Anti-termite-type wood plastic composite material and preparation process therefor

A kind of wood-plastic composite material and composite material technology, which is applied in the field of termite-proof wood-plastic composite material and its preparation technology, can solve the problems of short termite-proof durability and poor effect of termite-proof, achieve long-lasting insect-proof effect and ensure interface Compatibility, damage reduction effect

Active Publication Date: 2013-10-16
HUANGSHAN HUASU NEW MATERIAL SCI & TECH CO LTD
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current domestic wood-plastic anti-termite products are simply added with the corresponding anti-termite agent to introduce the anti-termite effect, but the anti-termite effect is not good, and the anti-termite durability is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A termite-resistant wood-plastic composite material, its components and parts by mass are:

[0030] 40 parts of plastic particles, 50 parts of plant fiber, 15 parts of compatibilizer, 20 parts of masterbatch, 3 parts of lubricant, 10 parts of filler, 5 parts of pigment, and 5 parts of functional additives;

[0031] The components and parts by mass in the masterbatch are: 50 parts of plastic particles, 50 parts of inorganic anti-termite agent, 2 parts of lubricant, and 1 part of organic anti-termite agent.

[0032] The plastic particles described are polyethylene, the brand is 5502AA, and the manufacturer is Shanghai Secco Petrochemical;

[0033] The plant fiber is wood powder, the trade mark is M11, and the manufacturer is Lin'an Mingzhu Wood Flour Factory;

[0034] Described compatibilizer is chlorinated polyethylene, the trade mark is 8008, and the manufacturer is Changzhou Huili Trading Co., Ltd.;

[0035] Described lubricant is polyamide, and the trade mark is EBS...

Embodiment 2

[0051] A termite-resistant wood-plastic composite material, its components and parts by mass are:

[0052] 20 parts of plastic particles, 40 parts of plant fiber, 10 parts of compatibilizer, 10 parts of masterbatch, 1 part of lubricant, 5 parts of filler, 2 parts of pigment, 2 parts of functional additive;

[0053] The components and parts by mass in the masterbatch are: 60 parts of plastic particles, 40 parts of inorganic anti-termite agent, 0.5 part of lubricant, and 0.3 part of organic anti-termite agent.

[0054] The plastic particles are polypropylene, the grade is EPS30R, and the manufacturer is Qilu Petrochemical;

[0055] Described plant fiber is bamboo powder, and specification is 80 orders, and manufacturer is Anji Songshan Wood Flour Factory;

[0056]The compatibilizer is ethylene-vinyl acetate copolymer (EVA), the brand is 630, and the manufacturer is Tosoh Corporation of Japan;

[0057] The lubricant is polyethylene wax, the trade mark is CH-100, and the manufac...

Embodiment 3

[0073] A termite-resistant wood-plastic composite material, its components and parts by mass are:

[0074] 30 parts of plastic particles, 45 parts of plant fiber, 10 parts of compatibilizer, 15 parts of masterbatch, 2 parts of lubricant, 10 parts of filler, 3 parts of pigment, 4 parts of functional additives;

[0075] The components and parts by mass in the masterbatch are: 55 parts of plastic particles, 45 parts of inorganic anti-termite agent, 1 part of lubricant, and 0.5 part of organic anti-termite agent.

[0076] The plastic particles described are polyethylene, the brand is 5502, and the manufacturer is Shanghai Secco Petrochemical;

[0077] The plant fiber is rice husk powder with a specification of 60 mesh, and the manufacturer is Huaiyuan Hengrui Bran Powder Processing Factory;

[0078] The compatibilizer is maleic anhydride grafted polypropylene, the trade mark is SZ-3, and the manufacturer is Huangshan Beinuo Technology Co., Ltd.;

[0079] The lubricant is paraffi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to an anti-termite-type wood plastic composite material and a preparation process therefor. The composite material comprises, by weight, 20-40 parts of plastic particles, 40-50 parts of plant fiber, 10-15 parts of compatilizers, 10-20 parts of masterbatches, 1-3 parts of lubricants, 5-10 parts of filling materials, 2-5 parts of pigments and 2-5 parts of functional auxiliaries. The preparation process comprises steps of the masterbatch preparation process and composite material preparation process. The anti-termite-type wood plastic composite material has advantages of inorganic and organic anti-termite agents, maintains the activity of anti-termite agents during the processing and usage of the wood plastic, thus the wood plastic composite material not only has anti-termite functions, but also has certain killing effects on termites, and the anti-termite effects last long. The problem of destruction of mechanical properties of products from inorganic anti-termite agents after addition of anti-termite agents is solved, and the wood plastic composite material has certain toughness intensity and anti-termite performances.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to a termite-proof wood-plastic composite material and a preparation process thereof. technical background: [0002] With the continuous expansion of the application range of wood-plastic composite materials, WPC is increasingly used as a wood substitute for building products, such as wood-plastic doors and windows, stairs, railings, wall panels, floors, tables and chairs, flower stands, wooden houses, wood Pavilions, wooden bridges, wooden villas, landscape balconies, courtyard wooden structures, etc. As a new type of composite material, wood-plastic composite material has a certain termite-proof performance than ordinary wood, but it will still suffer from termite erosion when used in some areas with severe termite diseases and insect pests. Because wood-plastic materials contain a certain amount of wood fiber filler, they can be eaten away and destroyed by ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L23/06C08L23/12C08K13/02C08K3/38C08J3/22B29B9/06B29C47/00
Inventor 洪海洲姚俊叶强汪建设方海兰
Owner HUANGSHAN HUASU NEW MATERIAL SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap