High temperature-resistant corrosion-resistant cement gum and construction method thereof

A technology of anti-corrosion cement and high temperature resistance, which is applied in the field of anti-corrosion. It can solve the problems of vitrified bricks not sticking, falling safety, long construction time, leakage, etc., and achieves high tensile strength, simple construction and long material life. Effect

Active Publication Date: 2014-06-04
TONGZHENG ENVIRONMENT PROTECTION GRP CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] According to previous engineering cases, the anti-corrosion process of the chimney flue after wet desulfurization is often constructed in the form of a combination of acid-resistant cement and vitrified bricks, but this construction process takes a long time and often leaks or due to time For a long time, vitrified tiles cannot stick and fall off, causing safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High temperature-resistant corrosion-resistant cement gum and construction method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Including component A and component B, the ratio of component A to group B is 18:0.8

[0031] Among them, component A is a high-temperature-resistant and corrosion-resistant polymer, including the following components, based on the total amount of component A as a mass percentage:

[0032] Silica gel 38.0wt%, silicone oil 8.8wt%, fumed silica 2.1wt%, active zinc oxide 1.8wt%, active silicon micropowder 11.8wt%, precipitated silica 3.5wt%, active aluminum hydroxide micropowder 12.0wt%, cast Stone powder 3.3wt%, diatomaceous earth is the balance;

[0033] Among them, component B is a coagulant, including the following components, based on the total amount of component B as 100 parts by mass: silicone oil 30 wt%; orthopropyl silicate 70 wt%.

Embodiment 2

[0035] Including component A and component B, the ratio of component A to group B is 20:1

[0036] Among them, component A is a high-temperature-resistant and corrosion-resistant polymer, including the following components, based on the total amount of component A as a mass percentage:

[0037] Silica gel 40wt%, silicone oil 9wt%, fumed silica 2.8wt%, active zinc oxide 2.2wt%, active silicon micropowder 12wt%, precipitated silica 4wt%, active aluminum hydroxide micropowder 12.7wt%, cast stone powder 4wt% , diatomaceous earth is the balance;

[0038] Among them, component B is a coagulant, including the following components, based on the total amount of component B as 100 parts by mass: silicone oil 32 wt%; orthopropyl silicate 68 wt%.

Embodiment 3

[0040] Including component A and component B, the ratio of component A to group B is 23:1.2

[0041] Among them, component A is a high-temperature-resistant and corrosion-resistant polymer, including the following components, based on the total amount of component A as a mass percentage:

[0042] Silica gel 47.2wt%, silicone oil 10.3wt%, fumed silica 3.9wt%, active zinc oxide 2.7wt%, active silicon micropowder 14.5wt%, precipitated silica 5.2wt%, active aluminum hydroxide micropowder 13.5wt%, cast Stone powder 5.3wt%, diatomaceous earth is the balance;

[0043] Among them, component B is a coagulant, including the following components, based on the total amount of component B as 100 parts by mass: silicone oil 35 wt%; orthopropyl silicate 65 wt%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high temperature-resistant corrosion-resistant cement gum and a construction method thereof. The high temperature-resistant corrosion-resistant cement gum comprises a component A and a component B. A ratio of the component A to the component B is 18-23: 0.8-1.2. The component A is a high temperature-resistant corrosion-resistant polymer and comprises 38.0-47.2wt% of silica gel, 8.8-10.3wt% of silicone oil, 2.1-3.9wt% of fumed silica, 1.8-2.7wt% of activated zinc oxide, 11.8-14.5wt% of active silica micropowder, 3.5-5.2wt% of precipitated silica, 12.0-13.5wt% of active aluminum hydroxide micropowder, 3.3-5.3wt% of glass-ceramic powder and 5-7.5wt% of diatomite. The component B is a coagulator and comprises 30-35wt% of silicone oil and 65-70wt% of tetrapropoxysilane. The high temperature-resistant corrosion-resistant cement gum has high temperature resistance, can prevent corrosion produced by various acid and alkali mediums and has good tensile strength and excellent penetration resistance.

Description

technical field [0001] The invention relates to the field of anti-corrosion technology, in particular to a high-temperature-resistant anti-corrosion mortar and a preparation method thereof. Background technique [0002] In my country, coal-fired boiler flue gas is one of the most important sources of air pollution and has become the primary goal of environmental governance. In 2005, my country's sulfur dioxide emissions reached 25.5 million tons, and the total emissions have surpassed that of Europe and the United States, ranking first in the world. Excessive flue gas emissions make the originally valuable sulfur resource a huge pollution source that endangers the environment. Therefore, it is imperative to remove sulfur dioxide in the tail gas in the flue gas, and the combination of various desulfurization processes (dry desulfurization process, semi-dry desulfurization process, wet desulfurization process, etc.) has the highest efficiency for boiler tail gas desulfurizati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 黄日昌林思源林万淦金荣森
Owner TONGZHENG ENVIRONMENT PROTECTION GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com