A method of using a release agent for copper anode plate casting

A technology of copper anode plate and mold release agent, which is applied in the direction of casting mold, casting mold composition, casting molding equipment, etc., can solve the problems of easy wrinkling on the casting surface, traces on the casting surface, and easy formation of pores, etc., so as to improve the appearance quality , lower the mucous membrane, reduce the effect of stomatal bubbling

Active Publication Date: 2016-08-24
KUNMING UNIV OF SCI & TECH TECH IND SALES MANAGEMENT +2
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The thickness of the coating film should also be strictly controlled. If it is too thick, it will cool slowly, and it is easy to form pores, and the surface of the casting is also easy to wrinkle; if it is too thin, it is easy to crack, and the surface of the casting will have marks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] Hereinafter, embodiments of the present invention will be described in detail. It should be noted that the technical features or combinations of technical features described in the following embodiments should not be regarded as isolated, and they can be combined and combined with each other to achieve better technical effects.

[0019] A method of using a mold release agent for copper anode plate casting, comprising the following steps:

[0020] Prepare a release agent emulsion. Mix water and release agent according to the mass liquid-solid ratio of 1.8 to 2.2:1, the water temperature is 65°C to 85°C, and stir evenly, and maintain a stable stirring state during use to prevent the release agent from settling. The release agent used is a composite release agent, and its composition is calculated by mass ratio, including 30% to 70% barium sulfate, 2.5% to 15% boron oxide, 20% to 45% silicon dioxide, 1% to 8 % calcium oxide and 1% to 7% aluminum oxide.

[0021] Spray re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for using a release agent for copper anode plate casting, comprising the following steps: preparing a release agent emulsion; spraying the release agent emulsion; and forming a release agent protective layer by the release agent emulsion ; The protective layer of the release agent is sintered to form a sintered layer of the release agent; the sintered layer of the release agent is separated from the anode plate. Through this method, the release agent can form a sintered layer of release agent on the surface of the copper mold, reduce the occurrence of adhesion between the copper mold and the anode plate, reduce the bubbling of pores on the surface of the anode plate, improve the quality of the anode plate, and protect the copper mold. Extend its service life.

Description

technical field [0001] The invention relates to a method for using a release agent for copper anode plate casting. Background technique [0002] In the casting process of anode copper in the current copper smelting process, the Outokumpu disc casting machine has been widely used, and the mold types used by the disc casting machine are divided into steel molds and copper molds, and steel molds will not occur during the production process. The phenomenon of anode plate sticking to the mold, but the copper production enterprise cannot complete the repair and processing after the steel mold is damaged, and must go to other related enterprises for processing, which delays the production progress and increases the production cost. After the copper mold is damaged, it can be cast by the manufacturer itself, which greatly improves the convenience of production. However, due to the sticking phenomenon of the copper mold and the cast anode copper plate, when using the copper mold, in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22C3/00B22C23/02B22D25/04
Inventor 沈强华于海波陈雯王家波刘中华何军黄智超钟忠马涛王旭孙安平蒋鸿
Owner KUNMING UNIV OF SCI & TECH TECH IND SALES MANAGEMENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com