Production process for hot-dip aluminium-zinc alloy plate

A production process, zinc alloy technology, applied in hot-dip plating process, metal material coating process, heat treatment furnace, etc., can solve the problems of poor product strength and high production cost, and achieve the effect of reducing production cost and excellent tensile strength

Inactive Publication Date: 2014-05-28
SHANDONG ZHONGTAI PLATE CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides a production process of a hot-dip aluminum-zinc alloy plate to solve the problems of high production cost and poor product strength in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] A production process for hot-dip aluminum-zinc alloy plate, the hot-dip aluminum-zinc alloy plate is composed of a steel plate base material and an aluminum-zinc alloy coating, including substrate cleaning treatment, annealing treatment, preparation of aluminum-zinc alloy plating solution, hot-dip plating and post-treatment, The base material of the steel plate is SPCC cold-rolled substrate, that is, cold-rolled carbon steel substrate. The composition of aluminum-zinc alloy coating is: AL10%-15%, Si0.3%-0.5%, Re0.2%, Mg0.5%, Zn83%, 500KW induction body is used to heat and stir the aluminum-zinc alloy in the preparation of the aluminum-zinc alloy plating solution, and the temperature of the aluminum-zinc alloy solution is kept at 460-600℃; the cold rolling carbon steel substrate is heated to 700℃ in the annealing furnace The annealing and recrystallization are carried out above. The annealing and reduction time of the cold-rolled carbon steel substrate in the annealing fu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production process for a hot-dip aluminium-zinc alloy plate, and belongs to the field of metal material preparation. The hot-dip aluminium-zinc alloy plate consists of a steel plate base material and an aluminium-zinc alloy clad layer, wherein the steel plate base material is a cold continuous rolling carbon steel baseplate, and the aluminium-zinc alloy plating comprises the following components in percentage by weight: 10% to 15% of AL, 0.3% to 0.5% of Si, 0.2% of Re, 0.5% of Mg and 83% of Zn. In the preparation of an aluminium-zinc alloy clad plating solution, a 500 KW inductor is adopted to heat and stir the aluminium-zinc alloy, and the temperature of the aluminium-zinc alloy solution is kept to be 460 to 600 DEG C; the cold continuous rolling carbon steel baseplate is heated to be above 700 DEG C in an annealing furnace to be performed annealing and recrystallization, and then conducted surface reduction activation under a high hydrogen atmosphere. The process adopts the aluminium-zinc alloy with low aluminium content as the plating, and then is combined with a specific production process and a heat treatment process, the surface of the cold rolled steel cold-roll steel sheet is combined and fully reacted with the aluminium-zinc alloy, the produced aluminium-zinc alloy plate has excellent tensile strength, elongation and hardness, meanwhile the production cost is reduced, and the production process can be widely applied to the field of rolled steel plates.

Description

technical field [0001] The invention belongs to the field of metal material preparation, in particular to a production process of a hot-dip aluminum-zinc alloy plate. Background technique [0002] At present, in the field of metal manufacturing technology, in order to improve the corrosion resistance, wear resistance and heat resistance of the cold-rolled steel sheet surface, the surface of the cold-rolled steel sheet is usually hot-dip galvanized with an Al-Zn alloy layer. As a wear-reducing material, Al-Zn alloy gradually replaces the expensive Sn and Pb alloy, and then gradually replaced tin bronze with the lack of copper resources, aluminum-zinc alloy has good mechanical properties, excellent casting process performance, low raw material cost and low melting energy consumption, no pollution to the environment. Advantages, more and more favored by the industry. However, the current production process of hot-dip Al-Zn alloy sheet has the following problems: the aluminum c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C2/06C23C2/40C21D9/56C22C18/04
Inventor 张波孙树亮武鹏乾
Owner SHANDONG ZHONGTAI PLATE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products