Environment-friendly water-based lubricating grease and preparation method thereof

A lubricating grease and water-based technology, applied in the field of lubricating grease, can solve the problems of non-environmental protection, high cost, waste, etc., and achieve the effects of easy cleaning, sufficient lubricity and adhesion, good heat transfer and cooling effects

Inactive Publication Date: 2013-08-14
SHENZHEN EUBO NEW MATERIAL TECH
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now most lubricants are oil-soluble. In many working conditions, such as cannon barrel cold extrusion and self-tightening processing, metal cutting, metal wire drawing, metal punching and extrusion, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example 1

[0017] Put 45 g of water-soluble polyether, 41.4 g of distilled water, and 11 g of stearic acid into the blending kettle, heat at 70-80° C. and stir evenly, and obtain a mixed solution after the dissolution is complete. Put 1g of calcium hydroxide and 0.55g of sodium hydroxide into the mixed solution and keep the temperature at 87~95℃ for 30min. After saponification, add 1 g of the composite solution of antiwear agent melamine cyanurate and zinc dialkyl dithiophosphate, 0.05 g of rust preventive agent benzotriazole, natural cooling to room temperature, grinding twice, and filtering to obtain the finished product.

Example Embodiment

[0018] Example 2

[0019] Put 30g of water-soluble polyether, 45g of distilled water, and 20g of stearic acid into the blending kettle, heat and stir evenly at about 70-80°C, and obtain a mixed solution after complete dissolution. Put 2g of calcium hydroxide and 1g of sodium hydroxide into the mixed solution, and keep the temperature at 87~95℃ for 30min. After saponification, 1.5 g of a composite solution of anti-wear agent melamine cyanurate and zinc dialkyl dithiophosphate, 0.05 g of rust preventive agent benzotriazole, natural cooling to room temperature, grinding twice, and filtering to obtain a finished product.

[0020] Tests on the finished product obtained in the above examples show that the water-based grease has a milky white appearance, a drop point of 100 or more, a penetration degree can reach the No. 1 hardness standard, and abrasion resistance can meet the requirements of basic metal processing conditions.

[0021] The invention uses water-soluble polyether as the bas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of lubricating grease, and particularly relates to environment-friendly water-based lubricating grease and a preparation method thereof. The water-based lubricating grease comprises the following components in percentage by mass: 65-90% of basic liquid, a mixed base thickening agent, 0.5-3% of extreme-pressure anti-wear additive and 0.02-2% of antirust agent, wherein the basic liquid is a mixture of water-soluble polyether and distilled water, and the mixed base thickening agent is generated by reaction of 1-4% of calcium hydroxide and 0.5-1.5% of sodium hydroxide with 6.5-24.5% of stearic acid. The water-based lubricating grease prepared by the method has the advantages of full lubrication and adhesion, good heat transfer and cooling effect and easy cleaning operation and is particularly suitable for occasions such as metal stamping and extrusion machining, metal rolling, metal wire drawing and metal pipeline machining.

Description

technical field [0001] The invention relates to the field of lubricating grease, in particular to an environment-friendly water-based lubricating grease and a preparation method thereof. Background technique [0002] With the continuous consumption of non-renewable resources such as petroleum, the global energy crisis has already appeared, and lubricants closely related to petroleum have become very common in various industries such as industrial equipment and daily necessities. Now most of the lubricants are oil-soluble. In many working conditions, such as cannon barrel cold extrusion self-tightening processing, metal cutting, metal wire drawing, metal punching and extrusion, etc., the grease is one-time use, waste Serious, it is not environmentally friendly; and after the operation is completed, special cleaning agents are required for cleaning, and the cost is very high. Contents of the invention [0003] The invention provides a water-based lubricating grease which ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M173/02C10M119/16C10N30/06
Inventor 李笑笑童蓉李士成岳风树
Owner SHENZHEN EUBO NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap