Diamond-micropowder-containing ceramic for nozzle and preparation method of diamond-micropowder-containing ceramic
A diamond micropowder and nozzle technology, applied in the field of ceramic materials, can solve the problems of not too high wear resistance, poor wear resistance, poor acid and alkali resistance, etc., and achieve the effect of increasing surface smoothness, high wear resistance and cost saving
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment Construction
[0014] A ceramic for nozzles containing diamond micropowder is made from the following raw materials in parts by weight (kg): strontium carbonate 2.5, boric acid 1.5, aluminum nitride 15, P2O5 1.5, Al2O3 36, K2O 1.5, diamond micropowder 3.5, silicon carbide 64 , bamboo charcoal powder 1.5, appropriate amount of deionized water, ethyl orthosilicate 3.5, appropriate amount of ethanol, auxiliary 5;
[0015] The auxiliary agent is made from the following raw materials in parts by weight (kg): kaolin 0.8, zircon 3.5, lanthanum oxide 0.2, diamond powder 0.2, Y2O3 0.3, La2O3 0.3, beryllium oxide 0.3, silane coupling agent kh-550 0.7 , polyethylene glycol 0.3, water 8; the preparation method is: pulverize zircon, pass through a 100-mesh sieve to obtain zircon powder; add polyethylene glycol into water, stir evenly, add zircon powder, stir for 25 minutes, Then add half weight of silane coupling agent kh-550, stir for 13 minutes, then add kaolin, stir and react for 25 minutes, then add ...
PUM
Property | Measurement | Unit |
---|---|---|
Vickers hardness | aaaaa | aaaaa |
flexural strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap