Magnesium alloy cutting fluid and preparation method thereof

A technology of cutting fluid and magnesium alloy, which is applied in the direction of lubricating composition and petroleum industry, etc., can solve the problems of insufficient anti-corrosion performance and insufficient hard water resistance, and achieve strong lubricating performance and anti-rust performance, strong hard water resistance, and not easy to break milk effect

Inactive Publication Date: 2014-12-17
句容金猴机械研究所有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Purpose of the invention: In order to solve the problem of insufficient hard water resistance and anti-corrosion performance of magnesium alloy cutting fluid in the prior art, the present invention proposes a magnesium alloy cutting fluid with strong hard water resistance and anti-corrosion performance and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A magnesium alloy cutting fluid, comprising the following components by weight: 20 parts of base oil, 5 parts of modified oleic acid amide, 20 parts of chelating agent, 10 parts of oil-soluble surfactant, 10 parts of fatty acid, 10 parts of silicate 10 parts of antirust agent, 30 parts of water;

[0020] Wherein, the above-mentioned base oil is a mixture of ester lubricating base oil and paraffin base oil, the chelating agent is aminocarboxylic acids, specifically a mixture of EDTA and DTPA, and the rust inhibitor is RT-9411 water-soluble rust inhibitor.

[0021] A preparation method of magnesium alloy cutting fluid, comprising the following steps:

[0022] (1) Mix and stir the required weight of base oil, fatty acid, silicate, chelating agent and antirust agent evenly, heat to 60°C, keep warm for 40min, and then cool to room temperature;

[0023] (2) Add oil-soluble surfactant, modified oleic acid amide and water to the above solvent and heat it to 50°C for 20 minutes...

Embodiment 2

[0025] A magnesium alloy cutting fluid, comprising the following components by weight: 30 parts of base oil, 10 parts of modified oleic acid amide, 30 parts of chelating agent, 20 parts of oil-soluble surfactant, 15 parts of fatty acid, 20 parts of silicate , 15 parts of antirust agent, 45 parts of water;

[0026] Wherein, the above-mentioned base oil is a mixture of naphthenic oil and alcohol base oil, the chelating agent is a mixture of hydroxycarboxylic acids, specifically PAA and MAO, and the rust inhibitor is RT-9417 oil-free water-soluble rust inhibitor.

[0027] A preparation method of magnesium alloy cutting fluid, comprising the following steps:

[0028] (1) Mix and stir the required weight of base oil, fatty acid, silicate, chelating agent and antirust agent, then heat to 80°C, keep warm for 60min, and then cool to room temperature;

[0029] (2) Add oil-soluble surfactant, modified oleic acid amide and water to the above solvent and heat it to 50°C for 30 minutes, c...

Embodiment 3

[0031] A magnesium alloy cutting fluid, comprising the following components by weight: 25 parts of base oil, 8 parts of modified oleic acid amide, 25 parts of chelating agent, 15 parts of oil-soluble surfactant, 13 parts of fatty acid, 15 parts of silicate , 13 parts of antirust agent, 38 parts of water;

[0032] Wherein, the above-mentioned base oil is a mixture of ester lubricating base oil and mineral base oil, the chelating agent is aminocarboxylic acid, specifically a mixture of EGTA and NTA, and the rust inhibitor is RT-9411 water-soluble rust inhibitor.

[0033] A preparation method of magnesium alloy cutting fluid, comprising the following steps:

[0034] (1) Mix and stir the required weight of base oil, fatty acid, silicate, chelating agent and antirust agent evenly, heat to 70°C, keep warm for 50min, and then cool to room temperature;

[0035] (2) Add oil-soluble surfactant, modified oleic acid amide, and water to the above solvent and heat it to 50°C for 25 minutes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a magnesium alloy cutting fluid and a preparation method thereof. Aiming at the characteristics of magnesium alloy, the magnesium alloy cutting fluid is prepared from base oil, modified oleamide, a chelating agent, an oil-soluble surfactant, fatty acid, silicate, an antirust agent and water according to a certain preparation method. The magnesium alloy cutting fluid disclosed by the invention has strong hard water resistance, and strong antiseptic property, lubricating property and anti-corrosion performance, is not easy to demulsify, and has high efficiency and long service life.

Description

technical field [0001] The invention relates to a cutting fluid and its preparation, in particular to a magnesium alloy cutting fluid and a preparation method thereof. Background technique [0002] In the process of metal processing, in order to reduce the cutting force during cutting, take away the heat generated in the cutting area in time to reduce the cutting temperature and prolong the durability of the tool, thereby improving production efficiency, improving the surface roughness of the workpiece, and ensuring the machining accuracy of the workpiece. For best economical results, metal cutting fluids are usually used. Therefore, the main function of cutting fluid has the following four aspects: lubrication, cooling, cleaning and rust prevention. [0003] The density of magnesium alloy is less than 2 / 3 of that of aluminum alloy and 1 / 4 of that of steel. It has high specific strength and specific stiffness, good dimensional stability, machinability, electrical and therma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M173/00C10M173/02C10N40/24C10N30/12
Inventor 张亚夫姚建祥
Owner 句容金猴机械研究所有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products