Iron-adhesive highway asphalt and preparation method thereof

A road and asphalt technology, applied in building components, building insulation materials, buildings, etc., can solve the problems of high cost, poor adhesion, low temperature resistance, etc.

Active Publication Date: 2014-02-26
辽宁瑞德公路科技有限公司
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, in the production of asphalt materials for iron-bonded roads, there are Modifi Company in Wuhan, Hubei Province and Zhixiang Technology Engineering Co., Ltd. in Chongqing. However, their products have defects of high cost, and are not resistant to low temperature. Difference

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Example 1 Preparation of iron-bonded road asphalt

[0038] The formula is:

[0039] 90# base asphalt 40 kg, styrene-butadiene-styrene triblock copolymer (SBS) 6 kg, aromatic oil 10 kg, aviation kerosene 5 kg, engine oil (No. 46 lubricating oil) 5 kg, natural rubber material (The particulate matter of vulcanized products containing natural rubber is the crushed product of the top part of the truck tire. The content of natural rubber is about 50%, and the particle size of the crushed product is 30 mesh) 20 kg, terpene resin 5 kg, coconut oil Acid 2 kg, EVA (polyvinyl acetate) 5 kg, kaolin 15 kg, APAO 5 kg, PE (polyethylene) 3 kg, phosphoric acid 0.5 kg.

[0040] The preparation method is:

[0041] Heat 90# matrix asphalt to 160℃ to melt, then add styrene-butadiene-styrene triblock copolymer, aromatic oil, aviation kerosene and engine oil, heat to 180℃, grind 4 times with colloid mill, and then add For the remaining materials in the formula, continue to stir and develop for 30 m...

Embodiment 2

[0051] Example 2 Preparation of iron-bonded road asphalt

[0052] The formula is:

[0053] 90# base asphalt 30 kg, styrene-butadiene-styrene triblock copolymer (PSBS) 8 kg, aromatic oil 6 kg, aviation kerosene 4 kg, engine oil (No. 46 lubricating oil) 8 kg, EPDM glue 15 Kg, terpene resin 3 kg, coconut acid: 3 kg, EVA (polyvinyl acetate) 4 kg, kaolin 10 kg, APAO 7 kg, PE (polyethylene) 2 kg, phosphoric acid 1 kg.

[0054] The preparation method is the same as in Example 1.

Embodiment 3

[0055] Example 3 Preparation of iron-bonded road asphalt

[0056] The formula is:

[0057] 90# matrix asphalt 20 kg, styrene-butadiene-styrene triblock copolymer (SIS) 10 kg, aromatic oil 3 kg, aviation kerosene 2 kg, engine oil (No. 46 lubricating engine oil) 10 kg, SBR (butyl Benzene rubber) 10 kg, terpene resin 2 kg, coconut acid 5 kg, EVA (polyvinyl acetate) 2 kg, kaolin 5 kg, APAO 3 kg, PE (polyethylene) 5 kg, phosphoric acid 2 kg.

[0058] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an iron-adhesive highway asphalt which is prepared from the following components in parts by weight: 20-40 parts of 90# matrix asphalt, 3-10 parts of styrene-butadiene-styrene triblock copolymer, 3-10 parts of aromatic oil, 2-5 parts of aviation kerosene, 5-10 parts of machine oil, 10-20 parts of rubber, 2-5 parts of terpene resin, 1-5 parts of organic acid, 2-5 parts of adhesive elastomer material, 5-15 parts of kaolin, 3-7 parts of APAO, 2-5 parts of polyethylene and 0.5-2 parts of phosphoric acid. The iron-adhesive highway asphalt has the advantages of low temperature resistance, no embrittling at low temperature, high adhesive force for steel surfaces, and excellent water resistance, and is suitable for cold areas.

Description

[0001] Technical field [0002] The invention relates to a sticky iron road asphalt and a preparation method thereof. Background technique [0003] Iron-bonded road asphalt material, also known as steel-bonded road asphalt material, is similar to the waterproof adhesive layer of conventional steel surface road paving and the lower steel surface contact layer. The iron-bonded highway asphalt material should meet the following two requirements: one is firm adhesion to the steel surface, and the other is waterproof, acting as a waterproof adhesive layer, and the surface of ordinary expressways has a certain degree of water permeability. Put an end to the contact of water and steel, and prevent the rust and corrosion of steel on the surface of the bridge (Scheme design and experimental study of waterproof bonding layer for steel bridge deck pavement; Zhang Lanjun, Mou Jianbo). [0004] At present, in the production of iron-bonded highway asphalt materials, domestic products are pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L7/00C08L53/02C08L45/00C08L23/08C08L23/12C08L23/06C08L23/16C08L9/06C08L9/00C08L75/04C08K13/02C08K5/01C08K3/34C08K3/32C08K5/09
Inventor 王晓伟刘京澎李兆顺屈丰来张海军徐明志陈有卿刘岩马绍平
Owner 辽宁瑞德公路科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com