Process of utilizing wood plastic composite for manufacturing formaldehyde-free bending glued parts

A technology of wood-plastic composites and parts, which is applied in the direction of manufacturing tools, wood processing appliances, and the joining of wooden veneers. It can solve the problems of inability to make curved furniture parts, reduce the bending performance of veneers, and affect the environmental protection of furniture, etc. problems, to achieve the effect of improving the surface decoration effect, solving the problem of formaldehyde pollution, and low requirements for equipment and molds

Active Publication Date: 2014-01-29
FUJIAN AGRI & FORESTRY UNIV
View PDF12 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the traditional production process, multi-layer glued curved wood furniture uses rotary-cut veneer as the core board and sliced ​​veneer as the surface board. Aldehyde adhesives are bonding materials, and there are different degrees of free formaldehyde in the prepared furniture products, which seriously affects the environmental protection of furniture and reduces the added value of products
At present, there has been research on rolling dense pinholes on the veneer surface, using high-density polyethylene (HDPE) plastic film as an adhesive, and making flat plywood by hot pressing according to the conventional plywood blanking method, but the technology cannot be used to make curved plywood. For furniture parts, due to the dense pinholes rolled on the surface of the veneer, the bending performance of the veneer is reduced, which is easy to cause the slab to break during the bending process, and the scrap rate increases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process of utilizing wood plastic composite for manufacturing formaldehyde-free bending glued parts
  • Process of utilizing wood plastic composite for manufacturing formaldehyde-free bending glued parts

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] (1) Preparation of "C" type chair back curved parts: According to the large radius of curvature of the part (650 mm), select the Eucalyptus veneer, the thickness of the veneer is 1.5 mm, and the moisture content of the veneer is 10%. The glued surface is processed by rolling holes, the pores are irregularly distributed, and the number of pores is 20-30 / cm 2 Between, the veneer is cut into specifications length × width: 400 × 250mm;

[0016] (2) Cutting the prefabricated polyethylene plastic film to a size 2mm larger in width than the veneer;

[0017] (3) According to the part thickness of 15 mm, combined with the thickness of the veneer and plastic film and the compression rate of the pressing and bending process, the layers of 11 layers of veneer and 10 layers of plastic film are alternately stacked to form the billet. Both sides are veneer;

[0018] (4) Place the slab in a hard mold made of "C" type laminated lumber, use high-frequency heating to heat and pressu...

Embodiment 2

[0022] (1) Preparation of "L"-shaped chair back and seat integrated curved parts: According to the large radius of curvature of the part (100 mm), birch veneer is selected, the thickness of the veneer is 1.5 mm, and the moisture content of the veneer is 10%. And carry out rolling hole treatment on the veneer glued surface, the pores are irregularly distributed, and the number of pores is 20-30 / cm 2 , the veneer is cut into specifications length × width: 1000 × 400 mm;

[0023] (2) Cutting the prefabricated polyethylene plastic film to a size 2mm larger in width than the veneer;

[0024] (3) According to the part thickness of 15 mm, combined with the thickness of the veneer and plastic film and the compression rate of the pressing and bending process, the layers of 11 layers of veneer and 10 layers of plastic film are alternately stacked to form the billet. Both sides are veneer

[0025] (4) Place the slab in a hard mold made of "L"-shaped laminated lumber, use high-frequen...

Embodiment 3

[0029] (1) Preparation of curved parts of armrest of "U"-shaped leisure chair: According to the small curvature radius of the part (60 mm), choose ash veneer, the thickness of the veneer is 1.5 mm, and the moisture content of the veneer is 12%. The veneer glued surface is processed by rolling holes, the pores are irregularly distributed, and the number of pores is 20-30 / cm 2 Between, the veneer is cut into a specification length×width: 800×220 mm;

[0030] (2) Cutting the prefabricated polyethylene plastic film to a size 2mm larger than the average width of the veneer;

[0031] (3) According to the thickness of the part is 10 mm, combined with the thickness of the veneer, plastic film and the compression rate of the pressurization and bending process, the layers of 9 layers of veneer and 8 layers of plastic film are alternately stacked to form the billet. Both sides are veneer

[0032] (4) Place the slab in a hard male and female mold made of "U"-shaped laminated wood, i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a new process of utilizing single-board / plastic film composite for manufacturing formaldehyde-free bending glued furniture parts. A plastic film serves as bonding material, a wooden single board serves as a basic unit, rolling hole processing is performed on a single board gluing face, tree type, thickness and specification of the single board are selected according to product usage, and a blank can be assembled, the board blank is placed in a special die to heat and press in high frequency, the board blank is bent, glued and formed, the plastic film is solidified after being cooled, and formaldehyde-free bending glued furniture parts are obtained. The process is simple and low in producing cost; the products are free of pollution and recyclable during manufacture, processing and usage, and has the advantages of environment protection, energy efficiency and efficiency, an environment friendly, safe and healthy consumption concept of the wood industry and the furniture industry can be met, and the process has extensive application value.

Description

technical field [0001] The invention is a new environmental protection technology suitable for industrialized manufacturing of curved formaldehyde-free furniture components, which belongs to the technical field of curved wood furniture production. Background technique [0002] The bending and gluing process of multi-layer veneers is an essential process for preparing curved furniture parts, and is widely used in the production of modern curved wood furniture. In the traditional production process, multi-layer glued curved wood furniture uses rotary-cut veneer as the core board and sliced ​​veneer as the surface board. Aldehyde adhesives are bonding materials, and there are different degrees of free formaldehyde in the prepared furniture products, which seriously affects the environmental protection of furniture and reduces the added value of products. At present, there has been research on rolling dense pinholes on the veneer surface, using high-density polyethylene (HDPE) ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27D1/06B27D1/08
Inventor 叶翠仙唐兴平徐志杰陈月琴杨伟星
Owner FUJIAN AGRI & FORESTRY UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com