A phosphate ion, MOF-5 technology, applied in the field of MOFs materials, to achieve the effect of wide material sources, low secondary pollution, and high adsorption capacity

Active Publication Date: 2015-06-17
YUNNAN UNIV
View PDF13 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] So far, MOFs materials are mostly used for the adsorption and removal of dyes or heavy metal ions. There are no articles or patents on the use of MOFs materials for phosphorus removal. This patent successfully uses MOFs materials for phosphorus removal in water bodies.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • MOFs materials for adsorbing phosphate anions
  • MOFs materials for adsorbing phosphate anions
  • MOFs materials for adsorbing phosphate anions

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Example 1: In lake water with a concentration of 1.1 mg / L and an initial pH of 6, 0.15 g of ZIF-8 material was added per 1 L, and the phosphorus removal rate was measured to be 98.9% after 1 min of reaction.

Embodiment 2

[0018] Example 2: 0.55 g of ZIF-8 material was added per 1 L of wastewater from a sewage treatment plant with a concentration of 12.8 mg / L and an initial pH of 10. After 30 minutes of reaction, the phosphorus removal rate was measured to be 93.4%.

Embodiment 3

[0019] Example 3: In industrial wastewater with a concentration of 29.1 mg / L and an initial pH of 3, 1.00 g of ZIF-8 material was added per 1 L, and the phosphorus removal rate was measured to be 90.5% after 100 min of reaction.

[0020] 2. Example of MOF-5 removing phosphorus in water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to MOF materials for adsorbing phosphate anions. The MOF materials are taken as adsorbents to be applied to adsorption of the phosphate anions in a water solution, and have remarkable adsorptivity on the phosphate anions. Several MOFs materials are respectively added in phosphorous water of different concentrations and phosphorous water of different pH values to be stirred for 1-120 min, the phosphorus removal rate can be up to 90-99%, and the processed MOFs materials have no phosphorus desorption phenomenon and secondary pollution on environment. The several MOFs materials have the advantages of being large in specific surface area, high in adsorption capacity, high in dephosphorization efficiency, small in usage amount, simplicity, safety, high efficiency and low cost. The invention relates to phosphorus removal application of industrial wastewater, lake water, tail water discharged by sewage treatment plants, and aquaculture wastewater.

Description

technical field [0001] The invention belongs to the application field of environment-friendly materials, and relates to a MOFs material used for adsorbing phosphate ions. Background technique [0002] In recent years, with the rapid increase of population and rapid industrial growth, environmental pollution has become increasingly serious. Excessive phosphorus in water will accelerate the eutrophication of the water body. Eutrophication refers to the large amount of nutrients such as nitrogen and phosphorus required by organisms entering lakes, estuaries, and inland seas, causing algal blooms, a large drop in dissolved oxygen in water bodies, and water quality deterioration. Phenomenon. This phenomenon is more serious in our country and has brought great harm to industry, aquaculture, agriculture and tourism. Phosphate is considered to be one of the key factors for the excessive growth of aquatic organisms, and has a greater impact on the existence of aquatic organisms suc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/22C02F1/28C02F1/58
Inventor 王家强李俊杰段德良闫智英郭云龙王敏
Owner YUNNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap