A kind of preparation method of propylene copolymer with low ethylene content and broad molecular weight distribution

A technology of propylene copolymer and propylene, which is applied in the field of preparation of propylene copolymer, and can solve problems such as high cost, complex catalyst synthesis technology, and insufficiently wide polymer molecular weight distribution.

Active Publication Date: 2017-01-25
PETROCHINA CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Chinese patents US2009023881A1, CN1266066A, US2011034649A1, CN102159594A, CN101213249A, and CN1163621 disclose methods for manufacturing polypropylene with a wide molecular weight distribution. The technology for manufacturing polypropylene with a wide distribution is based on catalyst composition or process control. The catalyst synthesis technology is complicated and costly. The universality of polymerization process control is poor, and the molecular weight distribution of the obtained polymer is not wide enough, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of propylene copolymer with low ethylene content and broad molecular weight distribution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037]The external electron donor is selected from isopropyltriethoxysilane (NPTES), the first polymer ethylene content is 0.35-0.45% (wt), and the second polymer hydrogen concentration is 9000-11000.

Embodiment 2

[0039] The external electron donor is selected from isopropyltriethoxysilane, the first polymer ethylene content is 0.15-0.25% (wt), and the second polymer hydrogen concentration is 9000-11000.

Embodiment 3

[0041] The external electron donor is selected from isopropyltriethoxysilane, the ethylene content of the first polymer is 0.05-0.15% (wt), and the hydrogen concentration of the second polymer is 9000-11000.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a propylene copolymer with ethylene content lower than 0.5% (wt) and wide molecular weight distribution. The method comprises a catalyst system and a two-step polymerization process. The catalyst system comprises a Ziegler-Natta catalyst with organosilane with extremely high hydrogen sensitivity. With the catalyst system, extremely high molecular weight can be produced in first step polymerization, and extremely low molecular weight can be produced in the second step. Polymerization products obtained in the two steps are mechanically mixed, wherein melt flow rate ratio (2.16kg, 230 DEG C) of the fist step and the second step is higher than 400, such that the propylene copolymer with wide molecular weight distribution can be obtained.

Description

technical field [0001] The invention relates to a preparation method of a propylene copolymer, in particular to a preparation method of a propylene copolymer with low ethylene content and wide molecular weight distribution. The propylene copolymer can be used in the field of polypropylene foaming, but not limited to this field. Background technique [0002] Polypropylene is one of the most widely used and fastest growing synthetic resins in the world. However, due to poor toughness and low melt strength of ordinary polypropylene, its application in extrusion coating, blow molding and foam molding is greatly limited, so high melt strength polypropylene technology has a bright future, theoretical research shows , a wide molecular weight distribution can greatly enhance the melt strength of polypropylene, so the method of manufacturing polypropylene with a wide molecular weight distribution is an area of ​​interest to the theoretical and industrial circles. [0003] The wide d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F210/16C08F2/38C08F4/649
Inventor 刘义李广全许云波陈旭竺栋荣张长军刑赵中张庆国张保生谢岳庆慕雪梅林风强吴冬何永福李汝光
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com