Bacteriostatic coating and preparation method thereof

A coating and polyacrylate emulsion technology, applied in the field of coatings, can solve the problems of loss of use value and shortened life, and achieve the effect of wide application range and good comprehensive performance

Inactive Publication Date: 2015-04-08
张明
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Steel is an important engineering and structural material, but d

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A kind of bacteriostatic coating, comprises following weight components: 25 parts of polyacrylate emulsions, 15 parts of polyurethane emulsions, 6 parts of nano-alumina, 5 parts of talcum powders, 5 parts of dispersants, 5 parts of adsorbents, 7 parts of curing agents, 2 parts of chitin, 4 parts of thixotropic agent, 3 parts of thickener, 2 parts of defoamer, 22 parts of deionized water.

[0013] A method for preparing the antibacterial coating, the method may further comprise the steps:

[0014] (1) 100 parts of formic acid solution with a mass fraction of 1% was used to dissolve the chitin in the proportion to prepare a chitin solution;

[0015] (2) Put the deionized water, defoamer, dispersant, nano-alumina, talcum powder, polyacrylate emulsion, polyurethane emulsion, adsorbent, and curing agent into the high-speed stirring and shearing machine in sequence , chitin solution, thixotropic agent, thickener, and stir at a low speed while feeding; after feeding, stir at ...

Embodiment 2

[0017] A kind of bacteriostatic coating, comprises following weight components: 45 parts of polyacrylate emulsions, 20 parts of polyurethane emulsions, 15 parts of nano-alumina, 10 parts of talcum powders, 10 parts of dispersants, 10 parts of adsorbents, 15 parts of curing agents, 15 parts of chitin, 10 parts of thixotropic agent, 8 parts of thickener, 8 parts of defoamer, 25 parts of deionized water.

[0018] A method for preparing the antibacterial coating, the method may further comprise the steps:

[0019] (1) Use 50 parts of formic acid solution with a mass fraction of 1% to dissolve the chitin in the proportion to prepare a chitin solution;

[0020] (2) Put the deionized water, defoamer, dispersant, nano-alumina, talcum powder, polyacrylate emulsion, polyurethane emulsion, adsorbent, and curing agent into the high-speed stirring and shearing machine in sequence , chitin solution, thixotropic agent, thickener, and stir at a low speed while feeding; stir at a speed of 500...

Embodiment 3

[0022] A kind of bacteriostatic coating, comprises following weight components: 30 parts of polyacrylate emulsions, 20 parts of polyurethane emulsions, 7 parts of nano-alumina, 5 parts of talcum powders, 5 parts of dispersants, 5 parts of adsorbents, 7 parts of curing agents, 5 parts of chitin, 4 parts of thixotropic agent, 5 parts of thickener, 3 parts of defoamer, 15 parts of deionized water.

[0023] A method for preparing the antibacterial coating, the method may further comprise the steps:

[0024] (1) Use 60 parts of formic acid solution with a mass fraction of 1% to dissolve the chitin in the proportion to prepare a chitin solution;

[0025] (2) Put the deionized water, defoamer, dispersant, nano-alumina, talcum powder, polyacrylate emulsion, polyurethane emulsion, adsorbent, and curing agent into the high-speed stirring and shearing machine in sequence , chitin solution, thixotropic agent, thickener, and stir at a low speed while feeding; after feeding, stir at a spee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a bacteriostatic coating and a preparation method thereof, and belongs to the coating field; the bacteriostatic coating comprises the following components by weight: 25-45 parts of a polyacrylate emulsion, 15-20 parts of a polyurethane emulsion, 6-15 parts of nano alumina, 5-10 parts of a talcum powder, 5-10 parts of a dispersing agent, 5-10 parts of an adsorbent, 7-15 parts of a curing agent, 2-15 parts of chitin, 4-10 parts of a thixotropic agent, 3-8 parts of a thickening agent, 2-8 parts of a defoaming agent, and 22-25 parts of deionized water. The bacteriostatic coating has the achieved beneficial effects that the formaldehyde release amount of the bacteriostatic coating is 0 g/L, a TVOC value is 0 g/L, and the coating also has waterproof and bacteriostatic effects, the application range is wider, and a coating film has better comprehensive performance.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to an antibacterial coating and a preparation method thereof. Background technique [0002] Steel is an important engineering and structural material, but due to corrosion, its service life is greatly shortened or its use value is lost. According to statistics, the amount of corroded and scrapped steel accounts for more than 20% of the total amount of steel every year, and the loss of corroded steel in my country accounts for about 4% of the national economic output. In order to prevent steel corrosion, the simplest and most effective way is to use paint to protect. The annual demand for industrial coatings in my country is about 2.2 million tons, and 800,000 tons of organic solvents are volatilized every year. The waste of resources is about 3 billion yuan, and it also brings serious environmental pollution. As people's awareness of environmental protection increases, there is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/08C09D175/04C09D5/14C09D7/12
CPCC09D133/08C08K2201/011C08L2205/03C09D5/14C09D7/40C09D7/61C09D7/65
Inventor 张明
Owner 张明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap