A cyanide-free silvering electroplating solution and a preparing method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cyanide-free silver plating and electroplating solution technology, applied in the field of electroplating solution, can solve the problems of wear resistance, poor corrosion resistance, rough coating, poor conductivity, etc.
Inactive Publication Date: 2015-04-22
WUXI NUIST WEATHER SENSOR NETWORK TECH
View PDF3 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0028] The formula of this electroplating solution is as follows: silver nitrate 50g / L, potassium sulfate 40g / L, sodium sulfate 60g / L, buffering agent 30 g / L, wetting agent 5 g / L, brightener 5g / L, add deionized water to 1000ml.
[0029] Weigh an appropriate amount of wetting agent according to the formula, add deionized water, and stir until dissolved; then weigh an appropriate amount of silver nitrate, potassium sulfate, and sodium sulfate and add them to the above solution, and stir until dissolved at room temperature; then put the above solution in a water bath Heat to 65°C, add a proper amount of brightening additives, adjust the pH value of the solution with a buffer, and stir evenly.
Embodiment 2
[0031] The formula of this electroplating solution is as follows: silver nitrate 60g / L, potassium sulfate 47g / L, sodium sulfate 80g / L, buffering agent 35 g / L, wetting agent 10 g / L, brightener 12g / L, add deionized water to 1000ml.
[0032] Weigh an appropriate amount of wetting agent according to the formula, add deionized water, and stir until dissolved; then weigh an appropriate amount of silver nitrate, potassium sulfate, and sodium sulfate and add them to the above solution, and stir until dissolved at room temperature; then put the above solution in a water bath Heat to 65°C, add a proper amount of brightening additives, adjust the pH value of the solution with a buffer, and stir evenly.
Embodiment 3
[0034] The formula of the electroplating solution is as follows: silver nitrate 70g / L, potassium sulfate 54g / L, sodium sulfate 100g / L, buffer 40 g / L, wetting agent 15 g / L, brightener 20 g / L, add deionized water to 1000ml.
[0035] Weigh an appropriate amount of wetting agent according to the formula, add deionized water, and stir until dissolved; then weigh an appropriate amount of silver nitrate, potassium sulfate, and sodium sulfate and add them to the above solution, and stir until dissolved at room temperature; then put the above solution in a water bath Heat to 65°C, add a proper amount of brightening additives, adjust the pH value of the solution with a buffer, and stir evenly.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to a cyanide-free silveringelectroplating solution and a preparing method thereof. The electroplating solution comprises 50-90 g / L of silver nitrate, 40-70 g / L of potassiumsulfate, 60-140 g / L of sodiumsulfate, 30-50 g / L of a buffering agent, 5-25 g / L of a wetting agent and 5-35 g / L of a brightener, with the balance being deionized water and the total volume being 1000 mL. The electroplating solution is prepared by weighing a proper amount of the wetting agent according to the formula, adding the deionized water, stirring until the wetting agent is dissolved, weighing proper amounts of the silver nitrate, the potassiumsulfate and the sodium sulfate, adding the weighed silver nitrate, the weighed potassium sulfate and the weighed sodium sulfate into the above-mentioned solution, stirring at room temperature until the silver nitrate, the potassium sulfate and the sodium sulfate are dissolved, heating the solution to 65 DEG C by using a water bath, adding a proper amount of the brightener, adjusting the pH value of the solution by using the buffering agent, and stirring uniformly. A plating formed by the electroplating solution is wear-resistant, good in corrosion resistance, high in brightness, good in conductivity and good in stability.
Description
technical field [0001] The invention relates to a cyanide-free silver-plating electroplating solution and a preparation method, belonging to the technical field of electroplating solutions. Background technique [0002] Electroplating is the process of plating a thin layer of other metals or alloys on the surface of certain metals using the principle of electrolysis. It is a process of using electrolysis to attach a layer of metal film to the surface of metal or other material parts to prevent metal oxidation ( Such as rust), improve wear resistance, electrical conductivity, reflective properties, corrosion resistance (copper sulfate, etc.) and enhance the appearance. The outer layer of many coins is also electroplated. [0003] During electroplating, the plated metal or other insoluble materials are used as the anode, and the workpiece to be plated is used as the cathode, and the cations of the plated metal are reduced on the surface of the workpiece to be plated to form a...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More