Fly ash sintered material for water treatment

Abstract

The invention relates to a fly ash sintered material for water treatment. (1) Fly ash film ingredients comprise 60-70 parts by weight of fly ash, 20-30 parts by weight of clay and 10 parts by weight of carbon granules, the ingredients are mixed and ground to 80-200 meshes, water is added for uniformly mixing, a mixture is made into a variety of shapes, naturally dried and then sintered, the temperature is 1200-1700 DEG C, tree leaves are used for activation, then the mixture is taken out, and the aperture is made to be 0.1-90.0 micrometers; (2) a sewage treatment packing formula comprises 40-50 parts by weight of fly ash, 30-40 parts by weight of scrap iron, 10 pars by weight of anthracite, 7 parts by weight of clay and 3 parts by weight of catalyst, a ball mill is used for grinding the ingredients to 100 meshes, the water is added for uniformly mixing, the mixture is made into the shapes of circles, pipes and honeycombs of 2-6mm, drying is performed and the temperature is increased to 1100 DEG C; and (3) water treatment basic ingredients comprise 65-75 parts by weight of fly ash, 15-25 parts by weight of clay, 5 parts of additives and 5 parts of wood chips, the ingredients are ball-milled to 60-80 meshes and made into the different shapes with the size of 2-6mm, drying is performed, the temperature is increased to 950-1300 DEG C, and the tree leaves are used for activating for 10 minutes. The fly ash sintered material can be widely used for seawater desalination and wastewater treatment, has low cost and is suitable for large-area popularization and application.

Description

technical field [0001] The invention relates to filtering and treating materials in the field of water treatment, which is a novel inorganic filtering material, that is, a fly ash film and a filler, in particular to a fly ash sintered material for water treatment. Background technique [0002] At present, there are mainly 7 ways of comprehensive utilization of fly ash at home and abroad: [0003] 1. Fly ash aerated concrete. Fly ash aerated concrete is a new type of wall material with light weight, thermal insulation and energy saving. The main raw material is fly ash, accounting for about 70%, and the others are lime, cement, gypsum, gas-generating agent, etc., and these raw materials are processed, mixed, poured, gas-thickened, cut, autoclaved and cured. . It can be used as roof insulation, maintenance wall, partition wall, and can also be used as a load-bearing wall with the highest floor of five floors. It is especially suitable for high-rise building filling w...

AI Technical Summary

Problems solved by technology

Compared with similar plastic products, ceramic membrane is expensive, but has many advantages. It is hard, durable, durable, not easy to block, and has stronger resistance to chemically aggressive liquids and high-temperature cleaning fluids. Its main The disadvantage is that the price is expensive, the manufacturing process is complicated, and it is difficult to promote it in a large area when it is used in special occasions.