Inorganic non-combustible safe aluminum composite panel

An aluminum composite panel, safety-level technology, applied in the direction of layered products, chemical instruments and methods, metal layered products, etc., to achieve the effects of facilitating molding, increasing viscosity, and improving material fluidity

Inactive Publication Date: 2015-07-01
山东吉祥装饰建材有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although some research institutions now improve its fire performance by adding various flame retardant components to polyethylene, it is difficult to make it truly safe and smoke-free.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inorganic non-combustible safe aluminum composite panel
  • Inorganic non-combustible safe aluminum composite panel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An inorganic non-combustible safety-grade aluminum composite panel, which consists of an aluminum base material, an inorganic core plate and an aluminum base material from top to bottom, and is prepared by hot-pressing continuous composite molding. The gap between the aluminum base material and the inorganic core plate is And between the inorganic core board and the aluminum substrate, it is made of polymer bonding material, and the thickness of the polymer bonding material is 0.1mm;

[0019] The above-mentioned inorganic core board is prepared from powder, white latex, polypropylene alcohol and water, wherein the weight ratio of powder, white latex, polypropylene alcohol and water is 89:7:4:20; the powder is made of hydrogen oxidized Aluminum, magnesium oxide, silicon carbide powder, anhydrous calcium sulfate and borax are prepared according to a weight ratio of 73:11:7:7:2; the particle diameters of the silicon carbide powder and borax are controlled above 100 mesh; I...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of advanced materials, and discloses an inorganic non-combustible safe aluminum composite panel. The composite panel comprises an aluminum substrate, an inorganic core plate and an aluminum substrate from top to bottom and is prepared in a hot-pressing continuous composite forming mode, and the aluminum substrates and the inorganic fireproof core layer are adhered through macromolecule adhesives. The composite panel is high in flame resistance and safety and has good application prospects.

Description

technical field [0001] The invention belongs to the field of new materials, and in particular relates to an inorganic non-combustible safety grade aluminum composite board. Background technique [0002] Aluminum-plastic composite panel (English name: aluminum plastic composite panel), referred to as aluminum-plastic panel, refers to a three-layer composite panel with plastic as the core layer and aluminum on both sides, and the surface of the product is covered with decorative and protective coatings. Layer or film (commonly referred to as coating unless otherwise specified) as the decorative surface of the product. [0003] According to the purpose: 1. Aluminum-plastic panels for building curtain walls: the minimum thickness of the upper and lower aluminum panels should not be less than 0.50mm, and the total thickness should not be less than 4mm. The aluminum material should meet the requirements of GB / T3880. Generally, 3000, 5000 series aluminum alloy plates should be use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B9/04B32B15/082B32B15/04B32B33/00
Inventor 陈杰刘继文白新桂杨玉彬
Owner 山东吉祥装饰建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com