Viscose fiber imitated rattan mat manufacturing process and product
A processing technology, silk imitation rattan mat technology, applied in textiles, papermaking, fabrics, textiles, etc., can solve the problems that the imitation rattan mat will break when soaked in water without waterproof treatment, so as to increase the antistatic performance, increase the feel, The effect of good breathability and adjustment ability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0033] Select grass waste and add CMC for beating, the degree of substitution is 0.5, the viscosity is 800cp, the temperature is 25°C, the concentration is 2%, the amount of CMC is 0.48kg / t slurry, the pH value of the slurry is 7, the reaction time between CMC and slurry is 20 minutes, the CMC The point of adding is to export the good pulp of the thickener before knocking, and beating at low consistency; it is made into semi-finished paper through paper processing technology;
[0034] Spray polyethylene emulsion water-repellent directly on the surface of the semi-finished paper for waterproof treatment, and then dry it thoroughly through a dryer; cut the dried semi-finished paper into sheets according to the specifications of the mat, leaving a margin;
[0035] Use sheet paper to wrap the cotton yarn core into a rope-like paper and roll it into a roll, use the rope-like paper as the weft thread, and ice silk as the warp thread for weaving, so as to obtain the main body of the i...
Embodiment 2
[0039] Select grass waste and add CMC for beating, the degree of substitution is 0.4, the viscosity is 700cp, the temperature is 20°C, the concentration is 1%, the amount of CMC is 0.5kg / t slurry, the pH value of the slurry is 8, the reaction time between CMC and slurry is 15 minutes, and the CMC Adding point is selected in the unknocked pulp pool, medium-consistency beating; semi-finished paper is made through paper processing technology;
[0040] Spray polyvinylidene chloride emulsion water repellant directly on the surface of the semi-finished paper for waterproof treatment, and then dry it thoroughly through a dryer; cut the dried semi-finished paper into sheets according to the specifications of the mat, leaving a margin;
[0041] Use sheet paper to wrap the cotton yarn core into a rope-like paper and roll it into a roll, use the rope-like paper as the weft thread, and ice silk as the warp thread for weaving, so as to obtain the main body of the ice silk imitation rattan m...
Embodiment 3
[0045] Use waste wood raw materials, kraft chemical wood pulp and add modified cellulase for beating: the amount of modified cellulase is 0.47kg / t pulp, the reaction time is 40 minutes, the enzyme use temperature is 50°C, the pH value is 7, and the addition point is selected In the hydropulper, low-consistency beating; through the paper processing process to make semi-finished paper;
[0046] Spray polyorganosilicon water repellent directly on the surface of the semi-finished paper for waterproof treatment, and then dry it thoroughly through a dryer; cut the dried semi-finished paper into sheets according to the specifications of the mat, leaving a margin;
[0047] Use sheet paper to wrap the cotton yarn core into a rope-like paper and roll it into a roll, use the rope-like paper as the weft thread, and ice silk as the warp thread for weaving, so as to obtain the main body of the ice silk imitation rattan mat;
[0048] The main body of the ice silk imitation rattan mat is unde...
PUM
| Property | Measurement | Unit |
|---|---|---|
| Width | aaaaa | aaaaa |