Water-based cast steel coating

A steel casting and coating technology, applied in the direction of coating, casting mold, casting mold composition, etc., can solve the problems of high surface roughness of castings, coating is easy to stick to sand, easy to stain, etc., to avoid the difficulty of sand cleaning and ensure the quality of castings Quality, thin and even coating results

Inactive Publication Date: 2014-01-29
QINGDAO LIANGLI PRECISION CASTING
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional cast steel materials use expensive zircon powder or graphite powder as the main raw material, and the graphite powder used is heavy in color, easy to dye, and mostly radioactive
Furthermore, after the traditional quartz sand coating is processed at high temperature, the coating is prone to sand sticking and cracking, the surface roughness of the casting is high, it is difficult to meet the quality standard, and the amount of residual waste remains high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] 50 parts of kyanite powder, 3 parts of attapulgite, 3 parts of magnesium chloride, 4 parts of barium chloride, 1.5 parts of resin, 2 parts of silica gel, and 2.5 parts of emulsifier. Pour the above-mentioned raw materials into a ball mill, add an appropriate amount of water, and stir at high speed for 30 minutes to obtain the product.

Embodiment 2

[0013] 60 parts of kyanite powder, 2 parts of attapulgite, 4 parts of magnesium chloride, 0.5 parts of barium chloride, 0.2 parts of resin, 3 parts of silica gel, and 3 parts of emulsifier. Pour the above-mentioned raw materials into a ball mill, add an appropriate amount of water, and stir at high speed for 30 minutes to obtain the product.

Embodiment 3

[0015] 70 parts of kyanite powder, 1.5 parts of attapulgite, 5 parts of magnesium chloride, 5 parts of barium chloride, 2 parts of resin, 0.5 part of silica gel, and 0.5 part of emulsifier. Pour the above-mentioned raw materials into a ball mill, add an appropriate amount of water, and stir at high speed for 30 minutes to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-based cast steel coating which comprises the following raw materials in parts by weight: 50-70 parts of kyanite powder, 0.5-3 parts of attapulgite, 1-5 parts of magnesium chloride, 0.5-6 parts of barium chloride, 0.2-2 parts of resins, 0.1-3 parts of silica gel and 0.1-3 parts of an emulsifier. The water-based cast steel coating provided by the invention is applicable to brush-coating resin sands and synthesized sand moulds. Magnesium chloride and barium chloride are added into the coating for easy shelling and preventing sand burning, so that the strength of the coating is improved, the resistance of the coating to high temperature molten steel is improved, the roughness on the casting surface is effectively improved, and the quantity of waste products is greatly reduced. The water-based cast steel coating has a greater market prospect.

Description

technical field [0001] The invention relates to a paint, in particular to a water-based cast steel paint. Background technique [0002] In recent years, with the development of China's industry, the requirements for steel materials are getting higher and higher. Traditional cast steel materials use expensive zircon powder or graphite powder as the main raw material, and the graphite powder used is heavy in color, easy to dye, and mostly radioactive. Furthermore, after the high-temperature treatment of the traditional quartz sand coating, the coating is prone to sand sticking and cracking, the surface roughness of the casting is relatively high, it is difficult to meet the quality standard, and the amount of residual waste remains high. [0003] The purpose of the present invention is to overcome the above defects, to produce a novel water-based cast steel coating that is easy to shell, high temperature resistant and sand sticking resistant. The object of the present invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00
Inventor 段文良
Owner QINGDAO LIANGLI PRECISION CASTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com