A kind of measuring method of carbon black content

A technology of carbon black content and measurement method, which is applied in the direction of weighing by removing certain components, can solve the problems of poor repeatability and inaccurate measurement of carbon black content, and achieve the effect of high accuracy

Active Publication Date: 2015-12-02
成都菲斯特新材料有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to our company's experiments, in the case of calcium carbonate fillers, especially in the case of high calcium carbonate fillers, the above-mentioned standards are basically inaccurate in measuring the carbon black content, and the repeatability is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of measuring method of carbon black content
  • A kind of measuring method of carbon black content
  • A kind of measuring method of carbon black content

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1 contains the test method of carbon black content in calcium carbonate plastic product A

[0033] This test method includes the following steps:

[0034] Step 1. Preparation stage: Check that the pressure of nitrogen and oxygen cylinders should be less than 1MPa to ensure no air leakage;

[0035] Porcelain boat should be heated to 550°C to remove its attached water and impurities, weigh the porcelain boat m (constant weight) at room temperature to be 12.7819g, and set aside; the sample (including CaCO 3 Black masterbatch (referred to as masterbatch) is baked at 95°C for 2 hours to remove the attached moisture of the sample, weigh the masterbatch m1=1.0021g at room temperature, and set aside; connect the test equipment.

[0036] Step 2. Use a carbon black content tester to perform pyrolysis and calcination tests on the masterbatch:

[0037] Place the porcelain boat with the masterbatch in the center of the quartz tube of the carbon black content tester tu...

Embodiment 2

[0054] The test method of carbon black content in the embodiment 2 calcium carbonate plastic products B

[0055] In this example, the test sample gets the same black masterbatch containing calcium carbonate in Example 1, and its carbon black content is 30 ± 1%; the calcium carbonate content is about 30%.

[0056] The test steps are basically the same as in Example 1, the difference is:

[0057] Step 1. In the preparation stage: the porcelain boat m (constant weight) is 12.4312g, and the masterbatch m1 is 0.9981g;

[0058] Step 3. Weighing after complete pyrolysis of the masterbatch: When the exhaust of the quartz tube does not make the lime water turbid, stop the tube electric furnace

[0059] Heating; when the temperature drops to 400°C, turn on and off the nitrogen gas to gradually lower the masterbatch in the porcelain boat to room temperature, and then weigh the weight of the porcelain boat containing the pyrolyzed masterbatch m2=0.4670g;

[0060] Step 4. Calcining the c...

Embodiment 3

[0063] The test method of carbon black content in the embodiment 3 calcium carbonate plastic products C

[0064] In this example, the test sample gets the same black masterbatch containing calcium carbonate in Example 1, and its carbon black content is 30 ± 1%; the calcium carbonate content is about 30%.

[0065] The test steps are basically the same as in Example 1, the difference is:

[0066] Step 1. In the preparation stage: the porcelain boat m (constant weight) is 11.2512g, and the masterbatch m1 is 1.0034g;

[0067] Step 2. Use a carbon black content tester to perform pyrolysis and calcination tests on the masterbatch:

[0068] Sample pyrolysis stage and pyrolysis standard: the ceramic boat placed in the quartz tube is heated to make the master material in the porcelain boat warm

[0069] The temperature is gradually increased, while heating, nitrogen is passed through the quartz tube, and the masterbatch is pyrolyzed in the nitrogen environment; the pyrolysis process ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of determination of the content of plastic products and particularly relates to a determination method for the content of carbon black. The determination method comprises the following steps: pre-treating and weighing a test sample and a porcelain boat-shaped disc; putting the test sample and the porcelain boat-shaped disc into a carbon black tester quartz tube; carrying out pyrolysis on the test sample under the environment of introducing nitrogen; after finishing the pyrolysis, cooling and cutting off the nitrogen; weighing the porcelain boat-shaped disc filled with the pyrolyzed test sample; putting the weighed porcelain boat-shape disc filled with the pyrolyzed test sample into the carbon black tester quartz tube; introducing oxygen and calcining; after calcining completely, turning off a machine and cutting off the oxygen; cooling; weighing at a room temperature; and calculating the content of the carbon black. Clarified lime water is used as a pyrolysis indication; if carbonate in the test sample is not completely decomposed, CO2 in a test is exhausted and air bubbles in the lime water become muddy. The pyrolysis is continually carried out until the lime water is not changed; when the lime water keeps clean, the carbonate is completely decomposed. The detection method is accurate and high in repeatability; the difficulty of determining the content of the carbon black in a plastic product containing the carbonate is successfully solved and the determination method is applicable to determining the content of the carbon black in plastic.

Description

technical field [0001] The invention belongs to the field of measuring the content of plastic products, in particular to a method for measuring the content of carbon black. Background technique [0002] Testing the carbon black content in black plastic products is required in the plastic processing industry at home and abroad. There is only "GB / 13021-91 Determination of Carbon Black Content in Polyethylene Pipes and Fittings" in China, and this method is also applicable to the determination of carbon black in polyolefin pipes and fittings. This standard follows ISO6964-1986 and is suitable for testing polyolefin products without fillers. The basic principle is to "pyrolyze a certain amount of sample at 550±50°C for about 45min in a nitrogen flow, and calcinate at 900±50°C. Calculate the carbon black content according to the mass difference before and after pyrolysis and calcination." This standard applies to testing polyolefin products without fillers. It is an inevitable...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N5/04
Inventor 彭志远薛燕李小华
Owner 成都菲斯特新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com