A technology of sutures and collagen fibers, applied in the field of sutures, can solve the problems of suture quality influence, material hydrolysis deterioration, mechanical strength decline, etc., to achieve the effects of accelerating wound healing, avoiding infection, and stabilizing the absorption period

Active Publication Date: 2015-04-08
SHANDONG BODA MEDICAL PROD CO LTD +1
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, chemical line raw materials are less and are controlled by foreign companies, so it is extremely difficult to obtain, and the cost increases a lot
In addition, if the moisture content of the chemical thread is too high, the material will be hydrolyzed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1

[0021] The present invention is used to prepare an absorbable suture thread, and its preparation method includes the following steps:

[0022] (1) Isolate protein chorionic membrane: select fresh goat casings, wash the inner wall of the casing, and scrape the chorionic membrane, mucosa, serous membrane, etc. in the casing to make it fall off;

[0023] (2) Collagen fiber purification: clean the sheep casings with water, soak them in 0.9% sodium chloride solution for 30 minutes, take them out and soak them in 30% sodium chloride solution for 10 minutes, and then separate and remove them. The fat in the collagen fiber obtains relatively pure collagen fiber;

[0024] (3) Degreasing and degreasing: Add the purified collagen fiber to a 0.5% sodium hydroxide solution at a temperature of 40 degrees Celsius and soak for 15 minutes. The solution also contains 1% lauryl sulfuric acid by weight. Sodium, which separates all the grease between the collagen fibers, clean it with ...

Example Embodiment

[0031] Example 2

[0032] The present invention is used to prepare an absorbable suture thread, and its preparation method includes the following steps:

[0033] (1) Isolate protein chorionic membrane: select fresh goat casings, wash the inner wall of the casing, and scrape the chorionic membrane, mucosa, serous membrane, etc. in the casing to make it fall off;

[0034] (2) Collagen fiber purification: clean the sheep casings with water, soak them in 0.9% sodium chloride solution for 30 minutes, take them out and soak them in 30% sodium chloride solution for 10 minutes, and then separate and remove them. The fat in the collagen fiber obtains relatively pure collagen fiber;

[0035] (3) Degreasing and degreasing: Add the purified collagen fibers to a 2% sodium hydroxide solution at a temperature of 60 degrees Celsius and soak for 10 minutes. The solution is also added with 0.5% dodecylbenzene by weight. Sodium sulfonate, so that all the grease between the collagen fibers is separated ...

Example Embodiment

[0042] Example 3

[0043] The present invention is used to prepare an absorbable suture thread, and its preparation method includes the following steps:

[0044] (1) Isolate protein chorionic membrane: select fresh goat casings, wash the inner wall of the casing, and scrape the chorionic membrane, mucosa, serous membrane, etc. in the casing to make it fall off;

[0045] (2) Collagen fiber purification: clean the sheep casings with water, soak them in 0.9% sodium chloride solution for 30 minutes, take them out and soak them in 30% sodium chloride solution for 10 minutes, and then separate and remove them. The fat in the collagen fiber obtains relatively pure collagen fiber;

[0046] (3) Degreasing and degreasing: Add the purified collagen fibers to a 1.5% sodium hydroxide solution at a temperature of 55 degrees Celsius and soak for 12 minutes. The solution is also added with 0.8% sodium stearate by weight. Separate all the grease between the collagen fibers, clean it with water and se...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to sutures and in particular relates to a method for preparing an absorbable suture. The method for preparing the absorbable suture disclosed by the invention comprises the following steps: (1) separating protein chorion; (2) purifying collagen fibers; (3) deoiling and degreasing; (4) inactivating viruses; (5) performing chrome tanning; (6) performing crosslinking dehydration; (7) polishing; (8) performing chitosan atomization; and (9) packaging. The absorbable suture prepared by the method disclosed by the invention has the characteristics of high tensile strength, knotting firmness, high biocompatibility and small toxic and side effects, and the suture can be absorbed by the body. The suture is completely absorbed, an absorption reaction is avoided, the suture does not need to be taken out, the tissue compatibility is high, and an adverse reaction in the human body is avoided regardless of the time; and moreover, the surface is smooth, the suture is difficultly infected by germs, and infection can be avoided.

Description

(1) Technical field [0001] The invention relates to a suture, in particular to a preparation method of an absorbable suture. (2) Background technology [0002] Medical sutures belong to the category of medical devices. Sutures are divided into two categories in the same industry: one is non-absorbable sutures: silk threads, polypropylene threads, nylon threads, etc.; the other is absorbable sutures: respectively for chemical and biological lines. At present, PGA chemically absorbable sutures are widely used in my country. However, the chemical line raw materials are less and controlled by foreign companies, so it is extremely difficult to obtain, and the cost increases a lot. In addition, if the moisture content of the chemical thread is too high, the material will be hydrolyzed and deteriorated, the mechanical strength will be reduced, and the quality of the suture will be seriously affected. Therefore, the raw materials of the chemical line rely heavily on imports, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L17/08
Inventor 张玉福高宏宇张硕黄绍青
Owner SHANDONG BODA MEDICAL PROD CO LTD
Who we serve
  • R&D Engineer