Complex-calcium-based tetrapolyurea lubricating grease and preparation method thereof
A calcium-based and lubricating grease technology, which is applied in lubricating compositions, petroleum industry, thickeners, etc., can solve the problems of poor comprehensive performance of calcium-based polyurea grease, and achieve excellent comprehensive performance, excellent comprehensive performance, The effect of excellent mechanical stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0044] The present invention also provides a preparation method of composite calcium-based tetrapolyurea grease, the method comprising the following steps:
[0045] (1) In the presence of lubricating base oil, diisocyanate, diamine and monoamine are contacted and reacted, and the mixture obtained after the reaction is heated up and refined, wherein the molar ratio of diisocyanate, diamine and monoamine is (1.9- 2.1):1:(1.9-2.1);
[0046] (2) In the presence of lubricating base oil, calcium hydroxide is contacted with higher fatty acids, dibasic aromatic acids and C1-C6 fatty acids, and the mixture obtained after the reaction is heated and dehydrated;
[0047] (3) The product obtained in step (1) is mixed with the product obtained in step (2).
[0048] According to the method of the present invention, step (1) and step (2) are respectively implemented in different reactors, by preparing tetrapolyurea grease and complex calcium-based grease respectively, and then tetrapolyurea ...
Embodiment 1
[0078] This example is used to illustrate the complex calcium-based tetrapolyurea grease provided by the present invention and its preparation method.
[0079] (1) Preparation of tetrapolyurea grease
[0080] Raw material components: HVI500SN base oil (purchased from ExxonMobil Chemical Company, viscosity at 100°C is 11mm 2 / s): 435g; octadecylamine (purchased from ACROS company): 31.87g; ethylenediamine: 3.56g; 4,4'-diphenylmethane diisocyanate (purchased from ACROS company, MDI): 29.57g;
[0081] First mix 150g of HVI500SN base oil and 29.57g of MDI and heat to 50°C, slowly add 3.56g of ethylenediamine, heat up to 80°C, and react for 30 minutes to obtain mixture A1; mix 150g of HVI500SN base oil with 31.87g of octadecylamine, Heat to 60°C, add to mixture A1, heat up to 80°C, react for 30 minutes, continue to heat up to 210°C, then add 135g of HVI500SN base oil and cool to 100°C, then grind twice with a three-roller mill to obtain tetramer Urea grease.
[0082] (2) Prepara...
Embodiment 2
[0097] This example is used to illustrate the complex calcium-based tetrapolyurea grease provided by the present invention and its preparation method.
[0098] The method for preparing composite calcium-based tetrapolyurea grease according to Example 1, the difference is that, in the process of preparing composite calcium-based grease in step (2), replace terephthalic acid with the same molar amount of isophthalic acid Formic acid to prepare complex calcium-based tetrapolyurea grease.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com