Wear-resistant and corrosion-resistant enamel glaze with good adhesion

A technology of enamel glaze and adhesion, which is applied in the field of enamel glaze, can solve the problems of enamel glaze wear resistance, corrosion resistance and adhesion performance, etc., and achieve the effect of good wear resistance and corrosion resistance adhesion

Active Publication Date: 2016-04-13
得宝搪瓷(中山)有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The wear resistance, corrosion resistance and adhesion performance of commonly used enamel glazes are not very ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An enamel glaze with good wear resistance and corrosion resistance adhesion is composed of the following components:

[0023] 8 parts by mass mica,

[0024] 1 part by mass of sodium pyrophosphate,

[0025] 6 parts by mass of lithium oxide,

[0026] 7 parts by mass of boron oxide,

[0027] 4 parts by mass of cobalt oxide,

[0028] 3 parts by mass of barium oxide,

[0029] 6 parts by mass of aluminum oxide,

[0030] 6 parts by mass of feldspar,

[0031] 4 parts by mass of calcium oxide,

[0032] 8 parts by mass of sodium oxide,

[0033] 8 parts by mass of polyethylene wax powder,

[0034] 7 parts by mass of calcium fluoride,

[0035] 10 parts by mass of quartz.

Embodiment 2

[0037] An enamel glaze with good wear resistance and corrosion resistance adhesion is composed of the following components:

[0038] 9 parts by mass mica,

[0039] 1 part by mass of sodium pyrophosphate,

[0040] 6 parts by mass of lithium oxide,

[0041] 7 parts by mass of boron oxide,

[0042] 4 parts by mass of cobalt oxide,

[0043] 3 parts by mass of barium oxide,

[0044] 6 parts by mass of aluminum oxide,

[0045] 8 parts by mass of feldspar,

[0046] 4 parts by mass of calcium oxide,

[0047] 8 parts by mass of sodium oxide,

[0048] 8 parts by mass of polyethylene wax powder,

[0049] 7 parts by mass of calcium fluoride,

[0050] 15 parts by mass of quartz.

Embodiment 3

[0052] An enamel glaze with good wear resistance and corrosion resistance adhesion is composed of the following components:

[0053] 8.9 parts by mass of mica,

[0054] 1 part by mass of sodium pyrophosphate,

[0055] 6 parts by mass of lithium oxide,

[0056] 7 parts by mass of boron oxide,

[0057] 4 parts by mass of cobalt oxide,

[0058] 3 parts by mass of barium oxide,

[0059] 6 parts by mass of aluminum oxide,

[0060] 6.8 parts by mass of feldspar,

[0061] 4 parts by mass of calcium oxide,

[0062] 8 parts by mass of sodium oxide,

[0063] 8 parts by mass of polyethylene wax powder,

[0064] 7 parts by mass of calcium fluoride,

[0065] 13 parts by mass of quartz.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses wear-resistant corrosion-resistant enamel glaze with a good adhesive force. The wear-resistant corrosion-resistant enamel glaze comprises the following components by mass: 8-9 parts of micaceous, 1 part of sodium pyrophosphate, 6 parts of lithium oxide, 7 parts of boric anhydride, 4 parts of cobaltous oxide, 3 parts of barium oxide, 6 parts of aluminium oxide, 6-8 parts of feldspar, 4 parts of calcium oxide, 8 parts of sodium oxide, 8 parts of polyethylene wax powder, 7 parts of calcium fluoride, and 10-15 parts of quartz. The enamel glaze provided by the invention cannot fall off easily, and is wear-resistant and corrosion-resistant.

Description

technical field [0001] The invention relates to an enamel glaze with good wear-resistant and corrosion-resistant adhesion. Background technique [0002] The wear resistance, corrosion resistance and adhesion performance of commonly used enamel glazes are not very satisfactory. Contents of the invention [0003] The object of the present invention is to provide an enamel glaze material with good wear-resistant and corrosion-resistant adhesion, which is not easy to fall off, wear-resistant and corrosion-resistant. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of enamel glaze with good wear-resistant and corrosion-resistant adhesion, which consists of the following components: [0005] 8~9 parts by mass of mica, [0006] 1 part by mass of sodium pyrophosphate, [0007] 6 parts by mass of lithium oxide, [0008] 7 parts by mass of boron oxide, [0009] 4 parts by mass of cobalt oxide, [0010] 3 parts b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/14
Inventor 单佳单永其张文斌
Owner 得宝搪瓷(中山)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com