Electric vehicle battery lead paste and method of use thereof

An electric vehicle battery, lead paste technology, applied in battery electrodes, circuits, electrical components, etc., can solve the problems of long plate curing time, high impurity content, short negative plate life, etc. Easy to mix evenly, reducing the effect of dust flying

Active Publication Date: 2015-11-18
HENAN CHAOWEI POWER SUPPLY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0031] In view of the above problems, the purpose of the present invention is to provide an electric vehicle battery lead paste and its use method, which solves the problems of expensive additives, environmental pollution, many types of additives, high impurity content, high self-discharge of the battery, and long curing time of the plates. , can’t discharge electricity, and the life of the negative plate is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric vehicle battery lead paste and method of use thereof
  • Electric vehicle battery lead paste and method of use thereof
  • Electric vehicle battery lead paste and method of use thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072] It is composed of lead paste on the positive electrode and lead paste on the negative electrode. The lead paste on the positive electrode is made of: 1000kg of lead powder, 1.5kg of fiber, 5kg of sodium borate, 135kg of water and 70kg of sulfuric acid. The apparent density is 4.2g / cm 3 The lead paste on the negative electrode is made of: 990kg lead powder, 0.9kg fiber, 2.5kg sodium borate, 3kg polyaspartic acid sodium salt, 2kg barium stearate, 115kg water and 70kg sulfuric acid. The apparent density is 4.1 g / cm 3 of lead paste.

Embodiment 2

[0074] It is composed of lead paste on the positive electrode and lead paste on the negative electrode. The lead paste on the positive electrode is made of: 990kg of lead powder, 1.2kg of fiber, 4kg of sodium borate, 125kg of water and 65kg of sulfuric acid. The apparent density is 4.0g / cm 3 The lead paste on the negative electrode is made of: lead powder 1000kg, fiber 1.2kg, sodium borate 3kg, polyaspartic acid sodium salt 4kg, barium stearate 3kg, water 125kg and sulfuric acid 75kg. The apparent density is 4.3g / cm 3 of lead paste.

Embodiment 3

[0076] It is composed of lead paste on the positive electrode and lead paste on the negative electrode. The lead paste on the positive electrode is made of: lead powder 1010kg, fiber 1.8kg, sodium borate 6kg, water 145kg and sulfuric acid 75kg. The apparent density is 4.4g / cm 3 The lead paste on the negative electrode is made of: lead powder 1000kg, fiber 1.2kg, sodium borate 3kg, polyaspartic acid sodium salt 4kg, barium stearate 3kg, water 125kg and sulfuric acid 75kg. The apparent density is 4.3g / cm 3 of lead paste.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to lead paste, and particularly relates to lead paste for a battery of an electric vehicle, and a use method thereof. The lead paste is composed of the lead paste on a positive electrode and the lead paste on a negative electrode, wherein the lead paste on the positive electrode is composed of lead powder, fibers, sodium borate, water and sulfuric acid. The lead paste on the negative electrode is prepared by the lead powder, the fibers, sodium borate, sodium polyaspartate, barium stearate, water and sulfuric acid. An object of the invention is to provide the lead paste for the battery of the electric vehicle, and the use method thereof and solve the problems of high price of additives, environment pollutions, many species of the additives, high impurity content, high self discharge of the battery, long curing time of electrode plates, disability for discharging and short service life of a negative plate.

Description

technical field [0001] The invention relates to lead paste, in particular to electric vehicle battery lead paste and its application method. Background technique [0002] In the second edition of "Introduction to Lead-acid Batteries", there are records about the formula and paste procedure of the lead paste. The current conventional electric vehicle battery lead paste is: [0003] 1. Conventional process operation: [0004] The first step: lead powder is added to the paste machine; [0005] Step 2: Add the dry material formula to the paste mixing machine, including red lead, fiber, graphite, antimony trioxide, acetylene black, stannous sulfate, barium sulfate, humic acid, lignin, etc., and stir with the lead paste for about 8 minutes ; [0006] Step 3: Quickly add water in about 2 minutes, then wet stir for 8 minutes, and stir at the same time during the addition process; [0007] Step 4: Slowly add acid for about 20 minutes, and the density of sulfuric acid is 1.40g / cm ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/57
CPCH01M4/57H01M4/62H01M4/628Y02E60/10
Inventor 李松林柴成雷
Owner HENAN CHAOWEI POWER SUPPLY