A kind of high temperature resistant wall paint and preparation method thereof

A technology of high temperature resistance and coating, applied in the direction of coating, etc., can solve the problems of short high temperature resistance time, high temperature resistance and poor heat insulation performance, and achieve the effect of long high temperature resistance time and excellent impact resistance

Inactive Publication Date: 2016-05-11
泗阳县弘达新型墙体材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004]Technical solution to solve: In view of the shortcomings of existing wall coatings such as poor high temperature resistance, poor heat insulation performance, and short high temperature resistance time, the present invention provides a high temperature resistant wall surface Coating and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] This embodiment provides a kind of high-temperature-resistant wall paint, including the following raw materials in terms of parts by mass: 12 parts of silicone resin, 12 parts of fluororubber, 4 parts of zinc carbonate, 20 parts of aluminum oxide, and 5 parts of sepiolite , 15 parts of quartz powder, 7 parts of aluminum silver paste, 0.3 parts of sodium hydroxide, 3 parts of titanate, 23 parts of boric acid, 2 parts of benzoin ether, 70 parts of water.

[0016] A preparation method of high temperature resistant wall paint, comprising the following steps:

[0017] Step 1: Add silicone resin, fluororubber, zinc carbonate, aluminum oxide, sepiolite, quartz powder and aluminum silver paste into the mixer, stir and mix evenly to obtain mixture A;

[0018] Step 2: Put mixture A into a grinder and grind for 30 minutes until the fineness is 50 μm to obtain mixture B;

[0019] Step 3: Add titanate, boric acid, benzoin ethyl ether and water to mixture B, mix well, add sodium hyd...

Embodiment 2

[0021] This embodiment provides a high-temperature-resistant wall paint, including the following raw materials in parts by mass: 20 parts of silicone resin, 20 parts of fluororubber, 9 parts of zinc carbonate, 27 parts of aluminum oxide, and 12 parts of sepiolite , 25 parts of quartz powder, 15 parts of aluminum silver paste, 1.2 parts of sodium hydroxide, 8 parts of titanate, 40 parts of boric acid, 5 parts of benzoin ether, and 100 parts of water.

[0022] A preparation method of high temperature resistant wall paint, comprising the following steps:

[0023] Step 1: Add silicone resin, fluororubber, zinc carbonate, aluminum oxide, sepiolite, quartz powder and aluminum silver paste into the mixer, stir and mix evenly to obtain mixture A;

[0024] Step 2: Put mixture A into a grinder and grind for 50 minutes until the fineness is 70 μm to obtain mixture B;

[0025] Step 3: Add titanate, boric acid, benzoin ethyl ether and water to mixture B, mix well, add sodium hydroxide, co...

Embodiment 3

[0027] This embodiment provides a high-temperature-resistant wall paint, including the following raw materials in parts by mass: 15 parts of silicone resin, 14 parts of fluororubber, 5 parts of zinc carbonate, 23 parts of aluminum oxide, and 8 parts of sepiolite , 18 parts of quartz powder, 9 parts of aluminum silver paste, 0.6 part of sodium hydroxide, 4.5 parts of titanate, 28 parts of boric acid, 3.5 parts of benzoin ether, and 80 parts of water.

[0028] A preparation method of high temperature resistant wall paint, comprising the following steps:

[0029] Step 1: Add silicone resin, fluororubber, zinc carbonate, aluminum oxide, sepiolite, quartz powder and aluminum silver paste into the mixer, stir and mix evenly to obtain mixture A;

[0030] Step 2: Put mixture A into a grinder and grind for 35 minutes until the fineness is 55 μm to obtain mixture B;

[0031] Step 3: Add titanate, boric acid, benzoin ethyl ether and water to mixture B, mix well, add sodium hydroxide, co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A high-temperature-resistant wall paint and a preparation method thereof. The paint comprises the following raw materials in parts by mass: 12-20 parts of organic silicon resin, 12-20 parts of fluororubber, 4-9 parts of zinc carbonate, aluminum oxide 20-27 parts, 5-12 parts of sepiolite, 15-25 parts of quartz powder, 7-15 parts of aluminum silver paste, 0.3-1.2 parts of sodium hydroxide, 3-8 parts of titanate, 23-40 parts of boric acid, 2-5 parts of benzoin ether, 70-100 parts of water. The coating provided by the invention has excellent impact resistance, heat resistance, heat insulation and wear resistance, and has a long high temperature resistance time, and is especially suitable for coating walls in high temperature places.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a high-temperature-resistant wall coating and a preparation method thereof. Background technique [0002] Wall paint refers to the decoration and protection of the building wall, making the building wall beautiful and tidy, and at the same time protecting the building wall and prolonging its service life. According to the classification of building walls, wall coatings include two major parts: interior wall coatings and exterior wall coatings. Interior wall coatings focus on decoration and environmental protection; exterior wall coatings focus on protection and durability. In addition to its own decorative and protective functions, wall paint is also developing towards a colorful, fashionable, healthy and environmentally friendly trend. While people hope that the decorative effect of the paint is radiant, beautiful, noble, elegant, romantic, and warm, they also hop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/04C09D127/12C09D7/12
Inventor 胡刚
Owner 泗阳县弘达新型墙体材料有限公司