A method for preparing basic chromium sulfate tanning agent from chromite ore sulfuric acid leaching solution

A chrome sulfate tanning agent and leaching solution technology, which can be used in small raw hides/large raw hides/leather/fur treatment, small raw hides/large raw hides/leather hides/fur chemical treatment, tanning treatment, etc. problem, to achieve the effect of complete iron removal, strong continuity, and mild method conditions

Active Publication Date: 2016-11-23
NORTHEASTERN UNIV LIAONING
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problem that the existing chromite sulfuric acid leaching solution is difficult to remove iron, the present invention provides a method for preparing basic chromium sulfate tanning agent from the chromite sulfuric acid leaching solution. Iron removal, so that Fe in solution 3+ The concentration drops below 1g / L, and then deep iron removal of goethite is carried out, which realizes the effective separation of chromium and iron in the acidic system solution, and prepares high-quality basic chromium sulfate tanning agent products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing basic chromium sulfate tanning agent from chromite ore sulfuric acid leaching solution
  • A method for preparing basic chromium sulfate tanning agent from chromite ore sulfuric acid leaching solution
  • A method for preparing basic chromium sulfate tanning agent from chromite ore sulfuric acid leaching solution

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] The following preparation method of chromite sulfuric acid leaching solution is: grinding the chromite ore into particles, adding it to the reactor, and then adding sulfuric acid. The liquid-to-solid ratio of sulfuric acid to mineral powder is (1~4): 1mL / g, at the stirring speed The temperature is 60~160 rpm, the temperature is 90~160℃, the catalyst is added to carry out the acidolysis reaction, the reaction temperature is 110~170℃, the reaction time is 1~8h, the reaction solution is filtered and the filter residue is removed to obtain chromium Iron ore sulfuric acid leaching solution.

[0051] The used pyrite seed crystals and goethite seed crystals have a mass purity of >97% and a powder particle size of <74μm.

Embodiment 1

[0053] Using 500mL chromite sulfuric acid leaching solution as raw material, the concentration of metal ions in the leaching solution is [Cr 3+ ]=26.4g / L, [Fe 3+ ]=13.2g / L, [Mg 2+ ]=3.7g / L, [Al 3+ ]=4.5g / L.

[0054] Use as figure 1 As shown in the schematic diagram of the process flow of preparing basic chrome sulfate tanning agent from chromite sulfuric acid leaching solution, the method for preparing basic chrome sulfate tanning agent from chromite sulfuric acid leaching solution in this embodiment, the specific steps are as follows:

[0055] Step 1: Pour the chromite sulfuric acid leaching solution into the reactor, turn on the heating and stirring, the stirring speed is 2400rad / s (radian per second), raise the temperature of the leaching solution to 90℃, and slowly drop 2.5mol / L into the reactor Potassium hydroxide solution until the pH value of the solution reaches 2.3, and keep it unchanged for at least 1 min;

[0056] Then pour 2.5g jarosite seed crystal powder into the reacto...

Embodiment 2

[0066] Using 500mL chromite sulfuric acid leaching solution as raw material, the concentration of metal ions in the leaching solution is [Cr 3+ ]=30.7g / L, [Fe 3+ ] = 19.8g / L, [Mg 2+ ]=5.2g / L, [Al 3+ ]=6.6g / L.

[0067] In this embodiment, the method for preparing basic sulfate chrome tanning agent from chromite sulfuric acid leaching solution, the specific steps are as follows:

[0068] Step 1: Inject the chromite sulfuric acid leaching solution into the reactor, turn on the heating and stirring, the stirring speed is 1800rad / s, and the temperature of the leaching solution is raised to 85℃, and slowly drop 3mol / L sodium hydroxide solution into the reactor to reach the solution The pH value reaches 1.7 and remains unchanged for at least 1 min;

[0069] Pour 1g of yellow sodium iron vitriol seed crystal powder into the reactor, keep the stirring speed at 1800rad / s for aging reaction for 150 minutes, and monitor the pH value of the solution to stabilize in the range of 1.6 to 1.8 by addi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

In view of the existing problem of difficulty in removing iron from chromite sulfuric acid leachate, the present invention provides a method for preparing basic chromium sulfate tanning agent from chromite sulfuric acid leachate, which belongs to the field of mineral processing technology. The method includes controlling the temperature of the chromite sulfuric acid leach solution at 60 to 100°C, adjusting the pH value of the solution to between 1 and 3, adding pyrosite crystal seeds and crystallizing; filtering to obtain pyrosite crystals and filtrate; Keep the temperature of the filtrate, adjust the pH value of the solution to between 2 and 4, add goethite crystal seeds and crystallize; filter to obtain goethite crystals and filtrate; add diluted alkali solution to the filtrate to neutralize the solution. The salinity is 33±1%; the solution is then dried to obtain a basic chromium sulfate tanning agent. This process does not produce highly toxic Cr(Ⅵ). It is a clean and non-toxic tanning agent preparation method. Through two iron removal processes, more complete iron removal can be achieved, and the basic chromium sulfate tanned leather obtained The mass percentage of iron in the agent is less than 0.1%.

Description

Technical field [0001] The invention belongs to the technical field of mineral processing, and particularly relates to a method for preparing a basic sulfate chrome tanning agent from a chromite sulfuric acid leaching solution. Background technique [0002] Chromite is the main occurrence form of chromium in nature. Among them, iron, magnesium, aluminum and chromium co-exist in chromite in the form of isomorphic spinel, available (Mg, Fe 2+ )(Cr,Al,Fe 3+ ) 2 O 4 The general formula is expressed. Due to different mineralization conditions, some chromites do not contain magnesium, and some chromites do not contain aluminum. Chromite is widely used in the chemical industry and other fields and is an important raw material for the production of chromium salts. my country began to produce chromium salts in 1958, and in 2005 it surpassed the United States for the first time to become the world's largest country in chromium salt production. Up to now, nearly half of the world's chromi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C14C3/06
CPCC14C3/06
Inventor 刘承军赵青张庆松史培阳姜茂发
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com