Medical chitosan compound moisturizing dressing and preparation method thereof

A chitosan and chitosan solution technology, applied in medical science, bandages, absorbent pads, etc., can solve the problems of limited healing effect of chronic wounds, slow wound healing, loss of bioactive substances, etc., to promote rapid healing, The effect of high moisture content and good mechanical properties

Active Publication Date: 2014-04-09
SHENZHEN INST OF ADVANCED TECH
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional dry healing theory believes that wound healing requires a dry environment and the action of oxygen. However, in a dry environment, not only is it easy to dehydrate the wound and scab, it is not conducive to the crawling of epithelial cells, but it is also easy to lose biologically active substances. , resulting in slow wound healing, so medical dressings need to have a good moisturizing effect,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical chitosan compound moisturizing dressing and preparation method thereof
  • Medical chitosan compound moisturizing dressing and preparation method thereof
  • Medical chitosan compound moisturizing dressing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A preparation method of medical chitosan composite moisturizing dressing, comprising the steps of:

[0039] (1) Add chitosan to a dilute acetic acid solution with a volume fraction of 2.0%, and stir at room temperature until the chitosan is completely dissolved to form a chitosan solution with a mass fraction of 3% for later use;

[0040] (2) Add glycerin to the chitosan solution prepared in step (1), and stir evenly, wherein the mass ratio of chitosan to glycerin is 1:0.125;

[0041] (3) Add polyvinyl alcohol to the chitosan solution prepared in step (2), and stir in a water bath at 90°C until all polyvinyl alcohol is uniformly dissolved, wherein the mass ratio of chitosan to polyvinyl alcohol is 1:0.33;

[0042] (4) After the chitosan solution prepared in step (3) is allowed to stand and cool to room temperature, borate bioactive glass is added to the chitosan solution and stirred for 10 minutes until uniform, wherein chitosan and borate The mass ratio of bioactive ...

Embodiment 2

[0046] A preparation method of medical chitosan composite moisturizing dressing, comprising the steps of:

[0047] (1) Add chitosan to a dilute acetic acid solution with a volume fraction of 2.0%, and stir at room temperature until the chitosan is completely dissolved to form a chitosan solution with a mass fraction of 3% for later use;

[0048] (2) Add glycerin to the chitosan solution prepared in step (1), and stir evenly, wherein the mass ratio of chitosan to glycerol is 1:0.125;

[0049] (3) Add polyvinyl alcohol to the chitosan solution prepared in step (2), and stir in a water bath at 85°C until all polyvinyl alcohol is uniformly dissolved, wherein the mass ratio of chitosan to polyvinyl alcohol 1:0.25

[0050] (4) After the chitosan solution prepared in step (3) is allowed to stand and cool to room temperature, borate bioactive glass is added to the chitosan solution and stirred for 10 minutes until uniform, wherein chitosan and borate The mass ratio of bioactive glas...

Embodiment 3

[0054] A preparation method of medical chitosan composite moisturizing dressing, comprising the steps of:

[0055] (1) Add chitosan to a dilute acetic acid solution with a volume fraction of 2.0%, and stir at room temperature until the chitosan is completely dissolved to form a chitosan solution with a mass fraction of 3% for later use;

[0056] (2) Add glycerin to the chitosan solution prepared in step (1), and stir evenly, wherein the mass ratio of chitosan to glycerol is 1:0.3;

[0057] (3) Add polyvinyl alcohol to the chitosan solution prepared in step (2), and stir in a water bath at 100°C until all polyvinyl alcohol is uniformly dissolved, wherein the mass ratio of chitosan to polyvinyl alcohol is 1:0.33;

[0058] (4) After the chitosan solution prepared in step (3) is allowed to stand and cool to room temperature, borate bioactive glass is added to the chitosan solution and stirred for 10 minutes until uniform, wherein chitosan and borate The mass ratio of bioactive g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a medical chitosan compound moisturizing dressing which comprises the following components of chitosan, borate bioactive glass, polyvinyl alcohol and glycerinum, wherein the chemical component of the borate bioactive glass is as follows: aNa2O.bK2O.cMgO.dCaO.eB2O3.fP2O5, wherein a, b, c, d, e and f are mol parts, a is 5-9, b is 7-10, c is 7-10, d is 18-25, e is 48-55, f is 1-5, and a+b+c+d+e+f=100; the weight ratio of the chitosan to the borate bioactive glass to the polyvinyl alcohol to the glycerinum is 1:(0.125-0.5):(0.25-0.33):(0.125-0.3). The medical chitosan compound moisturizing dressing is good in moisturizing effect and good in mechanical property, and achieves a more prefect effect in the aspect of promoting a wound, especially a chronic wound, to be rapidly healed.

Description

technical field [0001] The invention relates to the field of biomedical materials, in particular to a medical chitosan composite moisturizing dressing and a preparation method thereof. Background technique [0002] Medical dressings refer to medical materials that cover wounds, temporarily protect wounds, prevent infection, and promote healing. As we all know, chitosan has good biocompatibility, skin affinity and degradability in various biomaterials of new medical dressings, and it also has good effects in antibacterial, hemostasis and promotion of wound healing. Therefore, Chitosan has broad application prospects in the field of medical dressings. [0003] The traditional dry healing theory believes that wound healing requires a dry environment and the action of oxygen. However, in a dry environment, not only is it easy to dehydrate the wound and scab, it is not conducive to the crawling of epithelial cells, but it is also easy to lose biologically active substances. , r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L15/28A61L15/18A61L15/24A61L15/20A61L15/44
Inventor 赵晓丽吴帅黄卓瑶潘浩波
Owner SHENZHEN INST OF ADVANCED TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap