Outdoor electric-insulation modified epoxy resin composition
An epoxy resin and electrical insulation technology, which is applied in the field of modified epoxy resin compositions, can solve problems such as the electrical insulation properties of materials not mentioned, achieve enhanced mechanical properties and electrical insulation properties, avoid shed damage, and provide excellent electrical properties. performance effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0037] Example 1 (Epoxy resin is not modified by silicone)
[0038] Preparation of epoxy resin composition:
[0039] The formula of the epoxy resin composition is as follows:
[0040]
[0041] Preparation method: (1) Add 100 parts by mass of bisphenol A epoxy resin to the high-speed disperser, heat to 65°C, and stir for 60 minutes; (2) Add 75 parts by mass of surface-modified alumina to the above In the epoxy resin, carry out high-speed dispersion and vacuum degassing treatment, the dispersion time is 3h, the vacuum degree is 100Pa; (3) 50 parts by mass of curing agent methyltetrahydrophthalic anhydride and 3 parts by mass of accelerator benzyldimethylamine Pre-mixing, the mixing temperature is 45℃, the stirring time is 40min, then 75 parts by mass of surface-modified alumina are added, and the high-speed dispersion and vacuum degassing are performed. The dispersion time is 2h and the vacuum degree is 150Pa; (4) Preheat the mold, put a release agent on the cavity, and use the APG p...
Example Embodiment
[0042] Example 2 (epoxy resin modified by silicone)
[0043] Preparation of epoxy resin composition:
[0044] The formula of the epoxy resin composition is as follows:
[0045]
[0046]
Example Embodiment
[0047] Example 3 (epoxy resin modified by silicone)
[0048] Preparation of epoxy resin composition:
[0049] The formula of the epoxy resin composition is as follows:
[0050]
[0051] Preparation method: (1) Add 100 parts by mass of bisphenol A epoxy resin prepolymer modified by amino-terminated polydimethylsiloxane to a high-speed disperser, heat the system to 85°C, and stir The time is 30min to mix the two thoroughly; (2) Add 75 parts by mass of the surface-modified alumina to the above epoxy resin, perform high-speed dispersion and vacuum degassing treatment, the dispersion time is 6h, and the degree of vacuum 200Pa; (3) Premix 50 parts by mass of curing agent methyltetrahydrophthalic anhydride and 3 parts by mass of accelerator benzyldimethylamine, mixing temperature at 55°C, stirring time for 20min, and then adding 75 parts by mass to pass through the surface The modified alumina is subjected to high-speed dispersion and vacuum degassing treatment, the dispersion time is 4h,...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap