Shoe rubber and production method therefor

A technology for shoe glue and metallocene catalysis, which is applied in the directions of adhesives, benzofuran-indene copolymer adhesives, adhesive types, etc. Good results

Inactive Publication Date: 2014-04-09
浙江固特新材料科技股份有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the existing shoe glues are solvent-based, which is volatile and contains harmful ingredients. During the production process, the harmful ingredients are easy to volatilize into the workshop, which will affect the health of production workers. Volatiliza...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The shoe glue described in this embodiment, it is by 10 parts by weight of naphthenic oil, 5 parts by weight of metallocene catalyzed polyolefin, 10 parts by weight of amorphous poly-α-olefin, 5 parts by weight of hydrogenated ethylene-isoprene-styrene The copolymer consists of 5 parts by weight of phenolic-terpene resin, 10 parts by weight of hydrogenated C5 petroleum resin, 5 parts by weight of polyisobutylene, 0.8 part by weight of antioxidant and 0.5 part by weight of coupling agent.

[0019] Described oxidized polyethylene wax is high-density oxidized polyethylene wax, and its melting drop point is 130-140 degree centigrade;

[0020] Described naphthenic oil hot melt adhesive 36# special oil;

[0021] The melt index of the metallocene-catalyzed polyolefin was 500 g / 10 minutes.

[0022] The softening point of amorphous poly-a-olefin is 100-130°C, and the viscosity is 8000-15000mpa.s.

[0023] Hydrogenated ethylene-isoprene-styrene copolymer is linear with styrene ...

Embodiment 2

[0029] The shoe glue described in the present embodiment is composed of 5 parts by weight of polyethylene wax, 20 parts by weight of naphthenic oil, 15 parts by weight of metallocene catalyzed polyolefin, 25 parts by weight of amorphous poly-alpha-olefin, 15 parts by weight of hydrogenated ethylene- It is composed of isoprene-styrene copolymer, 10 parts by weight of phenolic-terpene resin, 20 parts by weight of hydrogenated C5 petroleum resin, 10 parts by weight of polyisobutylene, 1.5 parts by weight of antioxidant and 1.5 parts by weight of coupling agent.

[0030] The production method of shoe rubber is to heat naphthenic oil to 150°C, add hydrogenated C5 petroleum resin, heat up to 170°C after melting, then add half the amount of antioxidant and then add amorphous poly-α-olefin and Metal-catalyzed polyolefin, after melting, lower the temperature to 150°C, then add hydrogenated ethylene-isoprene-styrene copolymer, add phenolic-terpene resin and the remaining half of the anti...

Embodiment 3

[0032] The shoe glue described in the present embodiment is composed of 3 parts by weight of polyethylene wax, 15 parts by weight of naphthenic oil, 10 parts by weight of metallocene catalyzed polyolefin, 20 parts by weight of amorphous poly-alpha-olefin, 10 parts by weight of hydrogenated ethylene- It consists of isoprene-styrene copolymer, 8 parts by weight of phenolic-terpene resin, 15 parts by weight of hydrogenated C5 petroleum resin, 8 parts by weight of polyisobutylene, 1 part by weight of antioxidant and 1 part by weight of coupling agent.

[0033] The production method of shoe rubber is to heat naphthenic oil to 150°C, add hydrogenated C5 petroleum resin, heat up to 170°C after melting, then add half the amount of antioxidant and then add amorphous poly-α-olefin and Metal-catalyzed polyolefin, after melting, lower the temperature to 150°C, then add hydrogenated ethylene-isoprene-styrene copolymer, add phenolic-terpene resin and the remaining half of the antioxidant aft...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Financial indexaaaaaaaaaa
Softening pointaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the hot melt adhesive field, and especially discloses a soft, air-permeable shoe rubber without pollution and a production method therefor. The shoe rubber is composed of, by weight, 0-5 parts of polyethylene wax, 10-20 parts of naphthenic oil, 5-15 parts of metallocene catalysis polyolefin, 10-25 parts of amorphous-form poly-alpha-olefin, 5-15 parts of hydrogenated ethylene-isoprene-styrene copolymers, 5-10 parts of phenolic aldehyde-terpene resins, 10-20 parts of hydrogenated C5 petroleum resins, 5-10 parts of polyisobutylene, 0.8-1.5 parts of antioxidants and 0.5-1.5 parts of coupling agents. The produced shoe rubber is soft and good air permeability. In seal air permeability tests, sealing is carried out with the shoe rubber under 1.5 barometric pressure, inside and outside air pressure balance is achieved after 1h, the breaking elongation rate of the shoe rubber is more than 300%, the tensile strength is more than or equal to 3 MPa, the viscosity is 3000+/-1000MPa.S (180 DEG C, a rotary viscosimeter), the C peel strength is more than 40N/2.5cm ( peeling at the temperature of 180 DEG C), and the softening point is more than 135+/-5 DEG C.

Description

technical field [0001] The invention relates to the field of hot melt adhesives, in particular to shoe adhesives and a manufacturing method thereof. Background technique [0002] Most of the existing shoe glues are solvent-based, which is volatile and contains harmful ingredients. During the production process, the harmful ingredients are easy to volatilize into the workshop, which will affect the health of production workers. Volatilization will affect the health of users; some shoe glue uses hot melt glue, which is relatively hard, which makes the soles poor in air permeability, especially when it encounters water during use, it will cause degumming and shorten the service life of the shoes. short. Contents of the invention [0003] The object of the present invention is to provide a kind of soft, breathable, non-polluting shoe glue and its production method in order to solve the deficiency of above-mentioned technology. [0004] In order to achieve the above object, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J123/00C09J157/02C09J153/02C09J161/06C09J145/02C09J123/06C09J123/20C09J11/06
CPCY02A50/20
Inventor 陈惠娟李光鹏邵宝有邵晓巍
Owner 浙江固特新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap