A kind of putty powder with high waterproof, high hardness and high adhesion for building exterior wall

A high-adhesion, building exterior wall technology, applied in the field of high waterproof, high-adhesion putty powder and high hardness for building exterior walls, can solve the problems of poor waterproof performance, poor putty powder hardness, and weak adhesion, etc. The effect of strong adhesion, good waterproof performance and excellent product performance

Active Publication Date: 2016-08-24
WUXUE ZHEWU CALCIUM IND CO LTD
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problems of poor hardness, poor waterproof performance, and weak adhesion in traditional putty powder for exterior walls, and provide a high waterproof, high hardness, and high adhesion putty powder for building exterior walls.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A kind of high waterproof, high hardness, high adhesion putty powder for building exterior walls of the present embodiment is composed of the following raw materials in parts by weight:

[0040] White cement 2500kg Calcium bicarbonate 1500kg

[0041] Talc powder 3000kg Ash calcium powder 3000kg

[0042] Paraffin 10kg Quartz Powder 900kg

[0043] Propylamine 7kg Hydroxypropyl methylcellulose 15kg

[0044] Wood fiber 8kg Rubber powder 3kg

[0045] Pigment 8kg.

[0046] The particle size of the white cement is 250-350 mesh; the particle size of the calcium bicarbonate is 280-380 mesh; the particle size of the talc powder is 250-350 mesh; the particle size of the ash calcium powder is 350-450 mesh; The particle size of the quartz powder is 250 to 300 mesh, SiO 2 The content is ≥99.0%; the particle size of the rubber powder is 5-120 meshes.

[0047] The preparation method of the putty powder in this embodiment is as follows: after mixing all the above-mentioned raw mat...

Embodiment 2

[0057] A high-waterproof, high-hardness, high-adhesion putty powder for building exterior walls of the present embodiment is composed of the following raw materials in parts by weight:

[0058] White cement 30 Calcium bicarbonate 20

[0059] Talc 25 Ash Calcium 30

[0060] Paraffin 0.12 Quartz Powder 12

[0061] Propylamine 0.1 Hydroxypropyl methylcellulose 0.15

[0062] Wood fiber 0.1 Rubber powder 0.35

[0063] Pigment 0.05.

[0064] The particle size of the white cement is 250-350 mesh; the particle size of the calcium bicarbonate is 280-380 mesh; the particle size of the talc powder is 250-350 mesh; the particle size of the lime calcium powder is 350-450 mesh; The particle size of the quartz powder is 250 to 300 mesh, SiO 2 The content is ≥99.0%; the particle size of the rubber powder is 5-120 mesh.

[0065] The preparation method and use method are the same as those in Example 1.

Embodiment 3

[0067] A high-waterproof, high-hardness, high-adhesion putty powder for building exterior walls of the present embodiment is composed of the following raw materials in parts by weight:

[0068] White cement 20 Calcium bicarbonate 8

[0069] Talc 35 Ash Calcium 20

[0070] Paraffin 0.08 Quartz Powder 5

[0071] Propylamine 0.05 Hydroxypropyl methylcellulose 0.2

[0072] Wood fiber 0.05 Rubber powder 0.2

[0073] Pigment 0.1.

[0074] The particle size of the white cement is 250-350 mesh; the particle size of the calcium bicarbonate is 280-380 mesh; the particle size of the talc powder is 250-350 mesh; the particle size of the lime calcium powder is 350-450 mesh; The particle size of the quartz powder is 250 to 300 mesh, SiO 2 The content is ≥99.0%; the particle size of the rubber powder is 5-120 mesh.

[0075] The preparation method and use method are the same as those in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of building materials, and is a high-waterproof, high-hardness, high-adhesion putty powder for building exterior walls, which is composed of the following raw materials in parts by weight: 20-30 parts by weight of white cement, and 8-20 parts by weight of calcium bicarbonate , talc powder 25~35, gray calcium powder 20~30, paraffin wax 0.08~0.12, quartz powder 5~12, propylamine 0.05~0.1, hydroxypropyl methylcellulose 0.15~0.2, wood fiber 0.05~0.1 rubber powder 0.2~ 0.35, pigment 0.05-0.1, the product formula of the invention is reasonable, the preparation method is simple, and the product performance is excellent, which effectively solves the problem of the low hardness, poor waterproof performance and weak adhesion of the existing putty powder for external walls, which is easy to cause construction workers to repeat construction Or the problem of high wall repair rate; the putty powder coating scraped by the product of the present invention has hardness comparable to that of granite, and good waterproof performance, strong adhesion, and almost zero repair rate, which is suitable for wide application.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a high waterproof, high hardness and high adhesion putty powder for building exterior walls. Background technique [0002] Putty powder is a building material with a large amount in architectural decoration. Before painting the wall, putty powder must be used to prime the wall. Traditional putty powder mainly uses white cement and gray calcium powder as raw materials, and generates stable calcium carbonate by self-solidification and absorption of carbon dioxide in the air. Therefore, the calcification reaction of gray calcium powder (calcium hydroxide) in traditional putty powder mainly occurs in putty. The surface layer of the powder coating, and the inner layer of the coating also has a large amount of unstable calcium oxide and calcium hydroxide, which leads to the following problems in the traditional putty powder coating: 1. Poor hardness: the calcification rate i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/34
Inventor 刘元庆
Owner WUXUE ZHEWU CALCIUM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More