Preparation method of surface coating treating agent capable of improving strength of phosphate strengthened quartz fiber composite material and coating treatment method

A quartz fiber and surface coating technology is applied in the field of preparation and coating treatment of a surface coating treatment agent for improving the strength of phosphate reinforced quartz fiber composite materials, and can solve the mechanical properties of phosphate reinforced quartz fiber composite materials at room temperature and high temperature It can achieve the effect of short processing time, excellent mechanical properties and simple operation.

Inactive Publication Date: 2013-08-28
INST OF PETROCHEM HEILONGJIANG ACADEMY OF SCI
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a surface coating treatment for improving the strength of the phosphate reinforced quartz fiber composite material in order to solve the problem of poor mechanical properties at room te

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0010] Specific embodiment one: a kind of preparation method of the surface coating treatment agent that improves the strength of phosphate reinforced quartz fiber composite material of the present embodiment is carried out according to the following steps:

[0011] The mass ratio of ethanol to thermosetting phenolic resin is 80: (10-30), and the thermosetting phenolic resin is dissolved in ethanol to obtain the surface coating treatment agent.

[0012] The thermosetting phenolic resin described in this embodiment is a commercially available product.

specific Embodiment approach 2

[0013] Embodiment 2: This embodiment differs from Embodiment 1 in that the mass ratio of ethanol to thermosetting phenolic resin is 80: (15-25). Other steps and parameters are the same as those in Embodiment 1.

specific Embodiment approach 3

[0014] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is: the mass ratio of ethanol and thermosetting phenolic resin is 80: (18~22). Other steps and parameters are the same as those in Embodiment 1 or Embodiment 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Bending strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a surface coating treating agent capable of improving the strength of a phosphate strengthened quartz fiber composite material and a coating treatment method, and relates to a preparation method of a surface coating treating agent for phosphate strengthened quartz fiber composite material and a coating treatment method. In order to solve the problems that the phosphate strengthened quartz fiber composite material prepared by using coating anticorrosive treatment in the existing method is bad in mechanical properties at normal temperature and high temperature, the treating agent is prepared by dissolving thermosetting phenolic resin in ethanol so as to obtain the surface coating treating agent. The preparation method comprises the following steps of: immerging quartz fiber in the surface coating treating agent for soaking; and airing after taking out so as to complete the coating treatment. The preparation method of the treating agent is simple, and the coating treatment method is simple; for the phosphate strengthened quartz fiber composite material prepared by taking the quartz fiber after being treated as a base material, the bending strength at the normal temperature reaches to 300MPa, and reaches to 124MPa at 500 DEG C; and the phosphate strengthened quartz fiber composite material can be applied to the high temperature resistance fields of aviation, aerospace, and the like.

Description

technical field [0001] The invention relates to a preparation method and a coating treatment method of a surface coating treatment agent for a phosphate-reinforced quartz fiber composite material. Background technique [0002] In the phosphate-reinforced quartz fiber composite material, due to the strong corrosiveness of phosphate to silica, the quartz fiber without surface coating will react with quartz to form silicic acid during the phosphate curing process due to high temperature and acidic conditions. Severely corrodes the quartz fiber, resulting in a serious decline in the mechanical properties at room temperature and high temperature. [0003] Various methods are used in China for coating anti-corrosion treatment, such as: silicone resin, alumina sol-gel, zirconia sol-gel, etc., but the anti-corrosion effect is not good. The bending strength is lower than 60MPa, and the mechanical properties at room temperature and high temperature are poor, so it is not suitable for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C25/34C04B14/42C04B28/34
Inventor 白雪峰王超曹先启陈泽明李博红王勃
Owner INST OF PETROCHEM HEILONGJIANG ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap