacturing a magnesium alloy wheel hub with the composite forming technology in this embodiment has the following specific steps:

[0022] (1) Use AZ31 magnesium alloy as the manufacturing material of the wheel hub. The AZ31 alloy is smelted according to the composition ratio and undergoes purification treatments such as refining, standing, cooling and iron removal. The pouring temperature is 680℃, and the melt is poured into the mold through a special pouring system. The entire pouring process is gas protected to protect the gas composition For CO 2 And SF 6 Mixed gas, where SF 6 The concentration is 0.5vol%.

[0023] (2) Heat the squeeze casting mold to 250°C, the squeeze casting pressure is 100MPa per unit area, and the pressure holding time is 60s.

[0024] (3) The magnesium alloy is subjected to homogenization treatment at 390°C for 10 hours; after the homogenization treatment, the magne...

Example Embodiment

[0027] Embodiment 2, the method of manufacturing a magnesium alloy wheel hub by the composite forming technology in this embodiment, the specific steps are as follows:

[0028] (1) Use AZ80 magnesium alloy as the manufacturing material of the wheel hub. The AZ80 alloy is smelted according to the composition ratio. After purification, refining, standing, cooling and iron removal, the pouring temperature is 700 ℃, and the melt is poured into the mold through a special pouring system. The entire pouring process is gas protected to protect the gas composition For CO 2 And SF 6 Mixed gas, where SF 6 The concentration is 0.5vol%.

[0029] (2) Heat the squeeze casting mold to 250°C, the squeeze casting pressure is 100MPa per unit area, and the pressure holding time is 60s.

[0030] (3) The magnesium alloy is subjected to homogenization treatment at 400°C for 16 hours; after the homogenization treatment, the magnesium alloy blank is heated to 380°C, the forging die is heated to 300°C, and t...

Example Embodiment

[0033] Embodiment 3, the method of manufacturing a magnesium alloy wheel hub by the composite forming technology in this embodiment, the specific steps are as follows:

[0034] (1) Use ZK60A magnesium alloy as the manufacturing material of the wheel hub. The ZK60A alloy is smelted according to the composition ratio. After purification, refining, standing, cooling and iron removal, the pouring temperature is 720℃, and the melt is poured into the mold through a special pouring system. The entire pouring process is gas protected to protect the gas composition For CO 2 And SF 6 Mixed gas, where SF 6 The concentration is 0.5vol%.

[0035] (2) Heat the squeeze casting mold to 250°C, the squeeze casting pressure is 100MPa per unit area, and the pressure holding time is 60s.

[0036] (3) The magnesium alloy is subjected to a homogenization treatment at 400°C for 10 hours; after the homogenization treatment, the magnesium alloy blank is heated to 380°C, the forging die is heated to 300°C, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

A production method of a magnesium alloy hub is characterized by including the steps of first, smelting; second, squeeze-casting; third, homogenizing; fourth, forging; fifth, thermal treatment; and sixth, subsequent treatment. Compared with the prior art, the production method has the advantages that the production method combines advantages of magnesium alloy hub production by casting and forging, and the magnesium alloy hub is made by squeeze-casting and forging according to the features of squeeze casting technology; the magnesium alloy hub is imparted with excellent comprehensive performance, the production process is simple, and the production cost is low.

Description

technical field [0001] The invention relates to a preparation method of a magnesium alloy wheel hub, belonging to the technical field of alloy production. Background technique [0002] As the lightest engineering metal material, magnesium alloy has a series of unique characteristics such as light specific gravity, high specific strength and specific stiffness, good damping and machinability, good thermal conductivity, strong electromagnetic shielding ability, good shock absorption and easy recycling. Advantages, known as "green engineering materials in the 21st century". The application of magnesium alloy materials has become an important development direction of automobile lightweight. [0003] In recent years, the application of magnesium alloy structural parts in automobiles has grown at a high rate of 20% per year. For example, Passat and Audi A4 and A6 cars have reached 13.6-14.5kg per vehicle, and will gradually increase to about 80kg in the future. According to the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23P15/00B22D18/02C22F1/06B21J5/02
Inventor 王军朱秀荣郑顺奇徐永东王荣邵志文陈大辉郭红燕聂景江任政
Owner NO 52 INST OF CHINA NORTH IND GRP CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap