Core-shell-particle toughened modified PC/PET alloy material

A technology for toughening and modifying alloy materials, which is applied in the field of toughening and modifying PC/PET alloy materials by core-shell particles, can solve the problem that the mechanical properties of PC/PET alloy materials can not be expected to achieve the desired effect, and the improvement of toughness is limited. The problems of strength, stiffness, heat resistance and processability decrease, to achieve the effect of improving toughness and rigidity, low cost, good processability and heat resistance

Inactive Publication Date: 2015-06-10
QINGDAO JIAYIYANG IND & TRADE
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the use of elastomer toughening can greatly improve the impact resistance of PC/PET alloy materials, but at the same time it also causes a serious decline in its strength, stiffness, heat resistance and processing performance; when using inorganic rigid particles to toughen at a certain Under the same

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1:

[0021] A core-shell particle toughening modified PC / PET alloy material, the components of which are proportioned by mass percentage as follows: PC 55%, PET 25%, styrene-acrylonitrile-glyceryl methacrylate (SAG) 3% , 10% ultrafine calcium carbonate particles with a particle size of 10-100nm, 5% ethylene-propylene-diene copolymer (EPDM), 0.5% methacrylic acid, 0.3% cumene hydrogen peroxide, antioxidant 1010 0.3 %, Pentaerythritol stearate (PETS) 0.9%. Wherein, the PC is bisphenol A type aromatic polycarbonate, and the weight average molecular weight is 20000~40000g / mol; the PET is polyethylene terephthalate, and its characteristic viscosity is 0.6~0.9dL / g.

[0022] Preparation method: (1), dry PC in a blast dryer at a temperature of 110 ℃ ~ 130 ℃ for 3 to 4 hours, and dry PET at 130 ℃ ~ 150 ℃ for 3 to 4 hours, and stand by; (2), It is 50 ℃~75 ℃ of high-speed mixers that the ultrafine calcium carbonate particles with particle diameters of 10~100nm are adde...

Example Embodiment

[0023] Example 2:

[0024] A core-shell particle toughening modified PC / PET alloy material, the components of which are proportioned by mass percentage: PC 55%, PET 30%, styrene-acrylonitrile-glyceryl methacrylate (SAG) 3% , 5% ultrafine calcium carbonate particles with a particle size of 10-100nm, 5% styrene-ethylene-butylene-styrene block copolymer (SEBS), 0.5% methacrylic acid, dicyclohexyl peroxydicarbonate 0.2%, the compound of antioxidant 1010 and antioxidant 168 0.3%, pentaerythritol stearate (PETS) 1%. Wherein, the PC is bisphenol A type aromatic polycarbonate, and the weight average molecular weight is 20000~40000g / mol; the PET is polyethylene terephthalate, and its characteristic viscosity is 0.6~0.9dL / g.

[0025] Preparation method: (1), dry PC in a blast dryer at a temperature of 110 ℃ ~ 130 ℃ for 3 to 4 hours, and dry PET at 130 ℃ ~ 150 ℃ for 3 to 4 hours, and stand by; (2), It is 50 ℃~75 ℃ of high-speed mixers that the ultrafine calcium carbonate particles wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Weight average molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention discloses a core-shell-particle toughened modified PC/PET alloy material. The core-shell-particle toughened modified PC/PET alloy material comprises following ingredients, by mass, 45 to 60% of PC, 5 to 30% of PET, 1 to 3% of a compatilizer, 5 to 10% of an inorganic rigid particle, 3 to 10% of an elastomer, 0.2 to 1% of methacrylic acid, 0.1 to 0.5% of an initiator, 0.1 to 0.5% of an anti-oxidant, and 0.1 to 1% of a lubricant. Beneficial effects are that: compared with the prior art, the inorganic rigid particle is used for surface pretreatment, and interaction and grafting reaction with the elastomer are carried out, so that a core-shell structure is formed and is used for modifying a PC/PET alloy material, wherein the inorganic rigid particle is taken as the core of the core-shell structure, and the elastomer is taken as the shell of the core-shell structure; original excellent performance of the PC/PET system is maintained, toughness and rigidity of the PC/PET alloy material are increased greatly; the core-shell-particle toughened modified PC/PET alloy material possesses excellent processability and heat resistance, is low in cost, and possesses a promising application prospect.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a core-shell particle toughened modified PC / PET alloy material. Background technique [0002] Polycarbonate / polyethylene terephthalate (PC / PET) alloy has many excellent properties, but the compatibility of PC and PET is limited when the two polymers are blended. Adding the third component to the PC / PET blend system can significantly improve the compatibility of the two polymers in the system. The third component usually has good compatibility or adhesion with the matrix resin, and its main function is to "bridge" between PC and PET micelles or react with the matrix resin PC and PET to form chemical bonds and combine with each other , thereby improving the overall compatibility of PC / PET alloys. With the expansion of the application range of PC / PET alloy materials, the requirements for functionalization and high performance of PC / PET alloy materials are put forward, es...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L67/02C08K9/04C08K3/26B29B9/06
CPCC08L69/00B29B9/06C08K2201/003C08L2201/08C08L2205/03
Inventor 不公告发明人
Owner QINGDAO JIAYIYANG IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap