Electrothermal high-temperature-resistant carbon fiber paper and preparation method thereof

A technology of carbon fiber paper and carbon fiber, which is applied in the direction of synthetic cellulose/non-cellulose material pulp/paper, fiber raw material processing, papermaking, etc., can solve the problems that cannot meet the application requirements of high-end use occasions, low temperature resistance level, etc., and achieve improvement Flame retardant effect, excellent performance, and the effect of improving safety performance

Active Publication Date: 2013-12-18
YANTAI METASTAR SPECIAL PAPER
View PDF11 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Most of the electrothermal carbon fiber paper currently used in the market is added with plant fibers and synthetic fibers with lower temperature resistance levels during the papermaking process, resulting in a lower temperature resistance level, and the working temperature is basically below 80°C.
Unable to meet the application requirements of some high-end use occasions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrothermal high-temperature-resistant carbon fiber paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A slurry of electric heating and high temperature resistant carbon fiber paper, the fibers in the slurry are composed of the following components by mass percentage: carbon fiber I: 65%; carbon fiber II: 15%; meta-aramid fibrids: 20%; Wherein, the length of the carbon fiber I is 1-5mm, and the fineness is 1.5D; the length of the carbon fiber II is 8-10mm, and the fineness is 1.5D; the beating degree of the meta-aramid precipitated fiber is 40-80 °SR.

[0035] A method for preparing the slurry, comprising the steps of:

[0036] (1) Preparation of three kinds of slurry:

[0037] Preparation of carbon fiber I slurry: add 1 part of carbon fiber I to 100 parts of water, stir and disperse for 5 minutes with a stirrer, the stirring speed is 300r / min, make the mixed liquid have no lumps visible to the naked eye, then add 400 parts of water, and then Use an ultrasonic dispersing device to disperse the mixed solution for 10 minutes, while stirring the mixed solution, so that th...

Embodiment 2

[0047] A slurry of electric heating and high temperature resistant carbon fiber paper, the fibers in the slurry are composed of the following components by mass percentage: carbon fiber I: 70%; carbon fiber II: 5%; meta-aramid fibrids: 25%; Wherein, the length of the carbon fiber I is 1-5mm, and the fineness is 1.5D; the length of the carbon fiber II is 8-10mm, and the fineness is 1.5D; the beating degree of the meta-aramid precipitated fiber is 40-80 °SR.

[0048] A method for preparing the slurry, comprising the steps of:

[0049] (1) Preparation of three kinds of slurry:

[0050] Preparation of carbon fiber I slurry: add 1 part of carbon fiber I to 100 parts of water, stir and disperse for 5 minutes with a stirrer, the stirring speed is 300r / min, make no lumps visible to the naked eye in the mixed solution, then add 300 parts of water, and then Use an ultrasonic dispersing device to disperse the mixed solution for 5 minutes, while stirring the mixed solution, so that ther...

Embodiment 3

[0060] A slurry of electric heating and high temperature resistant carbon fiber paper, the fibers in the slurry are composed of the following components by mass percentage: carbon fiber I: 65%; carbon fiber II: 30%; meta-aramid fibrids: 5%; Wherein, the length of the carbon fiber I is 1-5mm, and the fineness is 1.5D; the length of the carbon fiber II is 8-10mm, and the fineness is 1.5D; the beating degree of the meta-aramid precipitated fiber is 40-80 °SR.

[0061] A method for preparing the slurry, comprising the steps of:

[0062] (1) Preparation of three kinds of slurry:

[0063] Preparation of carbon fiber I slurry: add 5 parts of carbon fiber I to 100 parts of water, stir and disperse for 10 minutes with a stirrer, and the stirring speed is 500r / min, so that there are no lumps visible to the naked eye in the mixed solution, then add 700 parts of water, and then Use an ultrasonic dispersing device to disperse the mixed solution for 10 minutes, while stirring the mixed so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses pulp of electrothermal high-temperature-resistant carbon fiber paper. Fiber in the pulp comprises the following components in percentage by weight: 40-70% of carbon fiber I, 5-30% of carbon fiber II and 5-30% of meta-aromatic acrylic fibrid, wherein the length of the carbon fiber I is 1-5mm, and the fiber number is 1.5D; the length of the carbon fiber II is 8-10mm, and the fiber number is 1.5D; the pulp beating degree of the meta-aromatic acrylic fibrid is 40-80 degree SR. The invention further discloses a preparation method of the pulp, meta-aromatic acrylic fibrid / carbon fiber composite electrothermal high temperature-resistant carbon fiber paper prepared by using the pulp and a preparation method thereof. According to the method disclosed by the invention, the mechanical strength and the operability of the composite paper are significantly improved, paper breaking during papermaking is reduced, the production efficiency is improved, the temperature resistance level and the flame retardance of the composite carbon fiber paper are simultaneously upgraded, and the safety performance is improved.

Description

technical field [0001] The invention relates to a papermaking method, in particular to a meta-aramid fibrid fiber / carbon fiber composite electric heating and high temperature resistant carbon fiber paper and a preparation method thereof. Background technique [0002] Carbon fiber is made of raw material fibers with a high carbon content (usually above 90%), placed in an inert gas, subjected to thermally stable oxidation at 200-300°C, carbonization and graphitization at 1000-2000°C. Carbon fiber has high temperature resistance, abrasion resistance, electrical conductivity, heat conduction and corrosion resistance, etc. It has significant anisotropy in shape, is soft, can be processed into various fabrics, has a small specific gravity, and exhibits high strength along the fiber axis. [0003] Electric heating carbon fiber paper can be used for heating in public bathrooms, hot yoga, sauna rooms, and massage rooms. Moreover, because of its safety, high efficiency, easy control,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H13/50D21H13/26
Inventor 王志新孙静孙岩磊王川光
Owner YANTAI METASTAR SPECIAL PAPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap