Fly ash high-foaming furniture plate

A technology of fly ash and high foaming, applied in the field of furniture boards, can solve problems such as environmental pollution, scratches caused by hard objects, poor wear resistance, etc., and achieve the effects of reducing costs, reducing dosage, and being convenient to use

Inactive Publication Date: 2015-01-28
朔州市润臻新技术开发有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this kind of wooden furniture is that it has poor wear resistance and is easily scratched by hard objects; in addition, due to the presence of harmful chemicals in many paints or adhesives, it often emits harmful gases to the human body, which is easy to cause damage to the human body. environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The raw material formula ratio of a kind of fly ash high foaming furniture board is: 280-300 mesh fine fly ash 43kg, 1mm rock wool 0.05kg, 80-100 mesh coarse fly ash 10kg, 1000-1200 mesh talcum powder 2.6kg, PVC 42kg, PVC recycling waste 6.9kg, lead salt composite stabilizer 2.0kg, ABS 1.8kg, ACR (401) 1.7kg, NC white foaming agent 0.6kg, paraffin 0.2kg, LP-60 (neutral saturated fatty alcohol two Carboxylic ester) 0.3kg, AC foaming agent 0.15kg, ACR (530) foaming and moisturizing agent 7.8kg, ACR (175) lubricating processing aid 0.8kg, stearic acid 1kg.

[0018] A kind of preparation method of fly ash high foaming furniture board is:

[0019] (1) Weigh the materials according to the ratio of the above raw material formula;

[0020] (2) Pour the two kinds of fly ash and talcum powder weighed above into a thermomixer and stir for 18 minutes, then add PVC and stir for 9 minutes, then add other ingredients of the above formula and stir;

[0021] (3) Put the above compound...

Embodiment 2

[0027] The raw material formula ratio of a kind of fly ash high foaming furniture board is: 280-300 mesh fine fly ash 44kg, 1mm rock wool 0.06kg, 80-100 mesh coarse fly ash 11kg, 1000-1200 mesh talcum powder 2.7kg, PVC 43kg, PVC recycled waste 7kg, lead salt composite stabilizer 2.1kg, ABS 2kg, ACR (401) 1.8kg, NC white foaming agent 0.7kg, paraffin 0.3kg, LP-60 (neutral saturated fatty alcohol dicarboxylic acid Grease) 0.25kg, AC foaming agent 0.25kg, ACR (530) foaming and moisturizing agent 8kg, ACR (175) lubricating processing aid 1kg, stearic acid 1kg.

[0028] A kind of preparation method of fly ash high foaming furniture board is:

[0029] (1) Weigh the materials according to the ratio of the above raw material formula;

[0030] (2) Pour the two kinds of fly ash and talcum powder weighed above into a thermomixer and stir for 19 minutes, then add PVC and stir for 9 minutes, then add other ingredients of the above formula and stir;

[0031] (3) Put the above compound int...

Embodiment 3

[0037] The raw material formula ratio of a kind of fly ash high foaming furniture board is: 280-300 mesh fine fly ash 45kg, 1mm rock wool 0.05kg, 80-100 mesh coarse fly ash 10kg, 1000-1200 mesh talcum powder 2.6kg, PVC 43kg, PVC recycled waste 6.9kg, lead salt composite stabilizer 2.1kg, ABS 1.8kg, ACR (401) 1.7kg, NC white foaming agent 0.6kg, paraffin 0.2kg, LP-60 (neutral saturated fatty alcohol two Carboxylic ester) 0.3kg, AC foaming agent 0.2kg, ACR (530) foaming and moisturizing agent 8kg, ACR (175) lubricating processing aid 0.9kg, stearic acid 1.1kg.

[0038] A kind of preparation method of fly ash high foaming furniture board is:

[0039] (1) Weigh the materials according to the ratio of the above raw material formula;

[0040] (2) Pour the two kinds of fly ash and talcum powder weighed above into a thermomixer and stir for about 17 minutes, then add PVC and stir for about 8 minutes, then add other ingredients of the above formula and stir;

[0041] (3) Put the abov...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fly ash high-foaming furniture plate which is prepared from 42-45kg of 280-300-mesh fine fly ash, 0.05-0.06kg of 1mm rock wool, 10-11kg of 80-100-mesh coarse fly ash, 2.5-2.7kg of 1000-1200-mesh talcum powder, 42-43kg of PVC (polyvinyl chloride), 6.8-7kg of PVC recycled waste, 1.9-2.1kg of lead salt composite stabilizer, 1.8-2kg of ABS (acrylonitrile-butadiene-styrene), 1.6-1.8kg of ACR (401), 0.5-0.75kg of NC white foaming agent, 0.2-0.3kg of paraffin, 0.25-0.3kg of LP-60 (neutral saturated fat alcohol dicarboxylate), 0.15-0.25kg of AC (azodicarbonamide) foaming agent, 7.5-8kg of ACR (530) foaming regulator, 0.8-1kg of ACR (175) lubricating processing assistant and 1-1.1kg of stearic acid. The manufacturing process comprises the following steps: weighing the materials; stirring the fly ash and talcum powder, adding the PVC, stirring, adding the other materials, and stirring; extruding a formed billet by an extruder; and preparing the formed billet into furniture. The fly ash high-foaming furniture plate has the advantages of light weight, elegant appearance, corrosion resistance and weathering resistance.

Description

technical field [0001] The invention relates to a furniture board, in particular to a high-foaming fly ash furniture board. Background technique [0002] Fly ash is the fine ash collected from the flue gas after coal combustion. Fly ash is the main solid waste discharged from coal-fired power plants. Fly ash is one of the largest industrial wastes in my country. With the development of the power industry, the discharge of fly ash from coal-fired power plants is increasing year by year. If a large amount of fly ash is not treated, it will generate dust and pollute the atmosphere; if it is discharged into the water system, it will cause river silting, and the toxic chemicals in it will also cause harm to human beings and organisms. All kinds of wooden furniture currently on the market are mostly processed by furniture boards such as solid wood jigsaw panels, composite panels, particle boards, blockboards, and medium-density fiberboards. There is usually a layer of paint or ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B38/02
Inventor 胡勇
Owner 朔州市润臻新技术开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com