Manufacturing method of electrothermal film

A production method and technology of electrothermal film, applied in the direction of heating element materials, etc., can solve the problems of peeling off of electrothermal film paint, low infrared emissivity, insufficient stability, etc., and achieve smooth surface, high light transmittance, good electrical conductivity and thermal conductivity. The effect of stability

Active Publication Date: 2014-10-01
成都世纪经尧科技有限公司
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to overcome the lack of stability in the prior art, poor temperature resistance, low infrared emissivity, poor adhesion, and the electrothermal film coating is easy to fall off from the substrate, and to provide a method for making an electrothermal film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A method for manufacturing an electric heating film, comprising the following steps:

[0036] A. Equipped with electrothermal film treatment liquid, electrothermal film treatment liquid is composed of tin tetrachloride, titanium trichloride, antimony trichloride, calcium dichloride, chromium trioxide, manganese dioxide, nickel trioxide, isopropanol, ethanol and water; wherein the mass percentage of tin tetrachloride is 40%, the mass percentage of titanium trichloride is 1%, the mass percentage of antimony trichloride is 15%, the mass percentage of calcium dichloride is 2%, three The mass percentage of chromium oxide is 1%, the mass percentage of manganese dioxide is 1%, the mass percentage of nickel trioxide is 1%, the mass percentage of isopropanol is 10%, the mass percentage of ethanol is 4%, water The mass percentage is 25%, after heating and mixing uniformly, cool to normal temperature for use;

[0037] B. The substrate mask; the substrate mask is a prior art, an...

Embodiment 2

[0042] A method for manufacturing an electric heating film, comprising the following steps:

[0043] A. Equipped with electrothermal film treatment liquid, electrothermal film treatment liquid is composed of tin tetrachloride, titanium trichloride, antimony trichloride, calcium dichloride, chromium trioxide, manganese dioxide, nickel trioxide, isopropanol, ethanol and water; wherein the mass percentage of tin tetrachloride is 40%, the mass percentage of titanium trichloride is 1%, the mass percentage of antimony trichloride is 15%, the mass percentage of calcium dichloride is 2%, three The mass percentage of chromium oxide is 1%, the mass percentage of manganese dioxide is 1%, the mass percentage of nickel trioxide is 1%, the mass percentage of isopropanol is 10%, the mass percentage of ethanol is 4%, water The mass percentage is 25%, after heating and mixing uniformly, cool to normal temperature for use;

[0044] B. The substrate mask; the substrate mask is a prior art, an...

Embodiment 3

[0049] A method for manufacturing an electric heating film, comprising the following steps:

[0050] A. Equipped with electrothermal film treatment liquid, electrothermal film treatment liquid is composed of tin tetrachloride, titanium trichloride, antimony trichloride, calcium dichloride, chromium trioxide, manganese dioxide, nickel trioxide, isopropanol, ethanol and water; wherein the mass percentage of tin tetrachloride is 40%, the mass percentage of titanium trichloride is 1%, the mass percentage of antimony trichloride is 15%, the mass percentage of calcium dichloride is 2%, three The mass percentage of chromium oxide is 1%, the mass percentage of manganese dioxide is 1%, the mass percentage of nickel trioxide is 1%, the mass percentage of isopropanol is 10%, the mass percentage of ethanol is 4%, water The mass percentage is 25%, after heating and mixing uniformly, cool to normal temperature for use;

[0051] B. The substrate mask; the substrate mask is a prior art, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing method of an electrothermal film. The manufacturing method comprises the following steps of A, preparing an electrothermal film treatment solution which comprises tin tetrachloride, titanium trichloride, antimony trichloride, calcium chloride, chromic oxide, manganese dioxide, nickel sesquioxide, isopropanol, alcohol and water, B, masking a substrate, C, heating the substrate to be 400-700 DEG C and then spraying the electrothermal film treatment solution on the substrate by a spray gun to form a semifinished electrothermal film, D, annealing the semifinished electrothermal film, and E, coating silver oxide paste on the surfaces of the two ends of the annealed semifinished electrothermal film, loading the semifinished electrothermal film into an electrode oven, baking and fusing the semifinished electrothermal film to form a whole, and obtaining the finished electrothermal film. The manufacturing method has the advantages that the stability of the electrothermal film is improved by adding antimony; the temperature resistance of the electrothermal film is improved by adding titanium; the infrared emitting ability of the electrothermal film is improved by adding nickel and manganese; and an adhesive force between the electrothermal film treatment solution and the substrate is increased by adding isopropanol.

Description

technical field [0001] The invention relates to the field of heating materials, in particular to a method for manufacturing an electrothermal film. Background technique [0002] Electrothermal film is widely used in various occasions and is a thin film heating material. The so-called thin film heating material is to form a layer of conductive film on the surface of the insulating material after a certain process is processed on the surface of the insulating material. Conductive particles form a network lattice structure on the surface of the insulating layer, and various additives added to the film can adjust the power of the electrothermal film. After electrification, this layer of film can be converted, so people also call it electrothermal film. [0003] However, the existing electrothermal film has the following problems: [0004] 1. Insufficient stability; [0005] 2. Poor temperature resistance; [0006] 3. Low infrared emissivity; [0007] 4. The adhesion is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H05B3/12C03C17/00
Inventor 颜彬罗膺
Owner 成都世纪经尧科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com