Low temperature vulcanized butyl rubber sheet
A technology of butyl rubber and rubber sheet, which is applied in the field of butyl rubber sheet, can solve the problems that are not suitable for large-scale container construction on site, and achieve the effects of superior adhesion performance, high corrosion resistance, and stable and reliable quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0019] The low-temperature vulcanized butyl rubber sheet consists of the following components in parts by weight:
[0020] Butyl rubber SB4266100 parts, semi-reinforcing carbon black 45 parts, thermal black N99035 parts, lubricant 5 parts, paraffin oil 10 parts, resin 3 parts, sulfur 1.5 parts, accelerator M1 part, accelerator TMTD0.5 Parts, Accelerator TTTE1.2 parts.
[0021] Among the above components, butyl rubber SB4266 is imported from ExxonMobil Corporation of the United States.
[0022] The vulcanization method of the rubber sheet is as follows: the made rubber sheet is pasted in the container, and then saturated steam is introduced under normal pressure to raise the temperature of the rubber sheet to 55°C and keep it warm for 24 hours, then heat it to 95°C and keep it warm After 50 hours, the vulcanization reaction was carried out.
[0023] The performance detection data of the butyl rubber plate of table 1 embodiment 1:
[0024]
Embodiment 2
[0026] The low-temperature vulcanized butyl rubber sheet consists of the following components in parts by weight:
[0027] Butyl rubber SB4266100 parts, semi-reinforcing carbon black 30 parts, thermal black N99050 parts, lubricant 3 parts, paraffin oil 5 parts, resin 2 parts, sulfur 1 part, accelerator M1 part, accelerator TMTD0.8 parts, accelerator TTTE1 part.
[0028] The vulcanization method of the rubber sheet is as follows: the made rubber sheet is pasted in the container, and then saturated steam is introduced under normal pressure to raise the temperature of the rubber sheet to 50°C and keep it warm for 20 hours, and then heat it up to 90°C Keep warm for 45 hours to carry out vulcanization reaction.
[0029] The performance test of the prepared low-temperature vulcanized butyl rubber sheet material is similar to that in Table 1 in Example 1.
Embodiment 3
[0031] The low-temperature vulcanized butyl rubber sheet consists of the following components in parts by weight:
[0032] Butyl rubber SB4266100 parts, semi-reinforcing carbon black 60 parts, thermal black N99020 parts, lubricant 10 parts, paraffin oil 15 parts, resin 5 parts, sulfur 4 parts, accelerator M3 parts, accelerator TMTD0.5 Parts, Accelerator TTTE2 parts.
[0033] The vulcanization method of the rubber sheet is as follows: the made rubber sheet is pasted in the container, and then saturated steam is introduced under normal pressure to raise the temperature of the rubber sheet to 60°C and keep it warm for 24 hours, and then heat it to raise the temperature to 95°C Keep warm for 50 hours to carry out vulcanization reaction.
[0034] The performance test of the prepared low-temperature vulcanized butyl rubber sheet material is similar to that in Table 1 in Example 1.