Preparation method of high performance composite sheet material and high performance composite sheet material

A composite plate, high-performance technology, applied in the direction of chemical instruments and methods, synthetic resin layered products, lamination devices, etc., can solve the problems of no outstanding advantages, no clear improvement in convenience and performance, and achieve cost savings, excellent resistance Combustibility, the effect of simple process

Inactive Publication Date: 2013-08-21
GUANGDONG ZHENGMEI FURNITURE TECH
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although the method disclosed in the above-mentioned patented technology controls the cost of the product, considering that the application of general plates not only needs to consider the wear resistance of the product, but also any defects in functions such as anti-corrosion, fire prevention, waterproof, anti-scratch, etc. will affect For the application of boards, of course, the p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high performance composite sheet material and high performance composite sheet material
  • Preparation method of high performance composite sheet material and high performance composite sheet material

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0033] Examples:

[0034] Such as figure 1 and figure 2 As shown, a method for preparing a high-performance composite board is prepared by preparing a melamine-impregnated veneer composite board and tightly adhering it with artificial boards and raw wood boards to achieve the preparation of the composite board. The melamine-impregnated veneer composite board includes a surface layer 01 And the preparation of the bottom layer 02 or the surface layer 01, the middle layer and the bottom layer 02, specifically including the following steps:

[0035] (1) Preparation of the surface layer 01 of the melamine impregnated veneer composite board: impregnate the raw veneer or technical veneer material in the melamine resin and benzene resin reaction tank, dry separately after the impregnation is completed, and cut into the required size; The ratio of the melamine resin and the benzene resin determines the hardness of the surface layer 01, and the ratio of the melamine resin and the benzene r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of high performance composite sheet material, and the composite sheet material is prepared by preparation of melamine dipping veneer and tight adhesion of wood-based plate and original board. Original veneers or technical veneer materials are impregnated in to a reaction tank containing melamine resin and benzaldehyde, and are dried after completing impregnation, and cut into needed dimensions; the impregnated original veneers or technical veneer are stacked with brown papers or common veneers together, and the materials are pressed together at a high temperature, and then the melamine dipping veneer composite board is formed. The high performance composite sheet material dipping surface layer is polished or directly coated with a toning paint and a waterproof wear resistant surface paint, and the surface treatment improves appearance effect and performance. The toning paint treatment may not be applied, and common surface paints may be coated for realization of surface treatment or the surface paint is not coated. The invention also discloses a high performance composite board with water resistance, heat resistance, arc resistance and excellent flame resistance.

Description

technical field [0001] The invention relates to the technical field of furniture design and manufacture, in particular to a method for preparing a high-performance composite board, and more particularly to a high-performance composite board for realizing the method. Background technique [0002] Melamine is an important organic chemical intermediate product, mainly used to make melamine resin, which has excellent water resistance, heat resistance, arc resistance and excellent flame retardancy. It can be used in the production of decorative boards, used in amino plastics, adhesives, coatings, currency paper strengthening agents, textile auxiliaries, etc. [0003] In the prior art, wooden boards are produced by sticking veneer, but the production process is complicated, and multiple subsequent painting steps are required, the production cost is high, it is not conducive to environmental protection, and the wear resistance is not good. The traditional melamine-impregnated film...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/04B32B27/10B32B27/42B32B37/10B32B38/08
Inventor 李黔安
Owner GUANGDONG ZHENGMEI FURNITURE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap