Wool/cattle fluff fiber/mulberry silk/copper ammonia fiber blended fabric and preparation method thereof

A technology of cupro ammonia fiber and blended fabrics, which is applied in the fields of textile, dyeing, and bleached products. It can solve the problems of pure spinning such as difficulty in carding, unsoftness, etc., and achieve smooth and plump hand feeling, good drapability, and excellent elasticity. Effect

Inactive Publication Date: 2015-04-15
江苏华西村纺织服装有限公司
View PDF11 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is a common practice in this industry to use velvet fiber instead of cashmere fiber, but the length of velvet fiber is short, the average length is about 28mm, and the curl degree and curl elasticity are worse than that of wool fiber. After decolorization and dyeing, the spinnability of velvet fiber is poor. Pure spinning is difficult
[0003] In addition, in order to increase the gloss, smoo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] A kind of wool / velvet fiber / mulberry silk / cupro fiber blended fabric, the raw material composition mass ratio of the fabric is: wool fiber 30%, velvet fiber 24%, mulberry silk 26%, cupro fiber 20%.

[0025] The fabric specifications are:

[0026] Warp yarn count: 98 / 2

[0027] Weft yarn count: 98 / 2+60 / 1

[0028] Finished Warp / Weft Density: 424×339 / 10cm

[0029] Square meter weight: 155g / ㎡

[0030] Finished width: 155-2cm.

[0031] A preparation method of wool / ox hair fiber / mulberry silk / cupro ammonia fiber blended fabric, which Main production process:

[0032] (one) Strip dyeing, combing : Pine cone→dyeing→dehydration→rewashing→B412 (three times needle combing)→B303→B304→B311 (combing)→B305 adding velvet fiber (1)→B305 (2)→B306

[0033] (2) Spinning: B412 mixed sliver → B423 head needle → B432 two needles → B442 three needles → B452 four needles → FB441 (coarse one) → FB441 (coarse two) → spinning → automatic winding → doubling → two-for-one twisting → steame...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Weightaaaaaaaaaa
Login to view more

Abstract

The invention relates to a wool/cattle fluff fiber/mulberry silk/copper ammonia fiber blended fabric. The fabric comprises the following material components in percentage by weight: 30% of wool fibers, 24% of cattle fluff fibers, 26% of mulberry silk and 20% of copper ammonia fibers. The preparation method includes the steps of: top dyeing and re-combing, spinning, weaving and dyeing and finishing; the top dying and re-combing process includes, dying separately, dehydrating and backwashing, and mixing the wool fibers, the mulberry silk and the copper ammonia fibers by B412, gilling for three times during the mixing process, adding the mulberry silk for three times, gilling by B303 and B304, and combing by B311, adding the cattle fluff fibers during the gilling process of B305, then gilling by B305 for a second time, and at last combing by B306. The prepared product is gentle in gloss, soft, fine and smooth and good in drapability, has the texture and style of silk fabric, and is low in cost.

Description

technical field [0001] The invention relates to a wool / ox hair fiber / mulberry silk / cupro ammonia fiber blended fabric and a preparation method thereof. Background technique [0002] Cashmere products are high-end clothing fabrics. They are breathable, warm, moisture-proof, soft and elastic, with good hand feeling and natural luster, which are deeply loved by consumers. However, the production of cashmere fiber is restricted by the natural environment and ecological factors, which cannot meet the growing high consumption demand. Therefore, it is necessary to develop textile fabrics with certain technical content and high added value to replace cashmere products so that the appearance and feel of the products can achieve the same effect. It has an advantage in taking performance and price. It is a common practice in this industry to use velvet fiber instead of cashmere fiber, but the length of velvet fiber is short, with an average length of about 28mm. The degree of crimp a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D03D13/00D06P3/85D06L3/02D03D15/225D03D15/233D03D15/47D03D15/50D03D15/54D06L4/13
Inventor 孙云丰张建刚胡蓉李敏芳庞志红
Owner 江苏华西村纺织服装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap