Polishing solution and polishing method thereof

A technology of polishing liquid and sodium dodecylbenzene sulfonate, which is applied in the field of polishing, can solve problems such as high requirements for the use environment and environmental pollution, and achieve the effects of improving roughness, reducing costs, and ensuring safety

Inactive Publication Date: 2013-12-04
WUJIANG JUNDA ELEVATOR PARTS
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The chemical polishing liquid currently used is composed of strong acid or strong alkali, such as sulfuric acid, hydrochloric acid, nitric acid, etc., which will produce a large amount of harmful gas during the polishing process, such as the polishing liquid containing nitric acid will produce a lot of yellow smoke during use , causing serious pollution to the environment
At present, there are also polishing solutions that do not use nitric acid, but strong acids or alkalis such as sulfuric acid and hydrochloric acid are added to them, and there are high requirements for the use environment and operation during use.
At present, there is no more efficient mild polishing fluid on the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of polishing liquid, comprises 10 parts of sodium dodecylbenzene sulfonate by weight component, 10 parts of acetic acid, 0.5 part of organosilicon defoamer, 3 parts of sodium tripolyphosphate, 5 parts of macrogol 2000, glycerin 5 parts, 3 parts of hexamethylenetetramine, 3 parts of copper sulfate, 5 parts of p-hydroxybenzoic acid, 15 parts of citric acid, 3 parts of ammonium chloride, 100 parts of purified water for industrial use.

[0020] Contains the following steps:

[0021] (1) Smooth the flaws and deep scratches on the surface of the stainless steel parts to be treated with sandpaper, and then perform mechanical sandblasting to remove the grinding marks;

[0022] (2) Heat the polishing solution to 80°C;

[0023] (3) Put the stainless steel parts treated in step (1) into the heated polishing solution for 8 minutes to complete the polishing treatment on the surface of the stainless steel parts;

[0024] (4) Take out the stainless steel parts, lower the temp...

Embodiment 2

[0026] A kind of polishing liquid, comprises 15 parts of sodium dodecylbenzene sulfonate by weight component, 12 parts of acetic acid, 1 part of organosilicon defoamer, 12 parts of nano silicon dioxide, 4 parts of sodium tripolyphosphate, polyethylene 6 parts of diol 2000, 6 parts of glycerin, 4 parts of hexamethylenetetramine, 3 parts of copper sulfate, 7 parts of p-hydroxybenzoic acid, 17 parts of citric acid, 4 parts of ammonium chloride, 110 parts of purified water for industrial use.

[0027] Contains the following steps:

[0028] (1) Smooth the flaws and deep scratches on the surface of the stainless steel parts to be treated with sandpaper, and then perform mechanical sandblasting to remove the grinding marks;

[0029] (2) Heat the polishing solution to 76°C;

[0030] (3) Put the stainless steel parts treated in step (1) into the heated polishing solution for 7 minutes to complete the polishing treatment on the surface of the stainless steel parts;

[0031] (4) Take o...

Embodiment 3

[0033] A kind of polishing liquid, comprises 16 parts of sodium dodecylbenzene sulfonate by weight component, 13 parts of acetic acid, 1.5 parts of organosilicon defoamer, 14 parts of nano silicon dioxide, 5 parts of sodium tripolyphosphate, polyethylene 7 parts of diol 2000, 6.5 parts of glycerin, 5 parts of hexamethylenetetramine, 4 parts of copper sulfate, 8 parts of p-hydroxybenzoic acid, 18 parts of citric acid, 5 parts of ammonium chloride, and 113 parts of industrially purified water.

[0034] Contains the following steps:

[0035] (1) Smooth the flaws and deep scratches on the surface of the stainless steel parts to be treated with sandpaper, and then perform mechanical sandblasting to remove the grinding marks;

[0036] (2) Heat the polishing solution to 75°C;

[0037] (3) Put the stainless steel parts treated in step (1) into the heated polishing solution for 6 minutes to complete the polishing treatment on the surface of the stainless steel parts;

[0038] (4) Tak...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polishing solution and a polishing method thereof, wherein the polishing solution comprises the following components in parts by weight: 10-20 parts of sodium doodecyl benzene sulfonate, 10-15 parts of acetic acid, 0.5-2 parts of organosilicon foam killer, 3-8 parts of sodium tripolyphosphate, 5-10 parts of polyethyleneglycol 2000, 5-10 parts of glycerol, 3-8 parts of hexamethylene tetramine, 3-6 parts of cupric sulfate, 5-10 parts of p-hydroxybenzoic acid, 15-20 parts of citric acid, 3-8 parts of ammonium chloride and 100-120 parts of solvent. A stainless steel surface polished with the polishing solution is clean and bright, has higher weatherability, and meanwhile achieves higher service efficiency and a longer service life.

Description

technical field [0001] The invention belongs to the technical field of polishing, in particular to a polishing liquid and a polishing method thereof. Background technique [0002] Stainless steel refers to steel resistant to weak corrosive media such as air, steam, water, and chemically corrosive media such as acids, alkalis, and salts. At present, there are many products of stainless steel materials, the shapes of parts are complex and diverse, and there are many processes in the processing process. Stainless steel will inevitably produce scratches, bruises, etc. during use, which makes stainless steel products unable to be used normally. Due to the complex and diverse shapes and sizes of stainless steel parts, the traditional mechanical polishing method can no longer meet the requirements of the product, and the electrolytic polishing method cannot meet the requirements of products with a certain size, and the uniformity of electrolytic polishing is relatively poor. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23F3/06
Inventor 徐志坚
Owner WUJIANG JUNDA ELEVATOR PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap