Multi-sulfonate type cement water reducing agent and preparation method thereof

A polysulfonate and water-reducing agent technology, applied in the field of fine chemicals preparation, can solve the problems of non-conformity with green production, poor water-reducing performance, irritating odor, etc., and achieves low equipment requirements, easy operation, enhanced The effect of dispersion properties

Active Publication Date: 2015-04-01
SHAANXI UNIV OF SCI & TECH
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of them are monosulfonic acid groups and disulfonic acid groups, and their water-reducing performance is not good. At the same time, the raw materials are polluted and have pungent odors, which do not meet the requirements of green production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A polysulfonate cement water reducer, its raw material components and consumption are as follows:

[0025] Allyl polyoxyethylene ether with a molecular weight of 500, maleic anhydride, p-toluenesulfonic acid and NaHSO 3 ; Wherein, the mol ratio of maleic anhydride and allyl polyoxyethylene ether is 1.0:2.0; p-toluenesulfonic acid accounts for 0.6% of the total mass of maleic anhydride and allyl polyoxyethylene ether; NaHSO 3 The molar ratio with maleic anhydride is 3.6:1.0.

[0026] The preparation process of the polysulfonate cement water reducer:

[0027] Slowly raise the temperature of allyl polyoxyethylene ether to 50°C for complete liquefaction, then quickly add maleic anhydride and p-toluenesulfonic acid, control the temperature at 100°C, stir continuously for 10 hours, and then dissolve NaHSO 3 Prepare a solution with a mass fraction of 20% and add dropwise, keep the temperature at 80°C, and stir for about 5 hours to prepare the trisulfonic acid-based water red...

Embodiment 2

[0029] A polysulfonate cement water reducer, its raw material components and consumption are as follows:

[0030] Allyl polyoxyethylene ether with a molecular weight of 1500, maleic anhydride, p-toluenesulfonic acid and NaHSO 3 ; Wherein, the mol ratio of maleic anhydride and allyl polyoxyethylene ether is 1.0:2.1; p-toluenesulfonic acid accounts for 0.6% of the total mass of maleic anhydride and allyl polyoxyethylene ether; NaHSO 3 The molar ratio with maleic anhydride is 3.2:1.0.

[0031] The preparation process of the polysulfonate cement water reducer:

[0032] Slowly raise the temperature of allyl polyoxyethylene ether to 60°C and completely liquefy it, then quickly add maleic anhydride and p-toluenesulfonic acid, control the temperature at 110°C, keep stirring for 8 hours, then dissolve NaHSO 3 Prepared as a solution with a mass fraction of 20% and added dropwise ， Keep the temperature at 90°C and stir for about 4 hours to prepare the trisulfonic acid-based water redu...

Embodiment 3

[0034] A polysulfonate cement water reducer, its raw material components and consumption are as follows:

[0035] Allyl polyoxyethylene ether with a molecular weight of 2500, maleic anhydride, p-toluenesulfonic acid and NaHSO 3 ; Wherein, the mol ratio of maleic anhydride and allyl polyoxyethylene ether is 1.0:2.4; p-toluenesulfonic acid accounts for 0.9% of the total mass of maleic anhydride and allyl polyoxyethylene ether; NaHSO 3 The molar ratio with maleic anhydride is 3.4:1.0.

[0036] The preparation process of the polysulfonate cement water reducer:

[0037] Slowly raise the temperature of allyl polyoxyethylene ether to 75°C and completely liquefy it, then quickly add maleic anhydride and p-toluenesulfonic acid, control the temperature at 130°C, keep stirring for 6 hours, then dissolve NaHSO 3 It is prepared as a solution with a mass fraction of 20% and added dropwise, keeping the temperature at 100°C and stirring for about 3 hours to obtain a trisulfonic acid-based w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a multi-sulfonate type cement water reducing agent and a preparation method thereof, and belongs to the technical field of fine chemical product preparation. The multi-sulfonate type cement water reducing agent is prepared from the following raw materials: allyl polyoxyethylene ether, acid anhydride, a catalyst and NaHSO3. The preparation method comprises the following steps: firstly, mixing allyl polyoxyethylene ether, acid anhydride and the catalyst, heating and continuously stirring to react for 6-10 hours, so as to generate a polymer with double bonds at two ends and the middle part; adjusting the temperature, and dropping NaHSO3, thereby preparing the multi-sulfonate type cement water reducing agent. The preparation method disclosed by the invention is simple and convenient to operate, easy in process control, low in equipment requirement, environment-friendly, and applicable to industrialization large-scale production. The multi-sulfonate type cement water reducing agent prepared by using the method is excellent in water reduction property and dispersion property.

Description

technical field [0001] The invention belongs to the technical field of preparation of fine chemicals, and in particular relates to a polysulfonate cement water reducer and a preparation method thereof. Background technique [0002] At present, according to the water reducing and strengthening ability of the water reducing agent, the water reducing agent can be mainly divided into four categories: one is the ordinary water reducing agent mainly based on lignin, and most of this type of water reducing agent is powdery and low air-entraining Retarder, with micro-air-entraining properties, can improve the anti-seepage freeze-thaw performance of concrete. However, the molecular structure of this type of water reducer is dominated by aromatic rings, and its flexibility is poor. The second is a high-efficiency water-reducer represented by a naphthalene-based water-reducer. This type of water-reducer is favored for its environmental protection and high plasticity. However, due to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/16C08G65/00C04B103/30
Inventor 李刚辉樊孟孟宋洁樊文娜
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap