A technology of polyamide composition and polyamide resin, which is applied in the field of polymer materials, can solve the problems of resin degradation and limited application, and achieve the effect of high fluidity

Inactive Publication Date: 2013-10-02
KINGFA SCI & TECH CO LTD
View PDF3 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned operation methods inevitably bring about the problem of resin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-fluidity PA10T polyamide resin and polyamide composition comprising same

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0042] Embodiment A1~A4: Preparation of PA10T Polyamide Resin A

[0043] In the pressure kettle equipped with magnetic coupling stirring, condenser tube, gas phase port, feeding port and pressure explosion-proof port, add the reaction raw materials according to the ratio in Table 1, and then add benzoic acid, sodium hypophosphite and deionized water; weight of sodium hypophosphite In order to remove 0.1% of the weight of other materials except the ionized water, the weight of deionized water is 30% of the total weight of the materials; vacuum is filled with high-purity nitrogen as protective gas, and the temperature is raised to 220 in 2 hours under stirring. o C, put the reaction mixture at 220 oC stirred for 1 hour, then the temperature of the reaction was raised to 230 with stirring o C; reaction at 230 o The constant temperature of C and the constant pressure of 2.2Mpa were continued for 2 hours, and the pressure was kept constant by removing the water formed. After the...

Example Embodiment

[0046] Embodiments B1~B4: Preparation of PA10T Polyamide Resin B

[0047] In the pressure kettle equipped with magnetic coupling stirring, condenser tube, gas phase port, feeding port and pressure explosion-proof port, add the reaction raw materials according to the ratio in Table 2, then add benzoic acid, sodium hypophosphite and deionized water; weight of sodium hypophosphite In order to remove 0.1% of the weight of other materials except ionized water, the weight of deionized water is 30% of the total weight of the materials; vacuum is filled with high-purity nitrogen as protective gas, and the temperature is raised to 220 in 2 hours under stirring. o C, put the reaction mixture at 220 o C stirred for 1 hour, then the temperature of the reaction was raised to 230 with stirring o C. React at 230 o The constant temperature of C and the constant pressure of 2.2Mpa were continued for 2 hours, and the pressure was kept constant by removing the water formed. After the reacti...

Example

[0050] Embodiment C1~C8 and comparative example 1~3: Preparation of polyamide compositions

[0051] According to the formula in Table 3-4, PA10T polyamide resin A, B, titanium dioxide, talcum powder, and other additives are mixed uniformly in the high-speed mixer, and then added to the twin-screw extruder through the main feeding port, and the reinforcing filler passes through The polyamide composition is obtained after side feeding, extrusion, water cooling, granulation and drying; wherein, the extrusion temperature is 330 o C.

[0052] table 3

[0053]

[0054] Table 4

[0055] Comparative Example 1 Comparative Example 2 Comparative Example 3 PA10T Polyamide A / wt% 0 40 0 PA10T polyamide B / wt% 60 50 0 Polyamide 6T / 66 / wt% 0 0 60 Titanium dioxide / wt% 30 9 30 Talc / wt% 9.8 0.8 9.8 Antioxidant 1098 / wt% 0.1 0.1 0.1 Licowax OP / wt% 0.1 0.1 0.1 Apparent viscosity / Pa s 180 20 105 Spiral flow li...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apparent viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-fluidity PA10T polyamide resin A. The relative viscosity of the PA10T polyamide resin A is 1.2-1.8 in 98% concentrated sulfuric acid at the temperature of 25 DEG C; the amino end group value of the PA10T polyamide resin A is 20-60mol/t and the carboxyl end group value is 70-130mol/t; and benzoic acid accounts for 2-20mol% of repetitive units in the PA10T polyamide resin A. A polyamide composition comprises the following components in percentage by weight: 5-29.8wt% of the PA10T polyamide resin A, 50-94wt% of PA10T polyamide resin B, 0.8-40wt% of mineral filler and 0.2-1wt% of other auxiliaries. The PA10T polyamide resin A disclosed by the invention has the advantages that the apparent viscosity is low and the fluidity is high under the melting condition; and when a certain proportion of the PA10T polyamide resin A is added in semi-aromatic polyamide, the obtained polyamide composition has high fluidity and basically-equal mechanical property and can be applied to occasions with high dimensional requirement on injection molding products.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a high-fluidity PA10T polyamide resin and a polyamide composition composed of it. Background technique [0002] Polyamide is widely used because of its good comprehensive properties, including mechanical properties, heat resistance, wear resistance, chemical resistance and self-lubrication, low coefficient of friction, certain flame retardancy, and easy processing. It is suitable for filling and modifying with glass fiber and other fillers to improve performance and expand application range. In recent years, semi-aromatic polyamides have been focused on development due to their better heat resistance and mechanical properties. [0003] PA10T polyamide resin, which is polymerized from decanedidiamine and terephthalic acid, has low water absorption and high melting point, and is currently developing rapidly. However, compared to PA6T polyamide resin, the melt viscosity of PA10T p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G69/26C08L77/06C08K13/02C08K3/22C08K3/34
CPCC08G69/26C08K3/22C08K3/34C08K2003/2241C08L77/06C08L2205/025
Inventor 张传辉袁志敏蔡彤旻吉继亮曾祥斌曹民夏世勇叶南飚陈大华殷年伟
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap