Corrosion-resistant stainless steel coffee pot material and preparation method thereof

A technology for stainless steel and coffee pot, applied in the field of stainless steel material and its preparation, can solve the problems of rising production cost, weak corrosion resistance of stainless steel, limited use range of stainless steel, etc.

Active Publication Date: 2014-01-29
WANBAOLI STAINLESS STEEL PRODS DONGGUAN
View PDF13 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The patent application with application number 200410047238.6 proposes to add 1.5-2.9% copper to nickel-saving austenitic stainless steel to achieve antibacterial effect, but due to the limited antibacterial ability of copper ions alone (about 1% of silver ions of the same weight), Therefore, the amount of copper added is relatively high, and the copper content of 2-5% will deteriorate the thermoplasticity of the steel, resulting in a decrease in performance, and after the copper is added,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A kind of corrosion-resistant stainless steel coffee pot material of the present embodiment comprises the following preparation steps:

[0051] a. Melt the cast iron in a vacuum induction furnace. When the cast iron starts to melt, add 16.00% of Cr element. When the cast iron is completely melted, add W 0.25%, V 0.40%, and Mo 3.00%. After the cast iron is completely melted, add it for 65 minutes C 0.03%, Cr 16.00%, Si 0.80%, Mn 0.60%, Ni 2.00%, B 0.0001%, N 0.18%, S≤0.004%, P≤0.014%, the rest is Fe and unavoidable impurity elements, the steel The aqueous solution is cast into a consumable electrode in a metal mold;

[0052] b. Carry out vacuum arc remelting or electroslag remelting refining on the cast consumable electrode to further reduce the content of impurity elements and smelting defects, and reduce the segregation of alloying elements to make electroslag ingots. The melt casting temperature is 1560°C;

[0053] c. The electroslag ingot is made into stainless steel...

Embodiment 2

[0057] A kind of corrosion-resistant stainless steel coffee pot material of the present embodiment comprises the following preparation steps:

[0058] a. Melt the cast iron in a vacuum induction furnace. When the cast iron starts to melt, add 18.00% Cr element. When the cast iron is completely melted, add W 0.30%, V 0.50%, and Mo 3.75%, and add it 70 minutes after the cast iron is completely melted C 0.045%, Si 1.00%, Mn 0.80%, Ni 2.50%, B 0.001%, N 0.20%, S≤0.004%, P≤0.014%, and the rest are Fe and unavoidable impurity elements. In-cast as a consumable electrode;

[0059] b. Carry out vacuum arc remelting or electroslag remelting refining on the cast consumable electrode to further reduce the content of impurity elements and smelting defects, and reduce the segregation of alloying elements to make electroslag ingots. The melt casting temperature is 1630°C;

[0060] c. The electroslag ingot is made into a stainless steel sheet, and then the stainless steel sheet is subjected...

Embodiment 3

[0064] A kind of corrosion-resistant stainless steel coffee pot material of the present embodiment comprises the following preparation steps:

[0065] a. Melt the cast iron in a vacuum induction furnace. When the cast iron starts to melt, add 20.00% of Cr element. When the cast iron is completely melted, add W 0.35%, V 0.60%, and Mo 4.50%. After the cast iron is completely melted, add it for 80 minutes. C 0.06%, Si 1.20%, Mn 1.00%, Ni 3.00%, B 0.002%, N 0.22%, S≤0.004%, P≤0.014%, and the rest are Fe and unavoidable impurity elements. In-cast as a consumable electrode;

[0066] b. Carry out vacuum arc remelting or electroslag remelting refining on the cast consumable electrode to further reduce the content of impurity elements and smelting defects, and reduce the segregation of alloying elements to make electroslag ingots. The melt casting temperature is 1700°C;

[0067] c. The electroslag ingot is made into stainless steel sheet, and then the stainless steel sheet is subject...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the fields of stainless steel materials and preparation technology thereof, in particular relates to a corrosion-resistant stainless steel coffee pot material and a preparation method thereof. The corrosion-resistant stainless steel coffee pot material comprises the following chemical components in percentage by mass: 0.03-0.06% of C, 16-20% of Cr, 0.8-1.2% of Si, 0.6-1% of Mn, 2-3% of Ni, 0.0001-0.002% of B, 0.4-0.6% of V, 3-4.5% of Mo, 0.25-0.35% of W, 0.18-0.22% of N, less than or equal to 0.004% of S, less than or equal to 0.014% of P, 0.25-0.35% of Ag, 2.5-3.5% of Cu, 0.001-0.012% of Ce, 0.03-0.08% of La, and the balance of Fe and inevitable impurity elements. The corrosion-resistant stainless steel coffee pot material has strong machining property, wear corrosion resistance and antibacterial property.

Description

technical field [0001] The invention relates to the technical field of stainless steel materials and their preparation, in particular to a corrosion-resistant stainless steel coffee pot material and a preparation method thereof. Background technique [0002] With the rapid development of the metallurgical industry and the improvement of daily life standards, the use of stainless steel has greatly increased, and a large number of beautiful and durable stainless steel products have entered the field of civilian consumption. Among them, the use of stainless steel in utensils and kitchen supplies accounts for the vast majority. most. Stainless Steel (Stainless Steel) refers to steel resistant to weak corrosive media such as air, steam, water, and chemically corrosive media such as acid, alkali, and salt. It is also called stainless acid-resistant steel. In practical applications, the steel resistant to weak corrosion medium is often called stainless steel, and the steel resista...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/54
Inventor 焦德宏
Owner WANBAOLI STAINLESS STEEL PRODS DONGGUAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap