Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Chrome-free zinc-aluminum coating anticorrosive paint comprising nickel-magnesium-manganese-silicon

A coating anti-corrosion, zinc-aluminum technology, applied in anti-corrosion coatings, coatings, etc., can solve the problems of reduced corrosion resistance, high price, and increased cost of coatings, and achieve excellent corrosion resistance, low price, and good adhesion Effect

Inactive Publication Date: 2013-08-07
HUNAN QIANXIN PIPE IND
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there are industrial applications of chromium-free Dacromet technology at home and abroad, but the corrosion resistance of the coating is significantly lower than that of traditional Dacromet coatings, and it needs to be used with another organic coating, which greatly increases the cost
The cost of chromium-free zinc-aluminum coating is much higher than that of zinc-chromium coating, so its price is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chrome-free zinc-aluminum coating anticorrosive paint comprising nickel-magnesium-manganese-silicon

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A chromium-free zinc-aluminum coating anti-corrosion coating containing nickel-magnesium-manganese-silicon, which is composed of two components A and B in a mass ratio of 3:1, wherein the formula mass percentage of component A is:

[0054] Zinc aluminum alloy powder 32%

[0055] Nano Silica 25%

[0056] Sodium lignosulfonate 15%

[0057] Benzotriazole 4%

[0058] Thiodiethylene glycol 0.35%

[0059] Triphenylphosphine 0.35%

[0060] Deionized water balance

[0061] The formula mass percentage of component B is:

[0062] Zirconium tetrafluoride 25%

[0063] Gamma-Aminopropyltriethoxysilane 18%

[0064] Phytate 14%

[0065] Cellulose Acetate 3.5%

[0066] Ethanol 7%

[0067] Deionized water balance

[0068] Wherein, the zinc-aluminum alloy powder is composed of Zn, Al, Ni, Mg, Mn and Si.

[0069] Wherein, the particle size of the nano silicon dioxide is 20-50nm.

[0070] The method for preparing the above-mentioned nickel-magnesium-manganese-silicon-containing ...

Embodiment 2

[0075] A nickel-magnesium-manganese-silicon-containing chrome-free zinc-aluminum coating anti-corrosion coating, which is composed of two components A and B in a mass ratio of 3:1, wherein the formula mass percentage of component A is:

[0076] Zinc aluminum alloy powder 25%

[0077] Nano silica 30%

[0078] Sodium lignosulfonate 12%

[0079] Benzotriazole 5%

[0080] Thiodiethylene glycol 0.2%

[0081] Triphenylphosphine 0.5%

[0082] Deionized water balance

[0083] The formula mass percentage of component B is:

[0084] Zirconium tetrafluoride 20%

[0085] Gamma-Aminopropyltriethoxysilane 20%

[0086] Phytate 10%

[0087] Cellulose Acetate 5%

[0088] Ethanol 5%

[0089] Deionized water balance

[0090] Wherein, the zinc-aluminum alloy powder is composed of Zn, Al, Ni, Mg, Mn and Si.

[0091] Wherein, the particle size of the nano silicon dioxide is 20-50nm.

[0092] The preparation method is the same as in Example 1.

Embodiment 3

[0094] A nickel-magnesium-manganese-silicon-containing chrome-free zinc-aluminum coating anti-corrosion coating, which is composed of two components A and B in a mass ratio of 3:1, wherein the formula mass percentage of component A is:

[0095] Zinc aluminum alloy powder 40%

[0096] Nano silica 20%

[0097] Sodium lignosulfonate 18%

[0098] Benzotriazole 3%

[0099] Thiodiethylene glycol 0.5%

[0100] Triphenylphosphine 0.2%

[0101] Deionized water balance

[0102] The formula mass percentage of component B is:

[0103] Zirconium tetrafluoride 30%

[0104] Gamma-Aminopropyltriethoxysilane 15%

[0105] Phytate 18%

[0106] Cellulose Acetate 2%

[0107] Ethanol 9%

[0108] Deionized water balance

[0109] Wherein, the zinc-aluminum alloy powder is composed of Zn, Al, Ni, Mg, Mn and Si.

[0110] Wherein, the particle size of the nano silicon dioxide is 20-50nm.

[0111] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a chrome-free zinc-aluminum coating anticorrosive paint comprising nickel-magnesium-manganese-silicon. The paint is composed of a component A and a component B with a mass ratio of 3:1. The component A comprises the raw materials of zinc-aluminum alloy powder, nano-silica, lignin sodium sulfonate, benzotriazole, thio diethylene glycol, triphenylphosphine, and deionized water. The component B comprises zirconium tetrafluoride, gamma-aminopropyl triethoxysilane, inositol hexaphosphate, butyl cellulose acetate, ethanol, and deionized water. The zinc-aluminum alloy powder is composed of Zn, Al, Ni, Mg, Mn and Si. The product provided by the invention has the advantages of no toxicity, no harm, no pollution, low-temperature fast processing, simple operation, wide raw material source, low cost, clean production, and the like.

Description

technical field [0001] The invention relates to a metal anticorrosion coating, in particular to a chromium-free zinc-aluminum coating anticorrosion coating containing nickel-magnesium-manganese-silicon. Background technique [0002] Chromium-free zinc-aluminum coating is a new surface treatment material developed to meet the VOC regulations of various countries in the world and the environmental protection requirements stipulated by the coating industry, replacing the traditional Dacromet zinc-chromium coating process. [0003] Dacromet is the transliteration and abbreviation of DACROMET, abbreviated as Dacromet, Dacromet, and Dickron. Domestically named zinc-chromium coating, it is a new type of anti-corrosion coating with zinc powder, aluminum powder, chromic acid and deionized water as the main components. Its anti-corrosion principle is to use hexavalent chromium ions in chromium salts to passivate the zinc and aluminum flakes in the coating to improve the anti-corrosio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/00C09D5/10
Inventor 张军
Owner HUNAN QIANXIN PIPE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com