Environment-friendly, pollution-free, high-efficiency mouse glue and production method thereof

A kind of high-efficiency technology for sticky mouse glue, which is applied in the directions of polymer adhesive additives, non-polymer adhesive additives, adhesives, etc. Stable performance, anti-aging and decomposition, low-cost effects

Active Publication Date: 2017-07-11
浙江固特新材料科技股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing sticky mouse glue is poor in viscosity and poor in use effect, and when used in the open air, the service life is shorter, and in low temperature conditions, the antifreeze performance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly, pollution-free, high-efficiency mouse glue and production method thereof
  • Environment-friendly, pollution-free, high-efficiency mouse glue and production method thereof
  • Environment-friendly, pollution-free, high-efficiency mouse glue and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1. Raw materials:

[0027]

[0028]

[0029] 2. The production method of environmental protection, pollution-free and high-efficiency sticky mouse glue, the specific steps are:

[0030] The first step: heating part of naphthenic oil, white oil or their mixture to 165°C, adding amorphous poly-alpha-olefin, styrene-butadiene-styrene block copolymer or their mixture, the The weight ratio of naphthenic oil, white oil or their mixture to amorphous poly-α-olefin, styrene-butadiene-styrene block copolymer or its mixture is 1:0.8, and oxidized polyethylene is added in proportion For wax and antioxidant, after it melts, add the remaining naphthenic oil, white oil or their mixture, and control the adding speed during this process to ensure that the system temperature is ≥150°C;

[0031] Step 2: Add butyl rubber in proportion. During this process, control the adding speed to ensure that the system temperature is ≥140°C. After it melts, add C5 hydrogenated petroleum resin an...

Embodiment 2

[0034] 1. Raw materials:

[0035]

[0036]

[0037] 2. The production method of environmental protection, pollution-free and high-efficiency sticky mouse glue, the specific steps are:

[0038] The first step: heating part of naphthenic oil, white oil or their mixture to 160°C, adding amorphous poly-α-olefin, styrene-butadiene-styrene block copolymer or their mixture, the The weight ratio of naphthenic oil, white oil or their mixture to amorphous poly-α-olefin, styrene-butadiene-styrene block copolymer or its mixture is 1:0.4, and oxidized polyethylene is added in proportion For wax and antioxidant, after it melts, add the remaining naphthenic oil, white oil or their mixture, and control the adding speed during this process to ensure that the system temperature is ≥150°C;

[0039] Step 2: Add butyl rubber in proportion. During this process, control the adding speed to ensure that the system temperature is ≥140°C. After it melts, add C5 hydrogenated petroleum resin and co...

Embodiment 3

[0042] 1. Raw materials:

[0043]

[0044]

[0045] 2. The production method of environmental protection, pollution-free and high-efficiency sticky mouse glue, the specific steps are:

[0046] The first step: heating part of naphthenic oil, white oil or their mixture to 170°C, adding amorphous poly-α-olefin, styrene-butadiene-styrene block copolymer or their mixture, the The weight ratio of naphthenic oil, white oil or their mixture to amorphous poly-α-olefin, styrene-butadiene-styrene block copolymer or its mixture is 1:1.2, and oxidized polyethylene is added in proportion For wax and antioxidant, after it melts, add the remaining naphthenic oil, white oil or their mixture, and control the adding speed during this process to ensure that the system temperature is ≥150°C;

[0047] Step 2: Add butyl rubber in proportion. During this process, control the adding speed to ensure that the system temperature is ≥140°C. After it melts, add C5 hydrogenated petroleum resin and co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the hot melt adhesive field, and especially discloses an environmentally friendly, nuisanceless and efficient rat adhesive with long viscidity holding time and a production method therefor. The rat adhesive is composed of 0.5-4 parts of oxidized polyethlene wax, 10-30 parts of butyl rubbers, 10-40 parts of one of naphthenic oil and white oil or a mixture thereof, 20-45 parts of C5 hydrogenated petroleum resins, 0.5-1 part of antioxidants, 0.5-1 part of attractants, and 4-15 parts of one of amorphous form poly-alpha-alkene, styrene-butadiene-styrene segmented copolymer hydride (SEPS) or a mixture thereof. The rat adhesive has advantages of good weather resistance, long viscidity holding time, good sagging resistance and the like.

Description

technical field [0001] The invention relates to the field of hot melt adhesives, in particular to an environment-friendly, pollution-free, high-efficiency mouse glue and a production method thereof. Background technique [0002] The existing sticky mouse glue has poor viscosity and poor use effect, and when used in the open air, the service life is shorter, and the antifreeze performance is poor under low temperature conditions. Contents of the invention [0003] The purpose of the present invention is to provide a kind of environment-friendly, pollution-free and high-efficiency sticky mouse glue and its production method in order to solve the deficiencies of the above-mentioned technologies. [0004] In order to achieve the above object, the environmental protection, pollution-free and high-efficiency sticky mouse glue designed by the present invention consists of 0.5-4 parts of oxidized polyethylene wax, 10-30 parts of butyl rubber, 10-40 parts of naphthenic oil and whit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J157/02C09J123/22C09J153/02C09J123/02C09J11/08C09J11/06A01M23/00
Inventor 李光鹏陈惠娟邵宝有
Owner 浙江固特新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com