High-hardness and high-gloss heat and flame resistant ABS plastic

A high-gloss, high-hardness technology, applied in the field of high-hardness, high-gloss flame-retardant and heat-resistant ABS plastics, can solve the problems of poor surface gloss, weak flame-retardant and heat-resistant performance, low strength, etc. Abrasion resistance, not easy to scratch effect

Inactive Publication Date: 2015-07-22
李凤燕
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current ABS resin plastic still has the disadvantages of low strength, poor surface abrasion resistance, poor flame retardancy and heat resistance in extreme cases, and poor surface gloss.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A high-hardness, high-gloss flame-retardant and heat-resistant ABS plastic, consisting of the following ingredients in parts by weight:

[0034] ABS resin 80 parts

[0035] 8 parts polyimide fiber

[0036] 15 parts of p-diazodiphenylamine paraformaldehyde condensate

[0037] Polyisocyanate block 5 parts

[0038] Silicone modified polyurethane resin 15 parts

[0039] 10 parts of 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline

[0040] Dimethyl styrylpyridine sulfate 3 parts

[0041] 2 parts isobutyraldehyde

[0042] Curing agent 8 parts

[0043] Dipropylene glycol dimethyl ether 1 part

[0044] 1 part polyvinyl butyral

[0045] Cadmium Sulfur Selenide 7 parts

[0046] 1 part of N-methylpyrrolidone

[0047] Zinc ferrite 8 parts

[0048] Diketopyrrolopyrrole pigment 8 parts

[0049] 0.2 parts of 4-tert-butylcyclohexanone

[0050] Cyclododecanone 0.2 parts

[0051] 2 parts gamma-butyrolactone

[0052] Barium sulfate 10 parts

[0053] 1,2,3,4-cyclopentane tetra...

Embodiment 2

[0056] A high-hardness, high-gloss flame-retardant and heat-resistant ABS plastic, consisting of the following ingredients in parts by weight:

[0057] ABS resin 100 parts

[0058] 20 parts polyimide fiber

[0059] 30 parts of p-diazodiphenylamine paraformaldehyde condensate

[0060] Polyisocyanate block 15 parts

[0061] Silicone modified polyurethane resin 25 parts

[0062] 20 parts of 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline

[0063] Dimethyl styrylpyridine sulfate 6 parts

[0064] 8 parts of isobutyraldehyde

[0065] Curing agent 12 parts

[0066] Dipropylene glycol dimethyl ether 4 parts

[0067] 4 parts polyvinyl butyral

[0068] Cadmium sulfur selenide 15 parts

[0069] 4 parts of N-methylpyrrolidone

[0070] Zinc ferrite 10 parts

[0071] Diketopyrrolopyrrole pigment 10 parts

[0072] 0.5 parts of 4-tert-butylcyclohexanone

[0073] Cyclododecanone 0.5 part

[0074] 5 parts gamma-butyrolactone

[0075] Barium sulfate 15 parts

[0076] 1,2,3,4-cyclop...

Embodiment 3

[0079] A high-hardness, high-gloss flame-retardant and heat-resistant ABS plastic, consisting of the following ingredients in parts by weight:

[0080] ABS resin 90 parts

[0081] 10 parts polyimide fiber

[0082] 20 parts of p-diazodiphenylamine paraformaldehyde condensate

[0083] Polyisocyanate block 10 parts

[0084] Silicone modified polyurethane resin 20 parts

[0085] 15 parts of 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline

[0086] Dimethyl styrylpyridine sulfate 5 parts

[0087] 6 parts of isobutyraldehyde

[0088] Curing agent 10 parts

[0089] Dipropylene glycol dimethyl ether 2 parts

[0090] 3 parts polyvinyl butyral

[0091] Cadmium Sulfur Selenide 10 parts

[0092] N-Methylpyrrolidone 2 parts

[0093] Zinc ferrite 9 parts

[0094] Diketopyrrolopyrrole pigment 9 parts

[0095] 0.3 parts of 4-tert-butylcyclohexanone

[0096] Cyclododecanone 0.4 parts

[0097] 3 parts gamma-butyrolactone

[0098] Barium sulfate 12 parts

[0099] 1,2,3,4-cyclopentane ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to high-hardness and high-gloss heat and flame resistant ABS plastic which comprises the following components: ABS resin, polyimide fiber, a diazo diphenylamine paraformaldehyde condensate, a polyisocyanate block polymer, silicone-modified polyurethane resin, 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, styryl pyridinealdoximedimethyl sulfate salt, isobutyraldehyde, a curing agent, dipropylene glycol dimethyl ether, polyvinyl butanol, cadmium sulfoselenide, N-methylpyrrolidone, zinc ferrite, diketo-pyrrolo-pyrrole pigment, p-tert-butyl-cyclohexanon, cyclododecanone, gamma butyrolactone, barium sulfate, 1,2,3,4-cyclopentanetetracarboxylic acid, and deionized water. The high-hardness and high-gloss heat and flame resistant ABS plastic is high in hardness, has metallic gloss on the surface only, is high in abrasion resistance, and is heat and flame resisting.

Description

technical field [0001] The invention relates to a flame-retardant and heat-resistant ABS plastic with high hardness and high gloss. Background technique [0002] ABS resin plastic is the polymer with the largest output and the widest application today. It has good physical and mechanical properties, high impact strength, chemical stability, good electrical properties, good product processing and machining performance, and is resistant to water, inorganic salts, acid and alkali, and is a widely used engineering material. However, the current ABS resin plastic still has the disadvantages of low strength, poor surface abrasion resistance, weak flame retardancy and heat resistance in extreme cases, and poor surface gloss. Contents of the invention [0003] In order to achieve the above object, the present invention adopts the following technical solution: a high-hardness, high-gloss, flame-retardant and heat-resistant ABS plastic, consisting of the following components by wei...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L79/08C08L59/00C08L75/04C08K13/02C08K5/07C08K3/24C08K3/30C08K5/1535C08K5/092
Inventor 李凤燕
Owner 李凤燕
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com