Modified asphalt waterproof sheet material

A technology of modified asphalt and waterproof membrane, which is applied in the direction of asphalt material adhesives, asphalt layered products, adhesive types, etc., and can solve problems such as high temperature resistance, aging resistance, and construction convenience defects

Active Publication Date: 2014-05-21
KUNMING FENGXING WATERPROOF MATERIAL +1
View PDF6 Cites 57 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, single-layer roof waterproofing generally includes thermoplastic PVC, TPO membranes, thermosetting EPDM membranes and some high-performance modified bitumen membranes, but there is no successful case of using elastomer (SBS) modified bitumen waterproof membranes. The reason is that the elastomer (SBS) modified asphalt waterproofing membrane has some defects in high temperature resistance, aging resistance and construction convenience.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified asphalt waterproof sheet material
  • Modified asphalt waterproof sheet material
  • Modified asphalt waterproof sheet material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The thickness of the glass fiber tire used is: 0.45mm, and the weight is 60g / m 2 , the thickness of the polyester tire is 1.0mm, and the weight is 220g / m 2 , the total thickness of the coil is 5mm, of which the thickness of the mineral particles on the upper surface is 1.2mm, the thickness between the two tire bases is 1mm, the thickness of the self-adhesive polymer modified asphalt rubber on the lower surface is 1.35mm, the width of the overlapping edge is 100mm, and the length of the coil is 1000mm .

[0047] Among them, the formula of high temperature resistant elastomer (SBS) modified asphalt compound is as follows:

[0048]

[0049]

[0050] Among them, the formula of self-adhesive polymer modified asphalt compound is as follows:

[0051]

Embodiment 2

[0053] The thickness of the glass fiber tire used is: 0.4mm, and the weight is 60g / m 2 , the thickness of the polyester tire is 1.0mm, and the weight is 220g / m 2 , the total thickness of the coil is 4mm, of which the thickness of the mineral pellets on the upper surface is 1mm, the thickness between the two tire bases is 1mm, the thickness of the self-adhesive polymer modified asphalt compound on the lower surface is 1.6mm, the width of the lap joint is 100mm, and the length of the coil is 1000mm.

[0054] Among them, the formula of high temperature resistant elastomer (SBS) modified asphalt compound is as follows:

[0055]

[0056]

[0057] Among them, the formula of self-adhesive polymer modified asphalt compound is as follows:

[0058]

Embodiment 3

[0060] The thickness of the glass fiber tire used is: 0.5mm, and the weight is 100g / m 2 , the thickness of the polyester tire is 1.0mm, and the weight is 150g / m 2 , the total thickness of the coil is 6mm, of which the thickness of the mineral pellets on the upper surface is 1mm, the thickness between the two tire bases is 1.5mm, the thickness of the self-adhesive polymer modified asphalt rubber on the lower surface is 2mm, the width of the overlapping edge is 100mm, and the length of the coil is 1000mm.

[0061] Among them, the formula of high temperature resistant elastomer (SBS) modified asphalt compound is as follows:

[0062]

[0063] Among them, the formula of self-adhesive polymer modified asphalt compound is as follows:

[0064]

[0065] The applicant has tested the physical and chemical properties of the above-mentioned waterproof membrane. The test results show that the above-mentioned waterproof membrane has no cracks or cracks at -30°C. The upper surface can ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Pullaaaaaaaaaa
Peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified asphalt waterproof sheet material. The modified asphalt waterproof sheet material is of a multilayer structure; the upper surface of the modified asphalt waterproof sheet material is a mineral granule layer; a fiberglass reinforcement basic layer and a polyester reinforcement basic layer are sequentially arranged in the middle part of the modified asphalt waterproof sheet material in sequence; a self-adhesion polymer modification asphalt sizing material layer is arranged in the bottom layer of the modified asphalt waterproof sheet material; adjacent layers are adhered through an elastomer polymer modification asphalt sizing material layer; an isolation film is adhered on the self-adhesion polymer modification asphalt sizing material layer. The structure of the modified asphalt waterproof sheet material provided by the invention can be applicable to small deformation of the basic layers, and has the advantages of higher size stability, convenience in construction, adhesion reliability and self-heating property. The invention provides a reliable and exposed modified asphalt waterproof sheet material, and is particularly applicable to monolayer roofs.

Description

technical field [0001] The invention relates to a modified asphalt waterproof coiled material, belonging to the field of waterproof materials. Background technique [0002] Because the single-layer flexible roof system has the characteristics of light weight, good waterproof and thermal insulation performance, quick construction, easy maintenance, long life, and excellent long-term cost performance, it can completely solve the problems of water leakage, cold bridge condensation, noise, etc. of traditional roof systems. Due to the problem of multi-curved surface construction, the single-layer flexible roof system has become the most important roof system form of flat roof engineering in European and American countries. [0003] The single-layer roof system was officially introduced into China in 1999 and used in various projects. In view of its many significant advantages, the single-layer roof system has been quickly recognized and accepted by the domestic market and has be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B11/10B32B17/02B32B27/40C09J195/00C09J153/02C09J11/08C09J11/06C09J11/04
Inventor 李文志刘金景徐茂震宗建华段文锋
Owner KUNMING FENGXING WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com