Rubber sealing material for automobile and preparation method of rubber sealing material

A technology for rubber seals and automobiles, applied in the field of polymer materials, can solve problems such as poor fatigue resistance and achieve good fatigue resistance

Inactive Publication Date: 2015-05-06
LIUZHOU YINGHANG AUTO PARTS
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing rubber seal materials for automobiles have poor fatigue resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The formula of automobile rubber sealing material of the present invention is as follows:

[0011] Natural rubber 68kg, neoprene 25kg, stearic acid 2.5kg, methyl hydrogen silicone oil 2.5kg, ethylene glycol 0.4kg, calcium carbonate 0.6kg, oleic acid diethanolamine borate 0.7kg, magnesium dimethacrylate 5kg , Dry oil alkyd resin 4kg, paraffin wax 1.5kg, diethanolamine borate 1.5kg, diacetyl peroxide 3kg, zinc oxide 9kg, white carbon black 7kg, antioxidant 1.2kg, sulfur 2kg.

[0012] The preparation method of automobile rubber sealing material of the present invention is as follows:

[0013] The natural rubber and chloroprene rubber in the formula amount are thinned separately and then mixed into the open mill, and then the remaining components are added into the open mill for mixing until uniform, and then the sheet is produced to obtain the mixed rubber, and the mixed rubber is One-stage vulcanization, the vulcanization temperature is controlled at 160°C, the vulcaniza...

Embodiment 2

[0015] The formula of automobile rubber sealing material of the present invention is as follows:

[0016] Natural rubber 65kg, neoprene 20kg, stearic acid 2kg, methyl hydrogen silicone oil 2kg, ethylene glycol 0.3kg, calcium carbonate 0.5kg, oleic acid diethanolamine borate 0.8kg, magnesium dimethacrylate 4kg, dry Natural oil alkyd resin 3kg, paraffin 1kg, diethanolamine borate 1.6kg, diacetyl peroxide 2kg, zinc oxide 10kg, white carbon black 6kg, antioxidant 0.5kg, sulfur 1kg.

[0017] The preparation method of automobile rubber sealing material of the present invention is as follows:

[0018] The natural rubber and chloroprene rubber in the formula amount are thinned separately and then mixed into the open mill, and then the remaining components are added into the open mill for mixing until uniform, and then the sheet is produced to obtain the mixed rubber, and the mixed rubber is One-stage vulcanization, the vulcanization temperature is controlled at 150°C, the vulcanizati...

Embodiment 3

[0020] The formula of automobile rubber sealing material of the present invention is as follows:

[0021] 70kg of natural rubber, 30kg of neoprene rubber, 3kg of stearic acid, 3kg of methyl hydrogen silicone oil, 0.5kg of ethylene glycol, 0.8kg of calcium carbonate, 0.6kg of oleic acid diethanolamine borate, 6kg of magnesium dimethacrylate, dry Natural oil alkyd resin 5kg, paraffin 2kg, diethanolamine borate 1.3kg, diacetyl peroxide 4kg, zinc oxide 8kg, white carbon black 8kg, antioxidant 2kg, sulfur 3kg.

[0022] The preparation method of automobile rubber sealing material of the present invention is as follows:

[0023] The natural rubber and chloroprene rubber in the formula amount are thinned separately and then mixed into the open mill, and then the remaining components are added into the open mill for mixing until uniform, and then the sheet is produced to obtain the mixed rubber, and the mixed rubber is One-stage vulcanization, the vulcanization temperature is controll...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a rubber sealing material for an automobile. The rubber sealing material is composed of the following components in parts by mass: 65-70 parts of natural rubber, 20-30 parts of chloroprene rubber, 2-3 parts of stearic acid, 2-3 parts of methyl hydrogen silicon oil, 0.3-0.5 part of ethylene glycol, 0.5-0.8 part of calcium carbonate, 0.6-0.8 part of oleic diethanolamine borate, 4-6 parts of magnesium dimethacrylate, 3-5 parts of drying alkyd resin, 1-2 parts of paraffin, 1.3-1.6 parts of diethanolamine borate, 2-4 parts of diacetyl peroxide, 8-10 parts of zinc oxide, 6-8 parts of white carbon black, 0.5-2 parts of an anti-aging agent and 1-3 parts of sulfur. The invention also provides a preparation method of the rubber sealing material. The rubber sealing material for the automobile, provided by the invention, has favorable fatigue resistance and is suitable for sealing all parts of the automobile.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a rubber sealing material for automobiles. Background technique [0002] Automobile rubber seal strip is one of the important parts of the car, widely used in the door, window, body, seat, sunroof, engine box and trunk, etc., with waterproof, sealing, sound insulation, dustproof , antifreeze, shock absorption, warmth and energy saving. It must have strong tensile strength, good elasticity, and relatively good high temperature resistance and aging resistance. Existing rubber sealing materials for automobiles have poor fatigue resistance. Contents of the invention [0003] The invention provides a rubber sealing material for automobiles, and for this purpose, the invention also provides a preparation method thereof. [0004] The invention provides a rubber sealing material for automobiles. The rubber sealing material is composed of the following component...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L11/00C08L83/05C08L67/08C08L91/06C08K13/02C08K5/09C08K5/053C08K3/26C08K5/55C08K5/098C08K5/14C08K3/22C08K3/36C08K3/06B29C35/02
CPCC08L7/00B29C35/02C08K2201/014C08L2205/035C08L2312/00
Inventor 莫海燕
Owner LIUZHOU YINGHANG AUTO PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap