Preparation method of spindle niobium oxides

A niobium oxide and spindle technology, applied in the field of niobium oxide materials, can solve the problems of few reports on nanomaterials, and achieve the effects of simple preparation process, low energy consumption, and high product purity

Inactive Publication Date: 2013-09-11
SOUTHWEST JIAOTONG UNIV
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The sol-gel method can prepare nano-powders with a particle size of less than 100nm and uniform distribution. At the same time, the sol-gel method is also an effective method for preparing porous materials, but the current research on one-dimensional Nb 2 o 5 There are still few reports on nanomaterials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of spindle niobium oxides
  • Preparation method of spindle niobium oxides
  • Preparation method of spindle niobium oxides

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1, a kind of preparation method of spindle niobium oxide, its concrete practice is:

[0026] a. Substrate pre-treatment

[0027] Cut the purchased niobium foil (d=0.2mm) into a size of 10mm*30mm, then perform ultrasonic cleaning in deionized water, alcohol, and acetone solution in sequence, and dry it in the air for later use.

[0028] b. Configure the mixed solution

[0029] In a container containing a mixed solution of hydrogen peroxide and deionized water (20ml of hydrogen peroxide (30wt%) and 20ml of deionized water), add ammonium fluoride, fully dissolve, and configure a mixed solution. The concentration of ammonium fluoride in the mixed solution It is 0.06684mol / L.

[0030] c. Hydrothermal treatment

[0031] Put the niobium foil in step a obliquely into the autoclave, take 20ml of the solution in step b and move it into the inner tank of the autoclave, leaving a gap of 1 mm in the inner cover to facilitate the volatilization of the solution, then seal the autoc...

Embodiment 2

[0035] The preparation of spindle body niobium oxide, its specific practice is:

[0036] a. Substrate pre-treatment

[0037] Cut the purchased niobium foil (d=0.2mm) into a size of 10mm*30mm, then perform ultrasonic cleaning in deionized water, alcohol, and acetone solution in sequence, and dry it in the air for later use.

[0038] b. Configure the mixed solution

[0039] In a container containing a mixed solution of hydrogen peroxide and deionized water (20ml of hydrogen peroxide (30wt%) and 20ml of deionized water), add ammonium fluoride, fully dissolve, and configure a mixed solution. The concentration of ammonium fluoride in the mixed solution It is 0.068mol / L.

[0040] c. Hydrothermal treatment

[0041] Put the niobium foil in step a obliquely into the autoclave, take 20ml of the solution in step b and move it into the inner tank of the autoclave, leaving a gap of 1 mm in the inner cover to facilitate the volatilization of the solution, then seal the autoclave; The re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Large end diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of spindle niobium oxides, which comprises the following specific steps of: carrying out ultrasonic cleaning on a niobium foil sequentially in deionized water, alcohol and an acetone solution, drying the niobium foil in air for later use; in a container filled with a mixed solution of hydrogen peroxide and deionized water, adding and completely dissolving ammonium fluoride so as to obtain a fluorine-containing mixed solution, wherein the concentration of ammonium fluoride in the mixed solution is 0.06684-0.07 mol / L; obliquely putting the niobium foil in a high-pressure reaction kettle, taking 20 parts of the fluorine-containing mixed solution and moving the 20 parts of fluorine-containing mixed solution to a liner of the reaction kettle, carrying out heat preservation on the high-pressure reaction kettle for 15 hours at a temperature of 150 DEG C, cooling the niobium foil to room temperature with the furnace; and taking out a substrate of the niobium foil and spindle niobium oxides growing on the substrate in the high-pressure reaction kettle, washing the substrate for many times by using deionized water, and drying the obtained product so as to obtain a target product. According to the method disclosed by the invention, spindle niobium oxide preparation equipment is simple, and the experiment process is simple and easy to implement.

Description

technical field [0001] The invention relates to the technical field of niobium oxide materials, especially the preparation method of spindle niobium oxide. Background technique [0002] Since the discovery of niobic acid (Nb 2 o 5 ·nH 2 Since O) has unique catalytic properties, the application of niobium oxides in heterogeneous catalysis has attracted widespread attention. For supported Nb 2 o 5 Niobium oxide (NbO) on the catalyst surface x ) species dispersion state and catalytic performance have been studied, due to the support species and Nb 2 o 5 different loads, NbO x Species have different structural states and properties on the support surface. Wachs et al. considered that NbO x The structural state of the species is related to the acidity and alkalinity of the support surface. On the surface of basic oxide supports such as MgO, NbO x Coordinated with highly twisted oxygen six (NbO 6 ) exists in octahedral form, while on acidic oxide supports such as TiO 2...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01G33/00
Inventor 杨峰贾永芳赵勇
Owner SOUTHWEST JIAOTONG UNIV