Electrically heated automobile windshield glass

A windshield, electric heating technology, applied in the direction of windshield, vehicle parts, windows, etc., can solve the problems of easy cracking and uneven heating of glass, and achieve the effect of improving rear view, uniform heating, and easy thermal bending.

Inactive Publication Date: 2015-03-11
DALIAN HEPTACHROMA SOLAR TECH CO LTD
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the above-mentioned problem that the traditional automobile windshield wire is heated, the automobile glass is heated unevenly, and the car glass is prone to bursting; Heated car windshield glass, the electric heated car windshield glass has beautiful appearance and good rear view effect; and the electric heated car windshield glass adopts surface heating method, which is evenly heated and not easy to burst, and the speed of defrosting, deicing and snow removal is fast

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrically heated automobile windshield glass
  • Electrically heated automobile windshield glass
  • Electrically heated automobile windshield glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] This embodiment discloses an electric heating automobile windshield, such as figure 1 As shown, it is a layer of FTO conductive glass substrate, electrodes are printed or pasted on the edges of the left and right sides of the FTO conductive glass substrate, and the electrodes are electrically connected to the power supply. The FTO conductive glass substrate is a float glass substrate deposited with an FTO conductive film, and the FTO conductive film is a transparent conductive layer of tin oxide doped with fluorine. The thickness of the FTO conductive glass substrate is: 20mm, and the thickness of the FTO conductive film is: 1000nm. The sheet resistance of the FTO conductive glass substrate is: 7ohm / □(7ohm / sq). The electrodes are conductive film silver bars. The power applied to the electrodes was 36V. The current direction 7 is indicated by the arrow.

[0047] The preparation method of electric heating automobile windshield of the present embodiment comprises the fo...

Embodiment 2

[0053] This embodiment discloses an electric heating automobile windshield, such as figure 2 As shown, it is a layer of FTO conductive glass substrate, electrodes are printed or pasted on the upper and lower edges of the FTO conductive glass substrate, and the electrodes are electrically connected to the power supply. The FTO conductive glass substrate is a borosilicate glass substrate deposited with an FTO conductive thin film. FTO is a transparent conductive layer of tin oxide doped with fluorine. The thickness of the FTO conductive glass substrate is: 2mm, and the thickness of the FTO conductive film is: 50nm. The sheet resistance of the FTO conductive glass substrate is: 7ohm / □ (7ohm / sq). The electrodes are conductive strips, conductive films or conductive glue. The power applied to the electrodes was 24V. The current direction 7 is indicated by the arrow.

[0054] The preparation method of electric heating automobile windshield of the present embodiment comprises the...

Embodiment 3

[0060] This embodiment discloses an electric heating automobile windshield, such as image 3 As shown, it is a layer of FTO conductive glass substrate, electrodes are printed or pasted on the edges of the left and right sides of the FTO conductive glass substrate, and the electrodes are electrically connected to the power supply. The FTO conductive glass substrate is a float glass substrate deposited with an FTO conductive thin film. FTO is a transparent conductive layer of tin oxide doped with fluorine. The thickness of the FTO conductive glass substrate is: 10mm, and the thickness of the FTO conductive film is: 100nm. The sheet resistance of the FTO conductive glass substrate is: 7ohm / □(7ohm / sq). The electrodes are conductive strips, conductive films or conductive glue. The power applied to the electrodes was 24V. The current direction 7 is indicated by the arrow.

[0061] The preparation method of electric heating automobile windshield of the present embodiment comprise...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technology of automobile glass, and discloses an automobile electric heating glass window and a manufacturing method. Firstly, trapezoid cutting, edge polishing and washing are carried out on an FTO conductive glass substrate, and the FTO conductive glass substrate is dried to be used later; secondly, the hot bending and the tempering process are carried out on the processed FTO conductive glass substrate through a die, and after bent glass with the needed strength and curvature is obtained, the edge and two opposite frames of the glass substrate are printed or pasted with conductive metal strips to form the positive electrode and the negative electrode; lastly, the positive electrode metal strip and the negative electrode strip are connected with a power source through an electrical connecting device, and then the automobile electric heating glass window is manufactured. The face heating method is adopted, the automobile glass can be heated more evenly, and bursting caused by uneven heating of the glass is effectively prevented; under the high temperature, the sheet resistance change is very small, the heating performance of the automobile electric heating glass window is changed little even when the automobile electric heating glass window is processed through heating bending and tempering, the appearance of an automobile can be beautified, and the back vision effect of a driver can be improved.

Description

technical field [0001] The invention relates to the automobile windshield technology, in particular to an electric heating automobile windshield. Background technique [0002] Automobile glass is one of the important safety components of automobiles. It has the functions of protecting occupants, waterproofing, dustproofing, heat resistance and sound insulation. Today, the area of ​​automotive glass accounts for about 1 / 3 of the surface area of ​​a car. According to the application site, automotive glass mainly includes front windshield glass, rear windshield glass, door glass, sunroof glass and front / rear corner window glass, etc. As early as 40 years ago, the windshield of automobiles had adopted a single-piece curved windshield, and gradually abandoned the flat windshield. Today's car windshields are generally made into a large curved surface with a certain curvature on the top, bottom, left, and right. With the development of the automobile industry, the application of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B60J1/00
Inventor 杨希川
Owner DALIAN HEPTACHROMA SOLAR TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products